Effects of Grain Size and Temperature on the Energy Storage and Dielectric Tunability of Non-Reducible BaTiO3-based Ceramics

Chaoqiong Zhu,Xiaohui Wang,Qiancheng Zhao,Ziming Cai,Zhenyong Cen,Longtu Li

DOI: https://doi.org/10.1016/j.jeurceramsoc.2018.11.034

IF: 5.7

2018-01-01

Journal of the European Ceramic Society

Abstract:BaTiO3-based ceramics with various grain sizes (136-529 nm) are prepared through a chemical coating method followed by sintering in a reducing atmosphere. Effects of grain size and temperature on electric properties, energy-storage properties, and dielectric tunability are studied via Current-Field (J-E) curves, ferroelectric hysteresis loops, Capacitance-Voltage (C-V) curves and Thermally stimulated depolarization currents (TSDC). At all temperatures, fine-grain ceramics yield a lower energy density but a higher energy efficiency under the same electric field, owing to a lower ferroelectric contribution. Meanwhile, fine-grain ceramics exhibit a higher maximum energy density due to their higher breakdown strength. Fine-grain ceramics with the grain size of 136 nm have the maximum energy density of 0.41 J/cm(3) under the breakdown strength of 75 kV/cm, the corresponding efficiency is 81%. C-V curves show that fine-grain ceramics have better bias-field stability. According to TSDC results, fine-grain ceramics exhibit fewer oxygen vacancies and a higher relaxation activation energy.