Abstract:To further the anti-ablation property of carbon/carbon composites (C/Cs) at extreme-high temperature, Cr-ZrC coating is fabricated on SiC-coated C/Cs. The anti-ablation properties of the ZrC coatings modified by various content of Cr are tested by oxyacetylene flame (heat flux: 2.4 MW/m(2)). Compared with pure ZrC coating, the ablation resistance property of the sprayed Cr-ZrC coating indicates an effective improvement. Cr acts as an accelerant by facilitating the liquid ZrO2 sintering and form a close structure. This dense structure can alleviate oxygen penetration. As the content of Cr increase (10 wt%, 15 wt% and 20 wt%), after cooling can also detect the retaining of tetragonal-ZrO2 (t-ZrO2). The phase transformation from t-ZrO2 to monoclinic ZrO2 (m-ZrO2) can lead to the volume expansion. The retaining of t-ZrO2 shows the phase transformation is impeded, which contributes to the thermal stability of the Cr modified ZrC coating. In the specimen, oxygen mainly diffuse through micropores, microcracks and grain boundaries. For Cr-ZrC coating, these diffuse ways could be partly or completely sealed by melted Zr-O-Cr coating during ablation test, which can effectively protect C/Cs during the oxyacetylene ablation test. When the content of Cr is 15 wt%, on the surface can form dense dendritic structure, which can effectively protect C/Cs from ablation.

Microstructure and Ablation Properties of SiC/ZrB2–SiC/ZrB2/SiC Multilayer Coating on Graphite

Ablation resistance of ZrB2SiC/SiC coating prepared by pack cementation for graphite

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

A Multilayer SiC/ZrB2/SiC Ablation Resistance Coating for Carbon/Carbon Composites

Microstructure, surface stress and surface temperature response of ZrB2–SiC based coatings

Ablation behavior and mechanism of SiCnw modified SiC-ZrC coating for graphite under a plasma ablation flame

Microstructure and Ablation Mechanism of SiC-ZrC-Al2O3 Coating for SiC Coated C/C Composites under Oxyacetylene Torch Test

SiC/ZrB2–SiC–ZrC Multilayer Coating for Carbon/carbon Composites Against Ablation

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Ablation Resistance of ZrB2–SiC Coating Prepared by Supersonic Atmosphere Plasma Spraying for SiC-coated Carbon/carbon Composites

Ablation Resistance of Different Coating Structures for C/ZrB2–SiC Composites under Oxyacetylene Torch Flame

Ablation Resistance of SiC‐modified ZrC Coating Prepared by SAPS for SiC‐coated Carbon/carbon Composites

Ablation Behavior of ZrC and ZrO2 Coatings on SiC Coated C/C Composites under Oxyacetylene Torch with Different Heat Fluxes

ZrB2-SiC coating to protect carbon/carbon composites against ablation

Ablation resistance and mechanism of SiC/ZrC-ZrB2 double layer coating for C/C composites under plasma flame

Ablation behavior of ZrB 2 –SiC protective coating for carbon/carbon composites

Ablation Resistance of SiC–ZrC Coating Prepared by a Simple Two-Step Method on Carbon Fiber Reinforced Composites

Microstructure and High Temperature Anti-Ablation Behavior of Cr-modified ZrC Coating for SiC-coated Carbon/carbon Composites

Ablation Resistance and Mechanism of SiC/ZrC-ZrB2double Layer Coating for C/C Composites under Plasma Flame

Microstructure Characteristics and Ablation Behavior of an Al1.92 Cr0.08 O3-SiC-ZrC Anti-Ablation Coating

Evaluation of Ablation Resistant ZrC-SiC Multilayer Coating for SiC Coated Carbon/carbon Composites under Oxyacetylene and Laser Conditions