Microstructure Evolution and Mechanical Properties of Heterogeneous Nano/Ultrafine‐Grained Austenitic Stainless Steel Prepared by Low‐Temperature Rolling and Annealing

Jia Liu,Haojie Wang,Long Huang,Xing Ma,Rong Zhang,Xiangtao Deng,Zhaodong Wang

DOI: https://doi.org/10.1002/srin.202200658

IF: 2.1258

2022-11-30

steel research international

Abstract:This study focuses on the microstructure evolution of austenitic stainless steel during room‐temperature and low‐temperature rolling. Low‐temperature rolling reduces the stacking fault energy of austenitic stainless steel and promotes the formation of shear bands, ε‐martensite, and α′‐martensite. A heterogeneous nano/ultrafine‐grained structure with a high yield strength (908 MPa) and satisfactory elongation (43%) is obtained by low‐temperature rolling and annealing. An 18Cr–8Ni austenitic stainless steel is subjected to cold rolling at room temperature and low temperature (−50 °C) under different amounts of deformation. The samples cold rolled to 70% deformation are then annealed to obtain nano/ultrafine‐grained steels with a good strength–ductility combination. The effects of cold rolling temperature and deformation amount on the microstructure evolution of austenitic stainless steel during rolling are investigated. The results reveal that low‐temperature rolling reduces the stacking fault energy of austenitic stainless steel and promotes the formation of shear bands, ε‐martensite, and α′‐martensite. For both low‐temperature and room‐temperature rolling, the austenite and α′‐martensite, austenite and ε‐martensite, α′‐martensite and ε‐martensite pairs follow the Kurdjumov–Sachs (K–S), Shoji–Nishiyama (S–N), and Burgers orientation relationships, respectively. The deformation‐induced martensite transformation sequence of austenitic stainless steel follows the processes γ → α' and γ → ε → α'. A heterogeneous nano/ultrafine‐grained structure with a grain size of 560 nm is obtained by low‐temperature rolling and annealing; room‐temperature rolling achieves a grain size of 690 nm. The heterogeneous nano/ultrafine‐grained steel exhibits a high yield strength of 908 MPa and maintains a satisfactory total elongation of 43%.

metallurgy & metallurgical engineering