Abstract:Abstract In order to investigate the effect of neon seeding on deuterium retention and surface modification of ITER-like forged tungsten with grains elongated perpendicular to the surface, pure and neon-seeded deuterium plasma exposures were performed in the linear plasma device PSI-2. The ion percentage of neon in the mixed plasma was around 10%. The sample temperature and deuterium ion fluence were kept at 450 K and 1 × 10 26 m −2 , respectively. The incident ion energy was 40 eV, just reaching the tungsten sputtering threshold for neon. Surface observations show that neon seeding leads to pronounced cracking and erosion of blister caps and a significant reduction of small blisters (<0.8 μ m). This is possibly attributed to surface sputtering and the inhibitory effect of neon-induced defects on blister nucleation by hindering dislocation movements. On the other hand, neon seeding increases the total deuterium retention by ∼70% according to the thermal desorption spectroscopy (TDS) measurements. A low-temperature desorption peak (∼660 K) which should be mainly ascribed to deuterium de-trapping from dislocations is observed to be broadened and shifts towards higher temperature in the case of neon seeding, suggesting enhanced inward diffusion and trapping of deuterium. An additional deuterium release peak appears at a higher temperature (∼803 K), indicating the creation of new deuterium-traps induced by neon. A comparison of the results of nuclear reaction analysis and TDS reveals that neon seeding not only increases deuterium retention in the surface region (<7.2 μ m) but also in the bulk (>7.2 μ m). We ascribe the enhanced deuterium retention to the increased deuterium-traps in the top-surface induced by Ne irradiation and the vertical grain boundary configuration of the forged W promoting the inward diffusion of deuterium.

Mitigated Blistering and Deuterium Retention in Tungsten Exposed to High-Flux Deuterium–neon Mixed Plasmas

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Influence of neon seeding on the deuterium retention and surface modification of ITER-like forged tungsten

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Blistering on Tungsten Surface Exposed to High Flux Deuterium Plasma

Blister-dominated retention mechanism in tungsten exposed to high-fluence deuterium plasma

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Effect of thickness on the blistering of tungsten exposed to deuterium plasma

Dependence of blistering and deuterium retention on damage depth in damaged tungsten exposed to deuterium plasma

Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Effect of Heavy Ion Pre-Irradiation on Blistering and Deuterium Retention in Tungsten Exposed to High-Fluence Deuterium Plasma

Deuterium behavior in tungsten exposed to deuterium plasma with rising or declining temperature

Surface Blistering and Deuterium Retention in Chemical Vapor Deposition Tungsten Exposed to Deuterium Plasma

Dependence of deuterium retention and surface blistering on deuterium plasma exposure temperature and fluence in lanthanum oxide doped tungsten

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma