Effect of Modification Treatment on the Microstructure and Tensile Properties of Mg2Si/AZ91 Composites In-Situ Synthesized by Incorporating Silica Fume

Wenlong Zhang,Xianfeng Li,Dongyan Ding,Ping Gao

DOI: https://doi.org/10.1016/j.jmatprotec.2018.12.031

IF: 6.3

2018-01-01

Journal of Materials Processing Technology

Abstract:In-situ Mg2Si/AZ91 composites were synthesized by incorporating silica fume and three modifiers including CeLa, Sb and AlSr. Effect of the modification treatment on the microstructure and tensile properties was investigated. It was found that among the three modifiers, Sb was the most effective in grain refinement of the matrix while AlSr was the most beneficial to size-reduction of the Mg2Si reinforcement. Adding CeLa facilitated formation of large needle-like Mg2Si while the addition of Sb was favorable for formation of large polygonal Mg2Si. For comparison, adding AlSr facilitated generation of fine granular Mg2Si. Among the three composites, the AlSr-modified composite showed the highest tensile strength and ductility, which was mainly due to the formation of fine, granular and dispersed Mg2Si and Mg17Al12 phases after AlSr modification. The highest tensile strength of 272 MPa obtained by using both silica fume and AlSr modifier was much higher than that by incorporating hollow fly ash cenosphere, indicating that the tensile strength of in-situ Mg2Si/AZ91 composites could be significantly improved by incorporating both silica fume and AlSr modifier.