Synergistic optimization of microstructure and mechanical properties of AISI 430 ferritic stainless steel via dual-phase zone annealing process
Lixin Meng,Wenqi Li,Fei Yang,Yujin Nie,Liuwei Zheng,Quanxin Shi,Jinyao Ma,Wei Liang,Huihu Lu
DOI: https://doi.org/10.1016/j.matchar.2024.114283
IF: 4.537
2024-08-23
Materials Characterization
Abstract:This study systematically evaluated the impact of dual-phase zone annealing on the microstructure and mechanical properties of cold-rolled 430 Ferritic Stainless Steel (FSS), focusing on the phase transformation process from ferrite to austenite and the dissolution and precipitation behavior of the M 23 C 6 phase. The annealing process significantly affects the microstructural characteristics of ferrite and martensite, including grain size, the distribution of grains of various sizes, aspect ratio, and phase content. The amount of martensite first increased and then decreased with rising annealing temperatures. The sample annealed at 1050 °C exhibited the highest martensite content of 29.5%. The variation in martensite content reflects the complex interplay between phase transformation kinetics and thermodynamic equilibrium. As the annealing time increased or temperature rose, the M 23 C 6 phase at ferrite grain boundaries gradually dissolved and re-precipitated at higher temperatures. At lower temperatures, the M 23 C 6 phase precipitated within martensite, but as the temperature increased, the precipitated phase diminished until it disappeared. Temperature changes affect the solubility of precipitates, atomic diffusion rates, and the uniform distribution of atoms across different phases. Appropriately increasing annealing temperature or extending annealing duration enhances the strength and hardness of 430 FSS. However, excessively high annealing temperatures lead to a decline in mechanical properties. The sample annealed at 1000 °C demonstrated the best mechanical properties, achieving a tensile strength of 783 MPa and an elongation of 16.0%. Furthermore, the analysis of fracture morphology and yield behavior in stress-strain curves further elucidated the macroscopic mechanical performance of the material.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing