Effect of Cooling Rate on Gamma ' Precipitate of Dz4125 Alloy under High Thermal Gradient Directional Solidification
Zhang Weiguo,Liu Lin,Huang Taiwen,Zha Xinbao,Yu Zhuhuan,Fu Hengzhi
DOI: https://doi.org/10.3321/j.issn:0412-1961.2009.05.013
IF: 1.797
2009-01-01
ACTA METALLURGICA SINICA
Abstract:The mechanical properties of Ni-based superalloy are mainly determined by quantity, shape, size and distribution of gamma' precipitates. For a given alloy, the quantity, shape, size and distribution of gamma' precipitates are mostly affected by solidification parameters during solidification process. In present, the influence of solidification parameters on gamma' precipitates has been extensively reported. But unfortunately, these researches on gamma' precipitates under as cast condition are mostly intuitive description of solidification phenomena and the in-depth research on the influence of solidification parameters on the morphology, distribution and size of gamma' precipitates is little, especially under high thermal gradient directional solidification. In this paper, the influence of cooling rates on the morphology, size and distribution of gamma' precipitates in dendrite core and interdendritic areas of directionally solidified nickel-based superalloy DZ4125 was investigated under high thermal gradient about 500 K/cm. The cooling rates used in this experiment were 2.525, 5.15, 13.17, 25.875 and 36.4 K/s, respectively. The relative mechanisms of changes in the morphology, distribution and size of gamma' precipitates were discussed. These results show that, with cooling rate increasing, the dendrite microstructure of DZ4125 alloy becomes fine. At the solidification rate of 36.4 K/s, the dendrite morphology changes to a superfine dendrite solidification mode. In this process, the morphology of gamma' precipitates changes from cubic to spheric shape and the sphericized speed of gamma' precipitates in dendrite core quicker than in interdendritic. Furthermore, the average size of gamma' precipitates decreases gradually so that they become well-distributed in both dendrite core and interdendritic. This average size of gamma' precipitates in dendrite core is smaller than in interdendritic, however the difference in size decreases with cooling rate increasing. These changes in the morphology, distribution and size of gamma' precipitates result mainly from the degree of supersaturation of solute in gamma solid solution Delta X, degree of undercooling in gamma solid solution Delta T, critical precipitation nucleation work of gamma' precipitate Delta G* and solution diffusion coefficient in gamma solid solution D caused by altering cooling rate.