Catalytic deactivation mechanism research over Cu/SAPO-34 catalysts for NH3-SCR (I): The impact of 950 °c hydrothermal aging time

Dequan Fan,Jun Wang,Tie Yu,Jianqiang Wang,Xiaoqian Hu,Meiqing Shen

DOI: https://doi.org/10.1016/j.ces.2017.10.032

IF: 4.7

2018-01-01

Chemical Engineering Science

Abstract:This work firstly unveiled deactivation mechanism of Cu/SAPO-34 after 950 °C aging.

What problem does this paper attempt to address?

Deactivation and Regeneration for the SO2-Poisoning of a Cu-SSZ-13 Catalyst in the NH3-SCR Reaction

Yan Wang,Zhaoqiang Li,Rongrong Fan,Xin Guo,Cheng Zhang,Yu Wang,Zhiyong Ding,Rong Wang,Wei Liu

DOI: https://doi.org/10.3390/catal9100797

IF: 3.9

2019-09-24

Catalysts

Abstract:Cu-SSZ-13 has been generally considered as the predominant commercial selective catalytic reduction (SCR) catalyst in the NH3-SCR reaction because of its superior activity and durability. However, in real applications, SCR catalysts readily undergo hydrothermal aging and sulfur poisoning. In this work, the deactivation and regeneration of a commercial Cu-SSZ-13 catalyst was investigated for SO2 exposures during hydrothermal aging and the effect of different regeneration temperatures was compared. By using XRD, SEM, H2-temperature programmed reduction (TPR), X–ray photoelectron spectra (XPS) and NH3-temperature programmed desorption (TPD) analysis, it was found that SO2 poisoning influenced the chabazite (CHA) structure even if regeneration cannot restore its original structure, the redox ability and ammonia storage performance also influenced by sulfation and the regeneration process. Moreover, the extent of a decrease in redox ability was more severe than acidity, suggesting that the amount of isolated Cu2+ and Cu+ reduction was responsible for irreversible deactivation over the Cu-SSZ-13 catalyst. Combined with the analysis of Ea values and pre-exponential factor of the SCR reaction, a more likely explanation for the irreversible deactivation was that active sites were lost mostly in sulfated and regenerated process sites.

chemistry, physical
Determining hydrothermal deactivation mechanisms on Cu/SAPO-34 NH3-SCR catalysts at low- and high-reaction regions: establishing roles of different reaction sites

Qing-Jin Lin,Ming-Ming Pei,Pan Yao,Shi Xu,Shu-Hao Xu,Shuang Liu,Hai-Di Xu,Yi Dan,Yao-Qiang Chen

DOI: https://doi.org/10.1007/s12598-021-01933-8

IF: 6.318

2022-03-07

Rare Metals

Abstract:Hydrothermal deactivation is a constant challenge in commercial catalytic process aimed at NOx emission control, which may be observed in the low (150–400 °C) or high (400–550 °C)-reaction regions. To the best of our knowledge, there is a lack of systematic research regarding the correlation between the reaction sites and the mechanism of hydrothermal degradation at various reaction regions. For a targeted investigation of this, Cu/zeolite catalysts have been prepared using different amounts of polyvinyl alcohol for adjusting their redox and acid properties. These catalysts exhibit hydrothermal deactivation in different reaction regions. No change is observed in the reaction mechanism even with hydrothermal deactivation, but various reaction sites determine the performance deterioration in the low- and high-reaction regions. The redox properties and weak acid sites affect the hydrothermal deactivation in the low-reaction region, whereas the moderate/strong acid sites related to the structure mainly influence the hydrothermal deactivation in the high-reaction region. This work provides several theoretical insights for optimizing the hydrothermal stabilities of Cu/zeolite catalysts.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Experimental and numerical study of Cu-SSZ-13 SCR system for NOx reduction and hydrothermal aging under diesel exhaust conditions

Yu Sun,Yejian Qian,Zhen Gong,Xiang Gu,Zhaohui Xie,Shun Meng,Binbin Tang

DOI: https://doi.org/10.1016/j.fuel.2023.129617

IF: 7.4

2023-08-30

Fuel

Abstract:Selective catalytic reduction (SCR) is a crucial technique for mitigating nitrogen oxides emission of internal combustion engines. Compared with vanadium-based catalysts, copper-based molecular sieve catalysts exhibit superior low-temperature catalytic performance and anti-aging properties. The catalytic characteristics of Cu-SSZ-13 catalyst in both fresh and aged states are investigated through experimental and numerical simulations. The catalytic performance of Cu-SSZ-13 catalyst with 200 g/L coating is investigated under wide inlet temperatures (180 °C–450 °C) and ANR (ammonia to nitrogen ratio) (1–1.4) conditions via an engine emission test device. Further, the apparatus is adopted to evaluate performance at various aging temperatures (600 °C, 700 °C, and 800 °C). The aging factor is introduced based on experimental results to establish and correct the kinetic model for SCR aging state. The results illuminate that the increase of ANR fails to compensate for decline of catalytic efficiency under low-temperature conditions (150 °C).The generated quantity of isocyanate acid through the side reaction of urea hydrolysis increases proportionally with ANR. And it increased supply only resulted in a marginal 1 %–3 % improvement of catalytic efficiency. As SV decreases from 60,000 h −1 to 35,000 h −1 , the catalyst efficiency increases from 22 % to 45 %, resulting in an elevation of reactant concentration and its gradient on the catalyst surface. This leads to accelerated reaction rates and enhanced diffusion effects. The catalytic efficiency can be significantly enhanced at low temperatures when NO 2 fraction in NOx falls within the range of 10 %–25 %. The sensitivity of SCR reactions to aging varies at low temperatures (<250 °C) due to the distinct reaction sites on catalyst for different types of SCR reactions. The NO 2 SCR reactions exhibit minimal susceptibility, while the rapid SCR reactions are significantly impeded. Moreover, it has been observed that the catalyst microstructure was completely deteriorated under hydrothermal aging test at 900 °C operating condition. In general, the low-temperature catalytic performance of Cu-SSZ-13 catalyst can be further optimized by pretreating inlet gas components and optimizing the catalyst structure.

energy & fuels,engineering, chemical
Evolution of Copper Species on Cu/SAPO-34 SCR Catalysts Upon Hydrothermal Aging

Xuesong Liu,Xiaodong Wu,Duan Weng,Zhichun Si,Rui Ran

DOI: https://doi.org/10.1016/j.cattod.2016.05.021

IF: 5.3

2017-01-01

Catalysis Today

Abstract:Cu-modified SAPO-34 molecular sieves with different Cu loading amounts were prepared by ion exchange and impregnation methods. Both series of catalysts were hydrothermally treated at 750 degrees C in 10 vol% H2O/air for 24 h. The catalysts were characterized by inductively coupled plasma optical emission spectrometry (ICP-OES), electron paramagnetic resonance (EPR), X-ray photoelectron spectroscopy (XPS), H-2 temperature-programmed reduction (H-2-TPR), NH3 temperature-programmed desorption (NH3-TPD) and diffused,reflectance infrared flourier transform spectroscopy (DRIFTS). All the fresh catalysts show high activity toward the selective catalytic reduction of NOx with NH3 (NH3-SCR) at low temperatures regardless of preparation method. Generally, the hydrothermal aging shifts the operation window of the catalysts towards high temperatures. The improvement in high-temperatures activity is attributed to the migration of surface CuO clusters into the ion-exchanged sites as isolated Cu2+ during ageing, which suppresses the competitive oxidation of NH3. The loss of low-temperatures activity is also related to the decrease in the amount of active surface CuO clusters, inhibiting the oxidation of NO to NO2 and fast SCR reaction. Interestingly, the amount of Lewis acid sites increase linearly with the increasing isolated Cu2+, while the Bronsted acidity is weakened. (C) 2016 Elsevier B.V. All rights reserved.
Recent NH 3 -SCR Mechanism Research over Cu/SAPO-34 Catalyst

dequan fan

DOI: https://doi.org/10.1021/jp4114199

2014-01-01

Abstract:The preliminary mechanism research of NH3-SCR and NH3 oxidation over Cu/SAPO-34 catalyst is explored. The XRD, SEM, in situ EPR, NH3-SCR, NH3 oxidation test, DRIFTs, and the kinetic tests were performed for the bulk characterization, catalytic activity measurement, and the mechanism estimation. The NH3-SCR result showed that Cu/SAPO-34 revealed excellent activity during 120-600 degrees C, while the NH3 oxidation appeared above 300 degrees C and caused the decline of NO conversion. The order of various reactants (NO, NH3, and O-2 for NH3-SCR and NH3, O-2, for NH3 oxidation) was estimated by the kinetic tests to explain their behaviors during the NH3-SCR process. The NH3-SCR presents strong dependence on adsorbed NH3 species on Cu/SAPO-34, but the NH3 oxidation does not. Furthermore, the EPR experiment proved that the isolated Cu2+ species are the active sites and the ammonia nitrites species are the intermediate for NH3-SCR over Cu/SAPO-34 catalysts. The different behavior of adsorbed NH3 species in NH3-SCR and NH3 oxidation was studied through DRIFTs to explain the competition between the two reactions for NH3 consumption at high temperature. Meanwhile, combining the results of previous research, the primary reaction mechanism over Cu/SAPO-34 during the NH3-SCR process was conducted.
Understanding the influence of hydrothermal treatment on NH3-SCR of NO activity over Cu -SSZ-16

Rui Li,Xiangqiong Jiang,Jiecheng Lin,Zhiping Zhang,Qintong Huang,Guangying Fu,Yujun Zhu,Jiuxing Jiang

DOI: https://doi.org/10.1016/j.cej.2022.136021

IF: 15.1

2022-08-01

Chemical Engineering Journal

Abstract:SSZ-16 zeolite with AFX topology was synthesized by hydrothermal method using 1,4-diazabicyclo[2.2.2]-octane-C4-diquat dibromide as organic structure directing agent. Cu x -SSZ-16 catalysts were prepared by exchanging SSZ-16 zeolite with Cu and applied for selective catalytic reduction (SCR) of NO x with ammonia. Among these catalysts, Cu2.2-SSZ-16 performs the best SCR denitration (deNO x ) performance that above 90% NO x conversion can be achieved at 175–600 °C. Especially, the influences of the hydrothermal aging at various temperatures (650, 750 and 850 °C) on active species and AFX framework of the Cu2.2-SSZ-16 catalyst are investigated in detail by various characterization methods including XRD, SEM, H2-TPR, NMR, UV–vis-DRS, EPR, NH3-TPD and in situ DRIFTS. Cu2.2-SSZ-16 still shows good NH3-SCR activity after hydrothermal aging at 650 and 750 °C due to more Cu2+-2Z species in the sample. Still, obvious deactivation can be observed after hydrothermal aging at 850 °C because of the collapse of AFX skeleton and the weak interaction between active Cu species and the skeleton. Nevertheless, Cu2.2-SSZ-16 is a competitive candidate for NH3-SCR deNO x reaction in practical applications.

engineering, chemical, environmental
Optimization of Hybrid Crystal with SAPO-5/34 on Hydrothermal Stability for deNOx Reaction by NH3

Qingjin Lin,Chenlu Lin,Jingying Liu,Shuang Liu,Haidi Xu,Yaoqiang Chen,Yi Dan

DOI: https://doi.org/10.1007/s40242-020-0117-z

IF: 3.1

2020-07-01

Chemical Research in Chinese Universities

Abstract:In order to deal with the challenge of the hydrothermal deactivation of selective catalytic reduction of NOx by NH3(NH3-SCR) catalyst and extend its lifetime, a novel Cu/SAPO-5/34 catalyst was prepared, and it almost maintains its deNOx performance with a high conversion rate of 90% NOx between 175 °C and 400 °C after undergoing the rigorous treatment at 800 °C for 12 h. Thus, Cu/SAPO-5/34 is more recalcitrant to the high-temperature hydrothermal deactivation than Cu/SAPO-34. Besides, the formation of N2O is always below 3×10−6(3 ppm) during the whole reaction temperature, performing an advanced catalytic selectivity. The effect of high-temperature hydrothermal treatment on the morphology, structure and texture property, the acid sites, as well as the active copper species were investigated. These characterizations manifest that the optimized high-temperature hydrothermal stability is associated closely with the good structural stability over Cu/SAPO-5/34-HT, which facilitates to preserve reaction sites, and then showing the better hydrothermal stability than Cu/SAPO-34.
Characterization of Commercial Cu-SSZ-13 and Cu-SAPO-34 Catalysts with Hydrothermal Treatment for NH3-SCR of NOx in Diesel Exhaust

Lei Ma,Yisun Cheng,Giovanni Cavataio,Robert W. McCabe,Lixin Fu,Junhua Li

DOI: https://doi.org/10.1016/j.cej.2013.03.078

IF: 15.1

2013-01-01

Chemical Engineering Journal

Abstract:Cu-SSZ-13 and Cu-SAPO-34 zeolite catalysts were fully formulated washcoat cordierite monoliths purchased from the major catalyst suppliers and were hydrothermally aged at 600, 750, and 850°C in simulated exhaust gases containing water. Their catalytic activities were tested in selective catalytic reduction (SCR) of NOx with ammonia. The microstructure of the zeolite supports, identity of copper species, acidity and reactant adsorption ability were investigated in detail using various characterization methods. The results showed that hydrothermal treatment of Cu-SSZ-13 and Cu-SAPO-34 catalysts had a significant influence on the physicochemical properties and reactant adsorption abilities of the catalysts, which resulted in different catalytic performances in NH3-SCR. The hydrothermal treatment drastically decreased the surface area and pore volume of both the Cu-SSZ-13 and Cu-SAPO-34 catalysts. TEM results indicated that obvious aggregation of Cu-SSZ-13 and Cu-SAPO-34 occurred while some CuO particulates migrated from isolated Cu2+ species were formed during the aging test. Hydrothermal treatment of the Cu-SSZ-13 and Cu-SAPO-34 catalysts caused the migration of Cu2+, a decrease in acidity and dealumination. The change in the coordination environment of Cu2+ affected NOx adsorption and activation on the catalyst surface. Both the copper sites and the acidity might be the main factor for the NH3-SCR reaction on Cu-CHA catalyst.
Migration of Cu Species in Cu/SAPO-34 During Hydrothermal Aging

Lei Wang,Jason R. Gaudet,Wei Li,Duan Weng

DOI: https://doi.org/10.1016/j.jcat.2013.06.010

IF: 7.3

2013-01-01

Journal of Catalysis

Abstract:In the present work, we report the migration of copper species in Cu/SAPO-34 during hydrothermal aging and its role in selective catalytic reduction (SCR) of NOx. Two Cu/SAPO-34 catalysts, prepared by ion-exchange and precipitation methods, were hydrothermally aged at 700 degrees C for 48 h and characterized in detail. The aged ion-exchanged catalyst exhibited little deterioration in activity; however, the catalytic activity of the precipitated catalyst, which showed inferior activity for the fresh sample, was markedly improved after hydrothermal treatment and became comparable to that of the ion-exchanged sample. A detailed characterization of the Cu species before, during, and after the hydrothermal treatment using a combination of experimental techniques clearly demonstrated that the copper species in the precipitated sample, which initially existed as CuO clusters on the external surface of SAPO-34, migrated to the ion-exchanged sites as isolated ions after aging. The change in copper oxidation states and coordination environment during the aging process was probed by in situ X-ray absorption spectroscopy, and a possible mechanism of Cu migration involving metallic Cu species was proposed. (C) 2013 Elsevier Inc. All rights reserved.
The Migration of Cu Species over Cu–SAPO-34 and Its Effect on NH3 Oxidation at High Temperature

Jun Wang,Yu Huang,Tie Yu,Shaochun Zhu,Meiqing Shen,Wei Li,Jianqiang Wang

DOI: https://doi.org/10.1039/c4cy00451e

IF: 6.177

2014-01-01

Catalysis Science & Technology

Abstract:The influence of Cu species migration, through hydrothermal treatment, on the NH3 oxidation mechanism and its inhibition on NH3-SCR activity over Cu–SAPO-34 catalysts were studied. XRD, SEM, EPR, H2-TPR, CO-DRIFTS were conducted to estimate the Cu species distribution. The results revealed that the CuO species initially existed on the external surface of the fresh impregnated Cu/SAPO-34 catalyst, and converted to isolated Cu2+ and nanosized CuO in the cavity of the SAPO-34 support during hydrothermal treatment. The NH3-SCR activity over the hydrothermally treated Cu/SAPO-34 catalysts improved due to the increase of the isolated Cu2+ amount, while the NH3 oxidation activity declined. Furthermore, the NO amount generated in the NH3 oxidation reaction over the hydrothermally treated samples was much less than the fresh one, which was also caused by the migration of Cu species. In addition, the kinetic NH3 oxidation was performed at temperatures from 340 °C to 440 °C, and the results indicated that CuO species were the active sites for the NH3 oxidation. In conclusion, the Cu species migration caused the decrease of the NH3 oxidation activity and the great variation in the generated NO amount. Furthermore, it was proposed that the NH3 oxidation mechanism over the Cu/SAPO-34 catalysts contained two steps: firstly, molecular NH3 reacted with O2 at CuO sites; secondly, the generated NO was reduced by NH3 to N2 at isolated Cu2+ sites.
Impact of Hydrothermal Aging on SO2 Poisoning over Cu-SSZ-13 Diesel Exhaust SCR Catalysts

Lai Wei,Dongwei Yao,Feng Wu,Biao Liu,Xiaohan Hu,Xingwen Li,Xinlei Wang

DOI: https://doi.org/10.1021/acs.iecr.8b04543

2019-01-01

Industrial & Engineering Chemistry Research

Abstract:The impact of hydrothermal aging on SO2 poisoning over Cu-SSZ-13 selective catalytic reduction (SCR) catalysts were investigated in this study. The catalyst samples were hydrothermally aged at various temperatures for SO2 poisoning and characterized by SO2 temperature-programmed desorption (SO2-TPD), X-ray diffraction (XRD), H-2 temperature-programmed reduction (H-2-TPR), and NH3-TPD. The performance evaluations were also performed to illustrate the impact on SCR activity and oxidation. The results showed that the Cu-SO4-like species decreased in the 750 degrees C aged sample via copper migration, while they increased in the 850 degrees C aged sample due to CuOx/CuAlOx formation. The low-temperature SCR activity and oxidation decreased due to sulfur poisoning. For the sulfated sample, however, it was determined that NOx conversion was slightly higher on the mildly hydrothermally aged sample. Furthermore, desulfation is easier for the mildly hydrothermally aged sample but more difficult for the severely hydrothermally aged sample.
Unraveling the Nature of Cerium on Stabilizing Cu/SAPO-34 NH3-SCR Catalysts under Hydrothermal Aging at Low Temperatures

Weibo Zhang,Meiqing Shen,Jun Wang,Xinyu Li,Jianqiang Wang,Gurong Shen,Chen Wang

DOI: https://doi.org/10.1016/j.jre.2022.07.010

IF: 4.632

2022-01-01

Journal of Rare Earths

Abstract:To reveal how cerium stabilizes Cu/SAPO-34 at low-temperature hydrothermal aging,various amounts of cerium were introduced into Cu/SAPO-34 via impregnation method and treated at 70 ℃ with RH 80％for 96 h.Cerium as Ce3+and CeO2 nanoparticle is located on the surface of Cu/SAPO-34,and Ce3+plays a vital role on gradually decreasing surface acidity and blocking defect sites with an increase of Ce loading.After hydrothermal aging,Cu/SAPO-34 with high Ce loading shows the superior SCR activity comparable to fresh samples.It is proven that the surface acidity determines the stability of the structure during hydrothermal aging process,and lower surface acidity prevents the number of Cu(Ⅱ)ions from decreasing significantly.Furthermore,the structure's stability helps the recovery of Cu(Ⅱ)ions and renders an outstanding regeneration ability.Our finding paves the way for the design of new Cu/SAPO-34 catalysts with good SCR activity and long-term stability in real application.
In situ regeneration of sulfated Cu/SAPO-34 catalyst for the selective catalytic reduction of NOx with NH3

Qifan Yu,Xuesong Liu,Hongfeng Chen,Shuang Liu,Peng Jiang

DOI: https://doi.org/10.1007/s11144-019-01662-1

2019-08-30

Abstract:The regeneration mechanism of sulfated Cu/SAPO-34 catalysts in reducing atmospheres (5% H2/Ar and NH3/Ar at 600 °C) was investigated by using a series of characterization methods. Hydrogen regeneration improved the catalysts' NH3-SCR activity from 150 to 550 °C remarkably, while ammonia regeneration exhibited relatively less obvious promotion effect. The TPR of hydrogen and EPR spectra data show that the regeneration process affects the amount and the coordination of the active isolated Cu2+ species significantly. The desulfation increases the amount of isolated copper ions and improves the catalytic activity of SCR.
Boosting the Catalytic Performance of Cu-SAPO-34 in NOx Removal Via Hydrothermal Treatment.

Xiaoyan Tian,Huimin Wang,Siyuan Xu,Lianyun Gao,Jinyan Cao,Jianjun Chen,Qiulin Zhang,Ping Ning,Jiming Hao

DOI: https://doi.org/10.1016/j.jes.2022.10.047

IF: 6.9

2024-01-01

Journal of Environmental Sciences

Abstract:Phosphate ions promoted Cu-SAPO-34 (P-Cu-SAPO-34) were prepared using bulk CuO particles as Cu2+ precursor by a solid-state ion exchange technique for the selective catalytic reduction of NOx with NH3 (NH3-SCR). The effects of high temperature (H-T) hydrothermal aging on the NOx removal (de-NOx) performance of Cu-SAPO-34 with and without phosphate ions were systematically investigated at atomic level. The results displayed that both Cu-SAPO-34 and P-Cu-SAPO-34 presented relatively poor NOx removal activity with a low conversion (< 30%) at 250-500°C. However, after H-T hydrothermal treatment (800°C for 10 hr at 10% H2O), these two samples showed significantly satisfied NOx elimination performance with a quite high conversion (70%-90%) at 250-500°C. Additionally, phosphate ions decoration can further enhance the catalytic performance of Cu-SAPO-34 after hydrothermal treatment (Cu-SAPO-34H). The textural properties, morphologies, structural feature, acidity, redox characteristic, and surface-active species of the fresh and hydrothermally aged samples were analyzed using various characterization methods. The systematical characterization results revealed that increases of 28% of the isolated Cu2+ active species (Cu2+-2Z, Cu (OH)+-Z) mainly from bulk CuO and 50% of the Brønsted acid sites, the high dispersion of isolated Cu2+ active component as well as the Brønsted acid sites were mainly responsible for the accepted catalytic activity of these two hydrothermally aged samples, especially for P-Cu-SAPO-34H.
Insights into the impact of lanthanum on hydrothermal-induced migration and transformation of copper species in Cu/SAPO-34 catalyst for NH3-SCR

Huimin Wang,Wei Li,Siyuan Xu,Mo Liu,Jiming Hao,Ping Ning,Qiulin Zhang

DOI: https://doi.org/10.1016/j.mcat.2021.111914

IF: 4.6

2021-10-01

Molecular Catalysis

Abstract:During the high-temperature hydrothermal aging process, the tolerance of the zeolite structure and the stability of the active Cu2+ ions directly determined the denitration (deNOx) performance of the copper-based zeolite catalysts in automobile exhaust treatment. Herein, we displayed the hydrothermal aging stability of La-free and La-doped Cu/SAPO-34 catalysts at variant temperatures (650, 750 and 850 °C). A series of characterization results signified that the addition of La into SAPO-34 framework by ion exchange method had obvious contribution to hold back the collapse of SAPO-34 structure and transformation of isolated Cu2+ ions. Different from Cu/SAPO-34 catalyst, Cu/La-SAPO-34 catalyst was more prone to maintain its superior catalytic activity after hydrothermal aging at 750 °C, which possessed great application potential. In addition, NH3-TPD and DRIFT spectra shed light on the variation of surface acidity over two kinds of catalysts inducing by hydrothermal treatment. It could be discovered that doping of La provided moderate surface acidity and excellent hydrothermal stability for Cu/SAPO-34 even up to 750 °C, which was in favor of the NH3-SCR reaction.

chemistry, physical
The Effect of Sulfate Species on the Activity of NH3-SCR over Cu/SAPO-34

Chen Wang,Jun Wang,Jianqiang Wang,Tie Yu,Meiqing Shen,Wulin Wang,Wei Li

DOI: https://doi.org/10.1016/j.apcatb.2016.11.033

2017-01-01

Abstract:The deactivation mechanism by different types of sulfate was investigated for the selective catalytic reduction of NOx on Cu/SAPO-34 catalyst. A Cu/SAPO-34 catalyst was treated with 50 ppm SO2 alone at 150 and 250 degrees C or in the presence of a SCR feed at 250 and 350 degrees C. Copper sulfate was found on all sulfated catalysts, but ammonia sulfate was found only on the catalyst sulfated in the SCR feed at 250 degrees C. In situ DRIFTs results show that both copper sulfate and ammonia sulfate species are formed on the isolated Cu2+ sites. All sulfated catalysts have lower NOx conversions compared with the Unsulfated catalysts due to reduced number of active sites. However, their apparent activation energies fot the SCR reaction remain the same, and their turnover frequencies are identical. This suggests that the deactivation mechanism is similar regardless of the type of sulfate species. On the other hand, it was found that ammonia sulfate was easier to remove than copper sulfate by a desulfation treatment at 600 degrees C, resulting in a larger extent of activity recovery. (C) 2016 Elsevier B.V. All rights reserved.
Critical Roles of Cu(OH)2 in Low-Temperature Moisture-Induced Degradation of Cu-SAPO-34 SCR Catalyst: Correlating Reversible and Irreversible Deactivation

Yue Ma,Xiaodong Wu,Liping Liu,Li Cao,Rui Ran,Zhichun Si,Feng Gao,Duan Weng

DOI: https://doi.org/10.1016/j.apcatb.2020.119306

2020-01-01

Abstract:Cu-SAPO-34 selective catalytic reduction (SCR) catalyst deactivates upon exposure to water vapor at temperatures lower than 100 degrees C, which deteriorates its application prospects. The deactivation under cycled aging-regeneration conditions can be categorized into two stages, namely reversible and irreversible deactivation. Based on SCR reaction tests, and characterizations with diffuse reflection infrared Fourier transform spectroscopy (DRIFTS), NH3 temperature-programmed desorption (NH3-TPD) and H-2 temperature-programmed reduction (H-2-TPR), it is concluded that the transformation of active isolated Cu(II) ions to Cu(OH)(2) is critical to both types of deactivation. Within the frame of reversible deactivation, Cu(OH)(2) can be converted back to SCR active Cu(II) ions by interacting with Bronsted acid sites during high-temperature regeneration. However, interactions between Cu(OH)(2) and hydrolyzed framework Al lead to the formation of CuAl2O4-like species, causing permanent loss of active Cu(II) ions and thus, irreversible deactivation.
Optimization of isolated copper species on the NH 3 -SCR performance over Cu/SSZ-39 modified by ammonia water

Shuhao Xu,Qingjin Lin,Jiayi Li,Jianli Wang,Haidi Xu,Yaoqiang Chen

DOI: https://doi.org/10.1016/j.cattod.2024.114731

IF: 5.3

2024-04-19

Catalysis Today

Abstract:To further improve the activity of Selective Catalytic Reduction of nitrogen oxide (NO x ) with Ammonia (NH 3 -SCR) and the hydrothermal stability at 900 °C on Cu-based small-pore zeolite catalyst, the interaction between ammonia water and Cu 2+ is used to regulate the interaction between Cu 2+ and Si-O-Al structures of the zeolite, and affect the migration of Cu 2+ in the channels of zeolite. The characterization results show that the microchemical environment of isolated Cu 2+ species is optimized, and more isolated Cu 2+ species can stably exist over the surface of Cu/SSZ-39, exhibiting a strong redox property. Besides, the ability of acid sites to adsorb and activate NH 3 is also enhanced, and the amount of H 2 O adsorbed in the pores of zeolite is reduced due to the stable surface isolated Cu 2+ species, which is conducive to the stability of the catalyst after hydrothermal aging at 900 °C. When the mole ratio of ammonia and copper is 3, the NH 3 -SCR performance and the hydrothermal stability at 900 oC are both optimized on the modified catalyst. The temperature window that the NO x conversion is higher than 90% (ΔT 90 ) on the unmodified catalyst is 200–475 °C, but the ΔT 90 on the modified catalyst is broadened to 178–544 °C. More importantly, after hydrothermal aging at 900 oC, the ΔT 90 on the modified catalyst is shifted to the higher temperature by 48 oC, with the maximum NO x conversion of 96%. This work would provide a new strategy for further optimizing Cu/SSZ-39 catalyst for deNO x emitted from diesel engines to meet higher emission standards in future.

chemistry, physical,engineering, chemical, applied
Improved hydrothermal durability of Cu-SSZ-13 NH3-SCR catalyst by surface Al modification: Affinity and passivation

Yue Ma,Songqi Cheng,Xiaodong Wu,Tongxi Ma,Liping Liu,Baofang Jin,Minghan Liu,Jianbo Liu,Rui Ran,Zhichun Si,Duan Weng

DOI: https://doi.org/10.1016/j.jcat.2021.11.022

IF: 7.3

2022-01-01

Journal of Catalysis

Abstract:To improve the hydrothermal durability of Cu-SSZ-13 selective catalytic reduction (SCR) catalyst, a thin Al2O3 modification layer was coated on the external surface of Cu-SSZ-13 by a chemical liquid deposition (CLD) method. The high-temperature SCR activity of the Al-modified Cu-SSZ-13 can be maintained upon 750–800 °C hydrothermal aging, and over-oxidation of NH3 is largely inhibited. Based on H2-TPR and EPR results, it is revealed that CuAl2O4-like species forms upon Al modification and converts further to CuAlO2-like species during aging, while the accumulation of CuO-like species is inhibited. The high affinity of Al-containing species (i.e., Al2O3 and CuAl2O4-like species) with Cu(OH)2 is suggested by DFT calculations, indicating that Cu(OH)2 detached from ion-exchange sites are captured by Al to form CuAlO2-like species instead of CuO-like species. The passivation of detached Cu species by coated Al leads to somewhat weakened low-temperature SCR activity, but successfully preserves the high-temperature SCR performance upon aging, which can be applied to high-temperature SCR scenarios.

chemistry, physical,engineering, chemical
Deactivation of Cu-SAPO-34 by urea-related deposits at low temperatures and the regeneration

Yue Ma,Xiaodong Wu,Junyu Zhang,Rui Ran,Zhichun Si,Duan Weng

DOI: https://doi.org/10.1016/j.jes.2019.02.008

Abstract:Selective catalytic reduction (SCR) with urea catalyzed by Cu-SAPO-34 is an effective method to eliminate NOx from diesel exhaust. However, urea-related deposits may form during cold-start and urban driving due to low exhaust temperatures. The activity of Cu-SAPO-34 at 175°C is significantly degraded by urea exposure, and 300°C is required for regeneration. Through in-situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) and temperature-programmed hydrolysis studies, the dominant stable deposit at 175°C is identified as biuret, which can be eliminated at 300°C. The urea-derived deactivation and regeneration mechanisms of Cu-SAPO-34 were compared with those of anatase-supported catalysts.

Catalytic deactivation mechanism research over Cu/SAPO-34 catalysts for NH3-SCR (I): The impact of 950 °c hydrothermal aging time

Deactivation and Regeneration for the SO2-Poisoning of a Cu-SSZ-13 Catalyst in the NH3-SCR Reaction

Determining hydrothermal deactivation mechanisms on Cu/SAPO-34 NH3-SCR catalysts at low- and high-reaction regions: establishing roles of different reaction sites

Experimental and numerical study of Cu-SSZ-13 SCR system for NOx reduction and hydrothermal aging under diesel exhaust conditions

Evolution of Copper Species on Cu/SAPO-34 SCR Catalysts Upon Hydrothermal Aging

Recent NH 3 -SCR Mechanism Research over Cu/SAPO-34 Catalyst

Understanding the influence of hydrothermal treatment on NH3-SCR of NO activity over Cu -SSZ-16

Optimization of Hybrid Crystal with SAPO-5/34 on Hydrothermal Stability for deNOx Reaction by NH3

Characterization of Commercial Cu-SSZ-13 and Cu-SAPO-34 Catalysts with Hydrothermal Treatment for NH3-SCR of NOx in Diesel Exhaust

Migration of Cu Species in Cu/SAPO-34 During Hydrothermal Aging

The Migration of Cu Species over Cu–SAPO-34 and Its Effect on NH3 Oxidation at High Temperature

Impact of Hydrothermal Aging on SO2 Poisoning over Cu-SSZ-13 Diesel Exhaust SCR Catalysts

Unraveling the Nature of Cerium on Stabilizing Cu/SAPO-34 NH3-SCR Catalysts under Hydrothermal Aging at Low Temperatures

In situ regeneration of sulfated Cu/SAPO-34 catalyst for the selective catalytic reduction of NOx with NH3

Boosting the Catalytic Performance of Cu-SAPO-34 in NOx Removal Via Hydrothermal Treatment.

Insights into the impact of lanthanum on hydrothermal-induced migration and transformation of copper species in Cu/SAPO-34 catalyst for NH3-SCR

The Effect of Sulfate Species on the Activity of NH3-SCR over Cu/SAPO-34

Critical Roles of Cu(OH)2 in Low-Temperature Moisture-Induced Degradation of Cu-SAPO-34 SCR Catalyst: Correlating Reversible and Irreversible Deactivation

Optimization of isolated copper species on the NH 3 -SCR performance over Cu/SSZ-39 modified by ammonia water

Improved hydrothermal durability of Cu-SSZ-13 NH3-SCR catalyst by surface Al modification: Affinity and passivation

Deactivation of Cu-SAPO-34 by urea-related deposits at low temperatures and the regeneration