Abstract:BaTi 2 O 5 (BT2) nanowires were successfully prepared via molten-salt method. The effects of synthesized temperature, dwell time, and molten salt concentration on the formation of BT2 nanowires were studied. X-ray diffraction patterns reveal that the BT2 nanowires crystallize in a monoclinic crystal structure. Neither the longer dwell time nor molten salt concentration has apparent influence on the formation of BT2 phase structure, whereas the synthesized temperature exerts great effect on the morphology of BT2 nanowires. One-dimensional morphology of the BT2 products was only obtained at a narrow temperature window (870–900 °C). At 970 °C, the morphology of BT2 nanowires was destroyed and they are broken into particles, growing as large flat crystals. The BT2 nanowires synthesized at 900 °C exhibit uniform morphology and grow in the [010] direction, which have an average diameter of 780 nm and length of 15 μm. The formation mechanism of BT2 nanowires in the MSS process is proposed. The BT2 nanowires exhibit the single-crystalline characteristics, as proven by high-resolution TEM images and electron diffraction patterns. Quantitative X-ray energy-dispersive spectroscopy analysis shows the BT2 nanowires having homogeneous chemical compositions, and their atomic cation ratio of Ba:Ti is 1:2.16. Dielectric properties of the BT2 nanowires synthesized at 900 °C are measured at room temperature with the frequency ranged from 10 2 to 10 6 Hz. The BT2 nanowires exhibit almost frequency independent dielectric behavior with dielectric constants of 28–31. The dielectric losses remain constant value of ~ 0.02 below 10 5 Hz, and increase up to 0.04 at 10 6 Hz.

Synthesis of Β-Y2si2o7 Nanowires Via a Facile Molten Salt Method and Their Thermal Properties

Effects of Preparing Conditions on the Synthesis of Y2SiO5 Nanoparticles by Low-Temperature Molten Salt Method

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Microstructural Characterization and Dielectric Properties of Single Crystalline BaTi2O5 Nanowires Prepared by Molten-Salt Method

Key to Enhance Thermoelectric Performance by Controlling Crystal Size of Strontium Titanate

Theoretical prediction and experimental investigation on the thermal and mechanical properties of bulk β-Yb2Si2O7

A Novel Design of Oxidation Protective Β-Y 2 Si 2 O 7 Nanowire Toughened Y 2 SiO 5 /Y 2 O 3 -Al 2 O 3 -Sio 2 Glass Ceramic Coating for SiC Coated Carbon/carbon Composites

Low‐Temperature Preparation of Β‐si3n4 Porous Ceramics with a Small Amount of Li2O–Y2O3

Enhanced Ionic Conductivity in Phase Stabilized Yttria-Doped Zirconia Nanowires

Growth mechanism and synchronous synthesis of 1D beta-sialon nanostructures and beta-sialon-Si3N4 composite powders by a process of reduction nitridation

Enhancement of thermal shock resistance in β-Si3N4 coating with in situ synthesized β-Si3N4 nanowires/nanobelts on porous Si3N4 ceramics

Sintering Behavior and Properties of Lithium Stabilized Sodium Β'' - Alumina Ceramics with YSZ Addition

A Simple Method to Synthesize Single-Crystalline Β-Wollastonite Nanowires

Synthesis, Densification and Characterization of Nanosized Oxide Ceramic Powders with Eutectic Compositions by Heating of Alcohol-Aqueous Salt Solutions

Fabrication and Evaluation of β-SiAlON Nanoceramics

Fabrication, Microstructure, And Corrosion Resistance Of Beta-Sialon Nano-Ceramics

Gel-cast-foam-assisted Combustion Synthesis of Elongated Β-Si3n4 Crystals and Their Effects on Improving the Thermal Conductivity of Silicone Composites

Thermal shock behavior and oxidation resistance of novel SiC nanowires+Si/Yb2Si2O7-Si/Yb2Si2O7 environmental barrier coatings

Molten-salt-mediated synthesis of SiC nanowires for microwave absorption applications

Synthesis of non‐agglomerating submicron/nano Yb 2 Si 2 O 7 powders by carbon‐coated coprecipitation method

Low-temperature Preparation of in Situ Toughened Yb Α-Sialon Ceramics by Spark Plasma Sintering (SPS) with Addition of Combustion Synthesized Seed Crystals