Abstract:Dissimilar metal welds (DMWs) between high-Cr martensitic heat-resistant steels and nickel-based alloys with nickel-based filler metals are widely used in fossil-fired power plants. Reports of premature failures of DMW joints have attracted considerable attention as such occurrences in the field can lead to significant economic loss and safety issues. Moreover, a comprehensive understanding of the high-temperature performance of new types of DMWs is lacking. In this work, creep tests were conducted over a stress range of 140-260 MPa at of 600 and 620 'C. A shift in the fracture location with variations in stress was observed, with three typical failure modes. At high stress levels (240-260 MPa), the DMW fractured in the base metal (BM) of martensitic steel, accompanied by a large degree of plastic deformation. At intermediate stress levels (200-240 MPa), the DMW fractured in the fine-grained heat-affected zone (FGHAZ) and the inter-critical heat-affected zone (ICHAZ), with creep cavities around coarsened carbides, indicating a typical type IV crack. At low stress levels (140-200 MPa), the DMW fractured in a mixed mode involving three stages. First, a crack initiated at the interface between the nickel-based weld metal and the martensitic steel, which was attributed to the interaction between the oxidation behavior of the martensitic steels and the thermal stress arising from the mismatch in the coefficients of thermal expansion. Second, the crack deflected into the FGHAZ/ICHAZ and developed into a type IV crack mode. Finally, the crack propagated into the adjacent BM, featuring significant plastic deformation. In addition, in the stress-LMP (Larson-Miller parameter) plot, the creep life at a relatively low stress level was shorter than that predicted by linear extrapolation of the data obtained at a high stress level, indicating a premature failure tendency at low stress. This premature failure tendency can be attributed to microstructure degradation in HAZs and preferential oxidation at the interface at low stress levels.

Effect of Loading Mode on Fracture Behavior of CrNiMoV Steel Welded Joint in Simulated Environment of Low Pressure Nuclear Steam Turbine

Stress Corrosion Cracking of NiCrMoV Steel Welded Joint under Applied Load in Simulated Environment of Low Pressure Nuclear Steam Turbine

Effect of Overlaying Welding Repair on Stress Corrosion Cracking Sensitivity of Low-Pressure Nuclear Steam Turbine Rotor in the Simulated Environment

Fracture Location Transition in Constant Load Tests of a NiCrMoV Steel Welded Joint

SCC Fracture Location Shifting Affected by Stress-Controlled Fatigue Damage of NiCrMoV Steel Welded Joints

Effect of Fatigue Damage on Stress Corrosion Cracking Sensitivity of Nuclear Steam Turbine Welded Joint

Stress corrosion crack propagation affected by microstructures for nuclear steam turbine rotor steels in the simulated environment

Study on Stress Corrosion Cracking Sensitivity of CrNiMoV Steam Turbine Rotor Steels

An Experimental Investigation of In-Plane Constraint Effect on Local Fracture Resistance of A Dissimilar Metal Welded Joint

Investigation of Local Brittle Zone in Multipass Welded Joint of NiCrMoV Steel with Heavy Section

Effect of Mechanical Heterogeneity on Strain and Stress Fields at Crack Tips of SCC in Dissimilar Metal Welded Joints

Low Cycle Fatigue Performance of 25cr2ni2mov Welded Joints

Effect of Microstructure on Local Strain Hardening Behavior along an Equal Toughness Matching Welded Joint of a 30cr2ni4mov Welded Rotor

Fracture Location Shift of Dissimilar Metal Welds under Coupled Thermal-Stress Effect

Stress Corrosion Crack Growth Rate of Welded Joint Used for Low-Pressure Rotor of Nuclear Turbine in Oxygenated Pure Water at 180 °C

Microstructure and Stress Corrosion Cracking of a SA508-309L/308L-316L Dissimilar Metal Weld Joint in Primary Pressurized Water Reactor Environment

Local fracture behavior in an Alloy 52M dissimilar metal welded joint in nuclear power plants

EFFECT OF DYNAMIC LOADING ON FRACTURE BEHAVIOR OF WELDED JOINTS OF STRUCTURAL STEEL

A Comparative Study on the Cyclic Plasticity and Fatigue Failure Behavior of Different Subzones in CrNiMoV Steel Welded Joint

Experimental Investigation of Fatigue Crack Growth Behavior of the 2.25cr1mo0.25v Steel Welded Joint Used in Hydrogenation Reactors