Abstract:The thermal stability of the dual phase AlCrFeCoNiCu 0.5 high entropy alloy thin films at up to 600 °C under vacuum was studied through detailed characterization. The evolution of microstructure and chemical composition was revealed by X-ray diffraction, transmission Kikuchi diffraction and transmission electron microscopy . Also, the mechanical properties were measured by nanoindentation . Although the crystalline phase of all the HEA thin films was BCC-dominated, the FCC phase fraction increased from 16.6% (as-deposited) to 28.1% (600 °C-annealed). The as-deposited films exhibited a columnar morphology with an average grain size of 106.1 nm for length and 31.3 nm for width and remained the columnar shape until 600 °C. The columnar grains showed an increasing tendency of size at 200 °C (221.3 nm and 45.6 nm for length and width) and 400 °C (283.9 nm and 56.2 nm). At 600 °C, the columnar grain size decreased to 211.8 nm in length and 59.3 nm in width. Concurrently, the occurrence of new equiaxed grains was observed with an average diameter of 42.4 nm. The reduction of columnar grain size and the formation of equiaxed grains at 600 °C were explained based on the energy dispersive spectroscopy. Although no preferential evaporation was found, the elemental distribution revealed the formation of two secondary phases, i.e., Cu-rich FCC phase and Cr-rich BCC phase. The nanoindentation results indicated that the mechanical properties increased as the increase of annealing temperature. The hardness and elastic modulus of 600 °C-annealed sample were 8.5 ± 0.3 GPa and 205.4 ± 3.5 GPa, respectively, which were 10.4% and 41.5% higher than those of the as-deposited thin film. These findings are critical for a fundamental understanding of the microstructure and properties change of the dual-phase HEA thin films in high working temperatures.

High Hardness Dual-Phase High Entropy Alloy Thin Films Produced by Interface Alloying

A Dual-Phase Fe-Co-Ni-Cr-Mn High Entropy Alloy Thin Film with Superior Strength and Corrosion-Resistance

High Strength Dual-Phase High Entropy Alloys with a Tunable Nanolayer Thickness

Study on Precipitation in (cocrfemnni)90al6ti4 High Entropy Alloy

Ultrahigh Specific Hardness of Co-Ni-V-Al Medium Entropy Alloy Thin Films

Introducing a new heterogeneous nanocomposite thin film with superior mechanical properties and thermal stability

Microstructure and mechanical properties of Al-Fe-Co-Cr-Ni high entropy alloy fabricated via powder extrusion

Realizing strength-ductility combination of Fe3.5Ni3.5Cr2MnAl0.7 high-entropy alloy via coherent dual-phase structure

Designing High Entropy Alloys with Dual fcc and bcc Solid-Solution Phases: Structures and Mechanical Properties

Abnormal hardening and amorphization in an FCC high entropy alloy under extreme uniaxial tension

Empirical design of single phase high-entropy alloys with high hardness

A promising new class of high-temperature alloys: eutectic high-entropy alloys

The microstructural evolution of dual phase high entropy alloy thin films by annealing

Investigation of mechanical and corrosion properties of light and high hardness cast AlTiVCrCu 0.4 high entropy alloy

High strength and ductility in a dual-phase hetero-structured AlCoCrFeNi2.1 eutectic high-entropy alloy by powder metallurgy

The phase stability at intermediate-temperature and mechanical behavior of the dual-phase AlCoCr0.5FexNi2.5 high entropy alloys

High-content ductile coherent nanoprecipitates achieve ultrastrong high-entropy alloys

A high-entropy alloy with hierarchical nanoprecipitates and ultrahigh strength

Novel as-cast NiAlCoFeNb dual-phase high-entropy alloys with high hardness

High temperature deformation behavior of dual-phase Al0.6CoCrFeNi high-entropy alloys

A dual-phase alloy with ultrahigh strength-ductility synergy over a wide temperature range