Deformation Behavior of High Yield Strength – High Ductility Ultrafine-Grained 316LN Austenitic Stainless Steel

D. M. Xu,G. Q. Li,X. L. Wan,R. L. Xiong,G. Xu,K. M. Wu,M. C. Somani,R. D. K. Misra
DOI: https://doi.org/10.1016/j.msea.2017.02.009
2017-01-01
Abstract:The concept of phase reversion annealing involving extensive cold deformation of metastable austenite to strain-induced martensite, followed by annealing at slightly elevated temperature, developed by Misra’s group in recent years [2], [3], [4], [5] was used to obtain ultrafine-grained structure in a 316LN austenitic stainless steel. The primary objective of this study is to elucidate the deformation mechanisms. The study suggested that an average austenite grain size in the ultrafine regime of ~2.0μm can be obtained using the experimental conditions described in the study, which is ~6 times finer than the grain size of commercial 316LN steel. The grain refinement led to high yield strength in ultrafine-grained 316LN steel without any significant compromise in ductility. The high plasticity of ultrafine-grained 316LN steel is attributed to the presence of mechanical twins.
What problem does this paper attempt to address?