Abstract:The sol-gel method synergized with a carbothermic reaction has been known to be one of the most promising strategies for preparing a high-quality boride and carbon-based ultrahigh-temperature ceramic, yet their growth mechanism remains underexplored. Herein, high-purity ZrB2 ceramic powders are prepared by a sol-gel method synergized with a subsequent carbothermic reaction. Specifically, sorbitol (C6H14O6) is adopted to build molecularly disperse networks of Zr-O-C-B. Structural characterizations reveal that the calcination temperature and duration have a great influence on the phase and morphological transformation of the precursor. The ZrB2 seeds start to be generated near ZrO2 particles around 1100degree celsius and grow from the surface to the core of ZrO2 particles with heat and mass transportation around ZrO2 driven by B2O3 at high temperature. Additionally, the ZrB2 powders could research a hardness of 22.5 GPa and a bending strength of 540 MPa after sintering, showing improved mechanical properties. This work reveals the growth mechanism of ultrafine and high-purity ZrB2 powders by a sol-gel method and a carbothermic reaction, which can be used as raw materials to obtain ZrB2 ultrahigh-temperature ceramics with improved mechanical properties.

Key issues on the reactive sintering of ZrB2 ceramics from elementary raw materials

Oxygen Contamination on the Surface of Zrb2 Powders and Its Removal

Reactive Hot Pressing and Sintering Characterization of ZrB2–SiC–ZrC Composites

In Situ ZrB2 Formation in B4C Ceramics and Its Strengthening Mechanism on Mechanical Properties

Microstructures and mechanical properties of reactive spark plasma-sintered ZrB2–SiC–MoSi2 composites

Fabrication of ZrB2 Ceramics by Reactive Hot Pressing of ZrB and B

Reaction mechanism of self-propagating magnesiothermic reduction of ZrB2 powders

Stability and Reactivity of Zirconium Diboride in Intermediate-Temperature Hydrothermal Conditions: A Comprehensive Analysis

Microstructure and Thermal Shock Behavior of Sol–gel Introduced ZrB 2 Reinforced SiBCN Matrix

Reactive sintering behavior and enhanced densification of (Ti,Zr)B2–(Zr,Ti)C composites

Thermal ablation behavior of SiBCN-Zr composites prepared by reactive spark plasma sintering

Ultrafine ZrB2 Ceramic Powders Prepared by a Sol–Gel Method Synergized with a Carbothermic Reaction and Their Improved Sintering Performance

Effect of pressure loading cycle on spark plasma sintered ZrB 2-SiC-Yb 2O 3 ceramics

Oxidation Behavior of SiBCN-Zr Composites at 1500 °C Prepared by Reactive Spark Plasma Sintering

Preparation and Properties of ZrB2-SiC Porous Ceramics by Spark Plasma Sintering

Reaction Behavior and Formation Mechanism of ZrB2 and ZrC from the Ni-Zr-B4C System during Self-Propagating High-Temperature Synthesis

Chemical Process and Solid Solution Formation in Reactive Hot Pressed ZrB2–SiC Ceramics Doped with W

Effects of ZrB2 powders on microstructure and mechanical properties of ZrB2-SiCw ceramics

Effect of ZrB2 powders on densification, microstructure, mechanical properties and thermal conductivity of ZrB2-SiC ceramics

Catalytic Properties of ZrB<sub>2</sub>-Based Ultra-High Temperature Ceramics Based on the Wall Temperature Response Method

Influence of TiB2 and CrB2 on densification, microstructure, and mechanical properties of ZrB2 ceramics