Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Structure and Mechanical Stability of Epoxy Modified Polyurethane Foam under Heat and Stress

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Static and Dynamic Behavior of PU Foams with Multilayer Coatings

Modification of Epoxy Resin by Polyurethane Based on Polyether

Effect of soft segment structure on properties of polyurethane elastomers

Pulverized Polyurethane Foam Particles Reinforced Rigid Polyurethane Foam And Phenolic Foam

Thermal stability of flexible polyurethane foams containing modified layered double hydroxides and zinc borate

Preparation and properties of novel poly(propylene oxide)-block- polylactide-based polyurethane foams

Effects of high functionality polyol on the structure and properties of rigid polyurethane foam

Mechanical and thermal properties of phenolic/glass fiber foam modified with phosphorus-containing polyurethane prepolymer

Multiscale investigation on molecular structure and mechanical properties of thermal‐treated rigid polyurethane foam under high temperature

Eco-Friendly Epoxy-Terminated Polyurethane-Modified Epoxy Resin with Efficient Enhancement in Toughness

Thermal stability and combustion properties of polyurethane foam modified with manganese phytate and expandable graphite

Thermal stimuli response diphenylmethane diisocyanate‐based polyurethane elastomer via adjustable silicon‐induced distinctive microstructure

Durability of PS-Polyurethane Dedicated for Composite Strengthening Applications in Masonry and Concrete Structures

Preparation of a polyurethane‐coated expandable graphite and its flame retardant application in rigid polyurethane foams

Experimental and Numerical Analyses of Thermal Failure of Rigid Polyurethane Foam

Study on epoxy resins modified by polycarbonate polyurethanes

Elaboration of Thermally Performing Polyurethane Foams, Based on Biopolyols, with Thermal Insulating Applications

Study on Mechanical Properties of Polyurethane Cross-Linked P(E-co-T)/PEG Blended Polyether Elastomer

Highly dispersed red phosphorus produced by mechanical milling for enhanced flame retardancy of polyurethane-based foam