Elucidating friction properties and strengthening mechanisms of Ni-based surfacing layer containing 9R phase
Le Zhang,Jiankun Xiong,Yang Li,Jian Xu,Xue Li,Haibo Zhang,Zhuo Chen,Jianping Yang,Wuxing Ou,Guijun Mao,Ting Li,Fuheng Nie,Xinjian Yuan
DOI: https://doi.org/10.1016/j.surfcoat.2023.129751
IF: 4.865
2023-06-27
Surface and Coatings Technology
Abstract:This study analyzed the strengthening mechanisms and friction properties of Inconel 625 surfacing layers fabricated by plasma transfer arc surfacing (PTA-surfacing) in ball-on-disc friction tests at room temperature and 650 °C. Results showed that Inconel 625 exhibited poor tribological performance at room temperature, but excellent at 650 °C. The average Vickers hardness of the high-temperature wear area (1.6826 ± 0.4059 GPa) was higher than that of the room temperature wear area (1.3900 ± 0.1875 GPa). The coefficient of friction for Inconel 625 decreased from 0.5362 at room temperature to 0.2846 at 650 °C. The wear rates of Inconel 625 at 650 °C and room temperature were 1.2063 × 10 −5 mm 3 /N·m and 20.9740 × 10 −5 mm 3 /N·m, respectively. The wear mechanisms at 650 °C were mainly abrasive, adhesion, oxidation wear, and some degree of delamination wear. The microstructural characterizations revealed that the wear subsurface at 650 °C comprised polycrystalline-mixed oxide layers (Ni(Cr,Fe) 2 O 4 , (Cr,Fe) 2 O 3 , and NiO), gradient grain refinement, nanoscale precipitations (M 23 C 6 , M 6 C, and laves), 9R structural phases, I-type twinning, and high-density dislocations, which synergistically enhance the outstanding high-temperature friction properties and strength.
physics, applied,materials science, coatings & films