Abstract:Microstructure stability directly affects the performance degradation of hot-end structural parts such as turbine discs. In this research, long-term (10–10000 h) thermal exposure experiments were conducted on a Ni–Co–Cr type superalloy at 800 °C. The mechanical properties were obtained through high-temperature (750 °C) tensile tests. Subsequently, the microstructure evolution process, including intragranular γ′ and μ phases, and the initiation and propagation of defects were systematically and thoroughly studied. The results showed that intragranular γ′ precipitates coarsened under thermal exposure. After 100 h of thermal exposure, μ phases were observed near the intergranular γ′ precipitates and grain boundaries. The size and volume fraction of the μ phase initially increased, and then remained relatively stable. Numerous cracks formed on the plane of the μ phases and intergranular γ′ precipitates. With an increase in tensile stress, these cracks interconnected and propagated along the intergranular γ′ precipitates, leading to the formation of pores. Moreover, because the size of the intragranular γ′ precipitates exceeded 80 nm, the critical resolved shear stress (CRSS) was primarily activated by the Orowan bypassing mechanism. Notably, the CRSS of dislocation motion, such as stacking fault, strong-coupled shearing, and Orowan bypassing, decreased with increasing intragranular γ′ precipitate size. Therefore, the intragranular strength also weakened and the intragranular γ′ precipitates coarsened under continuous thermal conditions. This research on precipitate evolution and failure mechanisms will contribute to a better understanding of failure mechanisms for Ni–Co–Cr-based superalloys.

Microstructure and Stress-Rupture Life of High W-content Cast Ni-based Superalloy after 1000–1100 °C Thermal Exposures

Effects of Microstructure and Lattice Misfit on Creep Life of Ni-based Single Crystal Superalloy During Long-Term Thermal Exposure

Based on Damage Caused by Microstructure Evolution During Long-Term Thermal Exposure to Analyze and Predict Creep Behavior of Ni-based Single Crystal Superalloy

Investigation of Microstructural Stability and Tensile Deformation Behavior of a Novel PM Ni-based Superalloy During Long-Term Thermal Exposure

Effect of Precipitates on High-Temperature Tensile Strength of a High W-content Cast Ni-based Superalloy

Influence of thermal exposure on microstructure and stress rupture property of a Re-containing Ni-based single crystal superalloy

Effect of Microstructure on High Temperature Mechanical Properties in Forming Ni-20cr-10mo-10co Superalloy

Microstructural Evolution and Tensile Property of 1cr15ni36w3ti Superalloy During Thermal Exposure

Effect of Μ Precipitation and Γ′ Evolution on Intra/intergranular Strength of Ni-Co-Cr-based Superalloys after 800 ℃ Thermal Exposure

Influence of thermal exposure on microstructural stability and tensile properties of a new Ni-base superalloy

Avoiding microstructural instabilities in high tungsten containing superalloys by adjusting Al content

Effects of Long Term Thermal Exposure on Microstructure and Mechanical Property Evolution of a New Wrought Ni–Fe Based Superalloy

Understanding the Fracture Mechanisms of Ni–Co–Cr-type Superalloys: Role of Precipitate Evolution and Strength Degradation

Mechanical Properties, Microstructure and Fracture Mechanism of 95W-3.5Ni-1.5fe Alloys at High Temperature

Effect of Long-Term Aging on the Microstructures and Stress Rupture Properties of a Ni-Based Single Crystal Superalloy at 980°C

Effect of μ precipitation and γ′ evolution on intra/intergranular strength of Ni-Co-Cr-based superalloys after 800 °C thermal exposure

Coupling effects of tungsten and molybdenum on microstructure and stress-rupture properties of a nickel-base cast superalloy

Mechanical Degradation Behavior and Γ′ Coarsening Mechanism of a Ni-based Superalloy During Long-Term High-Temperature Thermal Exposure

Effect of thermal exposure on the stability of carbides in Ni–Cr–W based superalloy

Effect of Overheating Treatment on Microstructure and Stress Rupture Properties of a Nickel-Based Single-Crystal Superalloy

Microstructure Characterization of Ni-Based Superalloys During Thermal Exposure