Abstract:A novel flower-like 0.1%WO3/CeO2(f) catalyst with high-efficiency was fabricated for the selective reduction of NOx by NH3. In contrast to traditional WO3/CeO2, this catalyst exhibited a significant SCR performance of 90% NOx conversion and 95% N2 selectivity within a wide temperature range of 175-450.C and great H2O and/or SO2 resistance under a high GHSV of 177,000 h 1. A variety of analytical techniques including SEM, XRD, XPS, NH3-TPD, H2-TPR and in situ DRIFTS-MS were employed for the catalysts characterization to fully understand the reaction mechanism over WO3/CeO2 catalysts. It was found that the flower-like structure promoted a more uniform dispersion of tungsten species on the support and a stronger interaction between WO3 and CeO2, thereby increasing the acid sites and surface vacancies. Moreover, more chemical active oxygen and trivalent cerium species were presented on 0.1% WO3/CeO2(f). In situ DRIFTS-MS and H2-TPR revealed that the reducibility was optimized for 0.1% WO3/CeO2(f). Then NH3 oxidation species could react with gaseous or adsorbed NOx during Eley-Rideal (E-R) pathway for 0.1%WO3/CeO2(f) at a high temperature (300. C). Meanwhile, NOx was reduced into more active bridged nitrates participating in the reaction via Langmuir-Hinshelwood (L-H) route, contributing to its superior deNOx performance. In comparison, the formation of inert adsorbed NH3 oxidization/ deformation species and bridged nitrates suppressed the SCR reaction over 0.1%WO3/CeO2, resulting in its inferior deNOx activity. This study not only provides a new strategy for developing high-efficiency ceria supported NH3-SCR catalyst, but also lays a foundation for investigating the reaction mechanism of cerium-based catalyst for further practical applications.

Design of a hierarchical Fe-ZSM-5@CeO2 catalyst and the enhanced performances for the selective catalytic reduction of NO with NH3

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

High-performance CeO2/halloysite Hierarchical Catalysts with Promotional Redox Property and Acidity for the Selective Catalytic Reduction of NO with NH3

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Single-Atom Ce-Modified Α-Fe2o3 for Selective Catalytic Reduction of NO with NH3.

Mn and Fe oxides co-effect on nanopolyhedron CeO2 catalyst for NH3-SCR of NO

Modification of Cu/ZSM-5 Catalyst with CeO2 for Selective Catalytic Reduction of NOx with Ammonia

Selective catalytic reduction of NO over Fe-ZSM-5: mechanistic insights by operando HERFD-XANES and valence-to-core X-ray emission spectroscopy

A Superior Cerium-Tungsten Bimetal Oxide Catalyst with Flower-Like Structure for Selective Catalytic Reduction of NO by NH3

Enhancing low-temperature NH3-SCR performance of Fe–Mn/CeO2 catalyst by Al2O3 modification

Revealing the Excellent Low-Temperature Activity of the Fe 1- x Ce x O δ -S Catalyst for NH 3 -SCR: Improvement of the Lattice Oxygen Mobility

Designing SO2-resistant Cerium-Based Catalyst by Modifying with Fe2O3 for the Selective Catalytic Reduction of NO with NH3

Remarkable Enhancement in the N-2 Selectivity of NH3-SCR over the CeNb3Fe0.3/TiO2 Catalyst in the Presence of Chlorobenzene

Unraveling the Complete Mechanism of the NH3-Selective Catalytic Reduction of NO over CeO2

Comparative study of 3D ordered macroporous Ce0.75Zr0.2M0.05O2−δ (M = Fe, Cu, Mn, Co) for selective catalytic reduction of NO with NH3

CeO2 doping boosted low-temperature NH3-SCR activity of FeTiOx catalyst: A microstructure analysis and reaction mechanistic study

Selective catalytic reduction of NO<sub>x</sub> with NH<sub>3</sub> over a novel Co-Ce-Ti catalyst

The design of the highly active NH3-SCR catalyst Ce-W/UiO-66: Close coupling of active sites and acidic sites

Revealing the Excellent Low-Temperature Activity of the Fe1–xCexOδ-S Catalyst for NH3-SCR: Improvement of the Lattice Oxygen Mobility