Abstract:<p>The fatigue crack growth rate of warm-rolled AISI 316 austenitic stainless steel was investigated by controlling rolling strain and temperature in argon and hydrogen gas atmospheres. The fatigue crack growth rates of warm-rolled 316 specimens tested in hydrogen decreased with increasing rolling temperature, especially 400 °C. By controlling the deformation temperature and strain, the influences of microstructure (including dislocation structure, deformation twins and α′ martensite) and its evolution on hydrogen-induced degradation of mechanical properties were separately discussed. Deformation twins deceased and dislocations became more uniform with the increase in rolling temperature, inhibiting the formation of dynamic α′ martensite during the crack propagation. In the cold-rolled 316 specimens, deformation twins accelerated hydrogen-induced crack growth due to the α′ martensitic transformation at the crack tip. In the warm-rolled specimens, the formation of α′ martensite around the crack tip was completely inhibited, which greatly reduced the fatigue crack growth rate in hydrogen atmosphere.</p>

What problem does this paper attempt to address?

The paper primarily investigates the fatigue crack growth behavior of 316 austenitic stainless steel subjected to warm rolling in a hydrogen environment. Specifically, the paper aims to address the following issues: 1. **Effect of Temperature on Microstructure**: By controlling the warm rolling conditions (such as temperature and strain), the study examines the microstructures formed at different temperatures (including dislocation structures, deformation twins, and α' martensite) and their evolution's impact on hydrogen embrittlement sensitivity. 2. **Fatigue Crack Growth Rate in Hydrogen Environment**: The study explores how the fatigue crack growth rate of warm-rolled 316 stainless steel varies with temperature in argon and hydrogen environments and analyzes the underlying mechanisms. 3. **Changes in Material Properties under Different Warm Rolling Conditions**: The research investigates how the mechanical properties (such as yield strength, tensile strength, and fracture toughness) of the material change under different warm rolling conditions (such as 25°C, 200°C, 400°C) and explores how these changes affect the fatigue crack growth behavior. Through the above studies, the paper aims to reveal how different microstructural characteristics formed during warm rolling influence the fatigue performance of the material in a hydrogen environment, providing a theoretical basis for further optimization of material design and application.

The dependence of fatigue crack growth on hydrogen in warm-rolled 316 austenitic stainless steel