Abstract:The micro-degradation processes related to the ductile-brittle transition are crucial for revealing hydrogen embrittlement mechanisms. This study investigates the evolution and transition of hydrogen-assisted damages in notched duplex stainless steel using a combination of microstructural characterization, numerical simulations, and mechanistic models. The results show that the brittle area of the fracture surface increases rapidly with decreasing cathodic potential, accompanied by the fractography transition in a sequence of voids, voids mixed with quasi-cleavage, and quasi-cleavage. While hydrogen-assisted dislocation emission from the void surface and stress concentration at the phase boundary promote nanovoid growth, hydrogen-enhanced plasticity facilitates preferential void growth along the ferrite block. At higher hydrogen concentrations, ferrite cleavage cracking may originate from prolate voids and hydrogen-augmented Cottrell dislocation reactions, reducing plastic strain near the crack tip and hence diminishing the formation of vacancies as void nuclei. Previous studies have focused on the statistics of hydrogen's effect on void size. This work demonstrates the dislocation mechanism of hydrogen-assisted void growth and provides new insights into the development of micro-mechanism-based models to predict hydrogen embrittlement.

Effects of Α′ Martensite and Deformation Twin on Hydrogen-Assisted Fatigue Crack Growth in Cold/warm-Rolled Type 304 Stainless Steel

The dependence of fatigue crack growth on hydrogen in warm-rolled 316 austenitic stainless steel

Warm Deformation Enhances Strength and Inhibits Hydrogen Induced Fatigue Crack Growth in Metastable 304 and 316 Austenitic Stainless Steels

Anomalous Evolution of Corrosion Behaviour of Warm-Rolled Type 304 Austenitic Stainless Steel

The role of hydrogen in promoting differences in fatigue crack growth rates observed in Type 304/304L stainless steel at elevated temperature

Effects of External Hydrogen on Hydrogen Transportation and Distribution Around the Fatigue Crack Tip in Type 304 Stainless Steel

Effect of Strain-Induced Martensite on Hydrogen Embrittlement of Austenitic Stainless Steels Investigated by Combined Tension and Hydrogen Release Methods

Hydrogen-induced Delayed Fracture Behavior of Notched 316L Austenitic Stainless Steel: Role of Grain Refinement

Hydrogen Effect on the Fatigue Crack Growth in Austenitic Stainless Steel Investigated by a New Method Based on Nanohardness Distribution

Embrittlement of Notched Duplex Stainless Steel: Role of Hydrogen-Assisted Void Growth and Cleavage

Effects of Hydrogen Pressure on Hydrogen-Assisted Fatigue Crack Growth of Cr-Mo Steel

Effect of pre-strain on critical conditions for hydrogen-induced delayed cracking and crack nucleation characteristic of DP1180 steel

The difference in fatigue crack growth induced by internal and external hydrogen in selective laser melted 304L stainless steel

Hydrogen Effect On The Deformation Behavior Of Austenitic Stainless Steels Investigated By Nanoindentation

Hydrogen embrittlement resistance of TWIP (twinning-induced plasticity) steel in high pressure hydrogen environment

Effects of finish rolling deformation on hydrogen-induced cracking and hydrogen-induced ductility loss of high-vanadium TMCP X80 pipeline steel

Modelling of Hydrogen Distribution at the Fatigue Crack Tip of Austenitic Stainless Steels in Internal and External Hydrogen Tests

Effects of grain boundary character distribution on hydrogen-induced cracks initiation and propagation at different strain rates in a nickel-saving and high-nitrogen austenitic stainless steel

Hydrogen Effect on the Deformation Evolution Process in Situ Detected by Nanoindentation Continuous Stiffness Measurement

Effects of defect size and location on high cycle fatigue life of a maraging stainless steel at ambient and cryogenic temperatures

Role of grain size and anisotropy of neighboring grains in hydrogen‐assisted intergranular fatigue crack initiation in austenitic stainless steel