Enhance coking tolerance of high-performance direct carbon dioxide-methane solid oxide fuel cells with an additional internal reforming catalyst
Tian Li,Yang Yang,Xinxin Wang,Keqing Zheng,Shuanglin Shen,Xuemei Ou,Bin Lin,Peizhong Feng,Shaorong Wang,Yihan Ling
DOI: https://doi.org/10.1016/j.jpowsour.2021.230533
IF: 9.2
2021-11-01
Journal of Power Sources
Abstract:Carbon deposition can be observed on the surface of Ni catalyst surface because of its high catalytic activity of hydrocarbon cracking, and thus cause the degradation of cell performance. In this work, anode supported single cells without and with the additional internal reforming catalyst NiFe2O4-GDC are successful assembled, and then used to characterize electrochemical performance and carbon tolerance in H2 and 50%CO2–50%CH4 fuels. Both single cells without and with NiFe2O4-GDC demonstrate similarly high electrochemical performance and low electrode polarization resistance fueled in H2, and the peak power densities are 1037.15 and 1163.36 mW/cm2 at 800 °C, respectively, the difference of which derived from the ohmic impedance and the electrode polarization resistance. Interestingly, to better understand the contribution of different electrode polarization impedances, the distribution of relaxation time (DRT) analysis is used to distinguish different rate-limiting steps with high resolution. While 50%CO2–50%CH4 fuel is applied, single cells with internal reforming catalyst NiFe2O4-GDC demonstrates high electrochemical performance (1046.72 mW/cm2 at 800 °C), long-term stability and excellent carbon tolerance from the Raman scanning analysis. All preliminary experimental results suggest that high performance and coking tolerance can be obtained for direct carbon dioxide-methane solid oxide fuel cells with an additional internal reforming catalyst.
energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical