Abstract:In general, single crystal shape memory alloys exhibit superior shape memory effect and superelasticity when compared to their polycrystalline counterparts. However, it is challenging and costly to prepare a single crystal in traditional ways, such as the Czochralski method and directional solidification technique. Recently, cyclic heat treatment (CHT) has emerged as a facile and cost-effective method to fabricate single crystal by inducing abnormal grain growth. In the present work, we aimed to fabricate Fe-Mn-Al-Cu single crystals utilizing the CHT technique. Single crystal Fe-Mn-Al-Cu shape memory alloys were successfully prepared, and the effect of CHT parameters on abnormal grain growth was investigated. It was revealed that increasing the cooling rate resulted in a non-monotonic response in the maximum grain size, which initially increased and was followed by a subsequent decrease. This behavior was attributed to the subgrain refinement, increase in subgrain misorientation angles, and the narrowing of the low density zones (LDZs) of subgrains. Decreasing the lower temperature of CHT caused similar trends in maximum grain size, due to the increase in subgrain misorientation angle and the expansion of the LDZs. Extending the holding time at the lower temperature of CHT had minimal impact on grain size. Increasing the heating rate of CHT resulted in a reduction in the maximum grain size because of the narrowing of the LDZs. Moreover, the addition of 2 wt% Cu led to a reduction of the maximum grain size, attributing to the decreased solvus temperature of the γ phase as a result of Cu addition. Consequently, the γ phase and subgrains were refined, and the LDZs were narrowed.

Excellent Superelasticity of Cu-Al-Mn-Cr Shape Memory Single Crystal Obtained Only Through Annealing Cast Polycrystalline Alloy

Excellent superelasticity and fatigue resistance of Cu-Al-Mn-W shape memory single crystal obtained only through annealing polycrystalline cast alloy

Low-cost Cu-based Shape Memory Single Crystals Obtained by Abnormal Grain Growth Showing Excellent Superelasticity

Abnormal Grain Growth in Annealing Cast Cu–Al–Mn–V Alloys and Their Superelasticity

Superelasticity of Different-Orientated Cu–Al–Ni-based Austenite Single Crystals

Microstructure characterization, stress–strain behavior, superelasticity and shape memory effect of Cu–Al–Mn–Cr shape memory alloys

Excellent Shape Recovery Characteristics of Cu-Al-Mn-Fe Shape Memory Single Crystal

Development of Cu-Mn-Ga-based Ferromagnetic Shape Memory Single Crystals

Role of (FeAl) nanoparticles in abnormal grain growth in the annealing of cast Cu-Al-Mn-Fe shape memory alloys

A Novel Ni-alloyed Cu-Al-Ga-Fe Shape Memory Alloy with Excellent Shape Recovery Performance

Microstructure, Martensitic Transformation And Superelasticity Of T1(49) (6)N1(45 1)Cu(5)Cr(0 3) Shape Memory Alloy

Microstructure, Martensitic Transformation and Excellent Shape Memory Effect of Ga-alloyed Cu–Al–Mn–Fe Shape-Memory Single Crystal

Structure and Properties of Ductile Cualmn Shape Memory Alloy Synthesized by Mechanical Alloying and Powder Metallurgy

Superelasticity and Shape Memory Effect in Cu–Al–Mn–V Shape Memory Alloys

Shape Memory and Superelasticity in Polycrystalline Cu–Al–Ni Microwires

Tunable Large Recovery Strain and Wide Response Temperature with Near-Zero Response Interval in Cu-Al-Mn-Fe Single Crystals

A Superior Strength-Ductility Synergy of Al 0.1 CrFeCoNi High-Entropy Alloy with Fully Recrystallized Ultrafine Grains and Annealing Twins

Microstructure Evolution and Tensile Property of a CuMnFeCoNi High-Entropy Alloy During Thermomechanical Treatment

Deformation Behavior of Β1 Phase in Polycrystalline CuAlMnZnZr Shape Memory Alloy with Wide Transformation Hysteresis

Fabrication of single-crystal Fe-Mn-Al-Cu alloys by cyclic heat treatments

Fully Recrystallized Al 0.5 CoCrFeNi High-Entropy Alloy Strengthened by Nanoscale Precipitates