Abstract:Inconel 617 nickel-based superalloy with 3 mm wall thickness was welded by laser beam using two different heat input welding parameters. The microstructure of the welded joint was observed by optical microscope and scanning electron microscope, and the mechanical properties of the welded joint at room temperature (25celcius) and high temperature (900celcius) were tested. The results show that the laser welding heat input has a significant effect on the microstructure and mechanical properties of Inconel 617 welded joints. The front width of the laser weld obtained by high heat input (200 J/mm) process parameters is 3.88 mm. The grain size in the middle of the weld fusion zone is coarse, and the grain orientation is disordered. The secondary dendrite arm spacing in the middle of the weld is large (6.71 mu m). The carbide particle size between the dendrites is coarse, and the solidification microsegregation of Mo, Cr alloy elements is serious. The width of heat affected zone is about 0.29 mm. The eutectic structure of gamma+carbide is formed in the grain boundary and grain interior. This is because during the heating process of the welding, the spherical carbide particles and the surrounding austenite in the heat-affected zone liquefy and the eutectic structure is formed during the solidification process after welding. The front width of the laser weld obtained by low heat input (90 J/mm) process parameters is 2.28 mm, the grains inside the weld are columnar which is formed by epitaxial growth along the fusion line and directional solidification along the heat flow direction. The secondary dendrite arm spacing in the middle of the weld is small (2.26 mu m), the carbide particles between dendrites are small, and the width of heat affected zone is about 0.15 mm. The tensile strength test at room temperature (25celcius) shows that the welded joints obtained under high heat input fracture from the middle of the weld, and the tensile strength and elongation decrease, which is caused by the segregation of solid solution elements in the weld. The welded joints obtained under low heat input fracture from the base metal. At high temperature (900celcius), all samples fracture from the base metal, which is due to the weakening of the grain boundary of the base metal at high temperatures.

Laser Welding of a Selective Laser Melted Ni-base Superalloy: Microstructure and High Temperature Mechanical Property

Effect of Welding Speed on Microstructure and Mechanical Properties of Selective Laser Melting Inconel 625 Alloy Laser Welded Joint

Effect of Welding Thermal Treatment on the Microstructure and Mechanical Properties of Nickel-Based Superalloy Fabricated by Selective Laser Melting

Microstructure and Mechanical Properties of High Power CO2 Laser Welded Inconel 625 Nickel Based Alloy

Study on laser welding of a Ti-22Al-25Nb alloy: Microstructural evolution and high temperature brittle behavior

CHARACTERIZATION OF MICRO STRUCTURAL AND MECHANICAL PROPERTIES OF INCONEL 625/A 517 HIGH STRENGTH QUENCHED AND TEMPERED STEEL DISSIMILAR WELDS

Selective laser melting of the hard-to-weld IN738LC superalloy: Efforts to mitigate defects and the resultant microstructural and mechanical properties

Experiments and modeling of microstructural and mechanical behaviors of laser-welded Ni-based superalloy at high temperatures

A Comparable Study on Laser Welding Behaviors of Selective Laser Melted 304 Stainless Steel, Inconel 718 Superalloy and Ti-6Al-4V Alloy

Effect of heat input on microstructure and mechanical properties of laser welded joint of Inconel 617 nickel-based superalloy

The Microstructures and Mechanical Properties of a Welded Ni-Based Hastelloy X Superalloy

Study on the Weldability, Microstructure and Mechanical Properties of Thick Inconel 617 Plate Using Narrow Gap Laser Welding Method

High-temperature mechanical properties of nickel-based superalloys manufactured by additive manufacturing

Study on Laser Beam Welding/superplastic Forming Technology of Multi-Sheet Cylinder Sandwich Structure for Inconel718 Superalloy with Ultra-Fine Grains

Laser-hybrid welding of 4716MA0 nickel-based alloy: effects of laser power on microstructure and properties

Microstructures and Mechanical Behaviors of Additive Manufactured Inconel 625 alloys via Selective Laser Melting and Laser Engineered Net Shaping

Microstructure and Tribological Behaviour of Inconel-625 Superalloy Produced by Selective Laser Melting

Ultrasonic vibration induced the improvement of mechanical properties and fracture behavior of Inconel 690 alloy joint during laser welding

Effect of laser welding parameters on the temperature distribution, microstructure and mechanical properties of dissimilar weld joint of Inconel 625 and stainless steel 304

Dissimilar Metal Welding of Ti6Al4V and Inconel 718 Through Pulsed Laser Welding-Induced Eutectic Reaction Technology

Microstructure and Mechanical Properties of Superalloy Laser Welded Joints for GH3625 Fabricated by Laser Additive