Abstract:In this study, the effect of the mechanical stability of residual austenite in a carburizing layer on the wear performance was explored. First, different amounts of residual austenite were obtained by quenching and cooling 23CrNi3MoA steel after carburization. The effects of the volume fraction, size, and distribution of the residual austenite on the stability and wear performance were investigated. Second, scanning electron microscopy (SEM), transmission electron microscopy (TEM), focused ion beam (FIB), and electron backscatter diffraction (EBSD) analyses were used to characterize the severely deformed layer under friction. In addition, the impacts of the size, morphology, content, and distribution of residual austenite on the wear performance were analyzed. The final results indicated that as the k of the residual austenite decreased, the wear performance of the sample first increased and then decreased. The wear performance improved due to the reduced stability of the residual austenite, which facilitated phase transformation of the residual austenite under friction. The phase transformation of residual austenite into martensite increased the hardness of the wear surface layer. In addition, nanotwinned martensite formed in the severe wear deformation layer. The generation of nanotwins could effectively hinder dislocation movement and store high-density dislocations near the twin boundaries, thereby improving the strength of the wear layer and reducing the wear rate. However, when the residual austenite stability continued to decrease, a large amount of block-like austenite at the grain boundaries underwent excessive plastic deformation during friction. This excessive plastic deformation increased the number of dislocations and led to incoordination between the phase-transformed martensite and the original martensite during deformation. Therefore, crack nucleation increased, and crack propagation accelerated, directly increasing the amount of wear on the wear surface and decreasing the overall wear resistance of the material. In this article, the wear mechanism of residual austenite during dry sliding friction was elucidated, and a basis for reasonable control of residual austenite in production work was provided.

Effect of ammonia addition on microstructure and wear performance of carbonitrided high carbon bearing steel AISI 52100

Effect of nitrided-layer microstructure control on wear behavior of AISI H13 hot work die steel

Influences of Partial Substitution of C by N on the Microstructure and Mechanical Properties of 9cr18mo Martensitic Stainless Steel

The Effect of N Content on the Microstructure and Wear Resistance of Improved High-Carbon Chromium Bearing Steel

Effect of Austempering Temperature on Microstructure Evolution, Mechanical Properties and Wear Resistance of Carbon-free Nano-bainite Steel

Effect of Nanobainite Content on the Dry Sliding Wear Behavior of an Al-Alloyed High Carbon Steel with Nanobainitic Microstructure.

The Microstructure Transformations and Wear Properties of Nanostructured Bainite Steel with Different Si Content

Sliding wear behavior of Cr–Mo–Cu alloy cast irons with and without nano-additives

The effects of load on the microstructure and wear behavior of Co–27Cr–22Fe alloy processed by high-temperature nitriding

Enhancing Dry Sliding Wear Resistance of High-Mn Austenitic Steel by Adding N

Sliding wear of medium-carbon bainitic/martensitic/austenitic steel treated by short-term low-temperature austempering

Microstructure–Wear Resistance Relationship of Nitrogen-Containing High-Speed Tool Steel, AISIM41: Non-equilibrium Solidification

Effect of nitrided-layer microstructure control on wear property of 42CrMo steel

Annealing Effect On The Microstructure Modification And Tribological Properties Of Amorphous Carbon Nitride Films

Microstructure evolution and mechanical properties of martensitic stainless bearing steels with different carbon nitrogen ratios

Effect of Titanium and Nitrogen Additions on the Microstructures and Three-Body Abrasive Wear Behaviors of Fe–B Cast Alloys

Microstructure and properties of hypereutectic high chromium cast iron containing nitrogen

Gaseous carbonitriding of high carbon chromium bearing steel: Correlation between composition, microstructure and stability

Effect of Microstructures on the Tribological Performance of Medium Carbon Steel

Effect of Heat Treatment Temperature on the Microstructure, Wear and Friction of Ni–Nb–V Alloyed Manganese Steel

Analyzing the effect of the mechanical stability of residual austenite on the wear performance