Effects of Molecular and Electronic Structures in CoOx/CeO2 Catalysts on NO Reduction by CO

Shuhao Zhang,Yuanyuan Li,Jiahao Huang,Jaeha Lee,Do Heui Kim,Anatoly I. Frenkel,Taejin Kim

DOI: https://doi.org/10.1021/acs.jpcc.8b12442

2019-01-01

Abstract:Ceria-supported transition metal oxide (such as CoOx) catalysts are promising, more cost-effective candidates to replace platinum group metal catalysts in the NO reduction process. A series of CoOx (0.2-31.3 Co/nm(2)) catalysts supported on CeO2 were prepared by the incipient wetness impregnation method and were tested for NO reduction by CO reaction in this work. Various characterization techniques, including Brunauer-Emmett-Teller, Raman spectroscopy, powder X-ray diffraction (XRD), X-ray absorption spectroscopy (XAS), and diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) were used to investigate the molecular and electronic structures of CoOx /CeO2 catalysts. It was observed that there are structural changes with varied Co loadings, such as (1) sub-monolayer: <2.3 Co/nm(2), (2) monolayer: 2.3-2.7 Co/nm(2), and (3) over-monolayer: >2.7 Co/ nm(2). The highest molar rate was observed at the 2.7 Co/nm(2) sample. In the case of over-monolayer samples, such as 7.1 Co/nm(2), the oxidation state of Co affected the catalytic activity. Using in situ XAS, an oxidation state change from Co3+ to Co2+ between 200 and 300 degrees C was identified. Catalyst deactivation was also affected by the change of Co oxidation states from the fresh sample (Co3+) to the used sample (Co3+/Co2+). N2O formation and decomposition were affected by the reaction temperature in a two-step procedure, where NO converts into N-2: (1) NO -> N2O and (2) N2O -> N-2. N-2 selectivity monotonically increased with an increasing reaction temperature between 200 and 400 degrees C. The results provided several structure-property relationships and a possible reaction mechanism for NO reduction by CO reaction over CoOx/CeO2 catalysts.