Abstract:The causes of many blade fractures of a steam turbine in a power plant were studied by means of macro analysis, mechanical tests, metallographic examination, SEM and X-ray fluorescence spectrum analysis (XRF). The results show that the blade cracks due to corrosion fatigue. Cl −,K +react with the turbine blades in the steam environment in physical, chemical and electrochemical ways, causing local spot corrosion on the blades, forming corrosion pits. In addition, the steam condensated has an erosion effect on the blades, both of which form a corrosion fatigue source. The autocatalytic process of block cell is formed when Cl −, K + react with the turbine blades. Under the action of combined load, the current density <math>i</math> of activation dissolution of metal can be expressed as a function of complex stress state.Crack growth has an important relationship with stress, depth and width of corrosion pits. The blade cracks are determined by threshold nominal stress range for crack elongation<math>Δσth</math>, which depends on the depth and width of corrosion pit. The combined alternating stress directly promotes the crack propagation until the fracture fail under the external conditions of alternating stress formed by tensile force, bending force, torsion force, and exciting force.

Study on Stress Corrosion Cracking Sensitivity of CrNiMoV Steam Turbine Rotor Steels

Stress corrosion crack propagation affected by microstructures for nuclear steam turbine rotor steels in the simulated environment

Stress Corrosion Cracking of NiCrMoV Steel Welded Joint under Applied Load in Simulated Environment of Low Pressure Nuclear Steam Turbine

Effect of Overlaying Welding Repair on Stress Corrosion Cracking Sensitivity of Low-Pressure Nuclear Steam Turbine Rotor in the Simulated Environment

Stress Corrosion Crack Growth Rate of Welded Joint Used for Low-Pressure Rotor of Nuclear Turbine in Oxygenated Pure Water at 180 °C

Experimental Investigation of Stress Corrosion Characteristics for 16mnr Steel in Nitrate Solution

Stress Corrosion Cracking Growth Rate Prediction Model for Nuclear Power Turbine Rotor Steel in a Simulated Environment

Effect of Loading Mode on Fracture Behavior of CrNiMoV Steel Welded Joint in Simulated Environment of Low Pressure Nuclear Steam Turbine

Effect of Fatigue Damage on Stress Corrosion Cracking Sensitivity of Nuclear Steam Turbine Welded Joint

Analysis on Premature Fracture of X12CrMoWVNbN10-1-1 Steel for USC Steam Turbine Rotors

Comparisons of 30cr2ni4mov Rotor Steel with Different Treatments on Corrosion Resistance in High Temperature Water

Comparative study on the stress corrosion cracking of a new Ni-advanced high strength steel prepared by TMCP, direct quenching, and quenching & tempering

Study on Stress Corrosion Cracking Growth of Turbine Rotor in Power Plant

Improvement of Stress Corrosion Cracking Resistance by Low Cycle Fatigue of a CrNiMoV Steel

Pitting Corrosion and Stress Corrosion Cracking Around Heat Affected Zone in Welded Joint of CrNiMoV Rotor Steel in Chloridized High Temperature Water

Experimental Investigations On Mechanical Properties Of A High Cr Ferritic Steel For Usc Steam Turbine Rotor

Investigation of Stress Corrosion Cracking Resistance of Irradiated 12Cr Ferritic-Martensitic Stainless Steel in Supercritical Water Environment

Stress Corrosion Cracking Behaviour of 1cr12ni2w1mo1v Steel after Plasma Hardening

Study of cracks in the last-stage rotor blade of a steam turbine and the corrosion fatigue properties of its materials

Assessment of tensile deformation and fracture toughness behavior of 10Cr steel at ambient and high temperatures

Analysis on corrosion fatigue cracking mechanism of 17-4PH blade of low pressure rotor of steam turbine