Abstract:Cemented carbides have belonged to the most important engineering materials since their invention in the 1920s. Commonly, they consist of hard WC grains embedded in a cobalt-based ductile binder. Recently, attempts have been made to substitute the cobalt using multicomponent alloys without a principal component (also known as high entropy alloys—HEAs). HEAs usually contain at least five components in more or less equal amounts. The substitution of a cobalt binder with HEAs can lead to the refinement of WC grains; it increases the hardness, fracture toughness, corrosion resistance and oxidation resistance of cemented carbides. For example, a hardness of 2358 HV, fracture toughness of 12.1 MPa.m1/2 and compression strength of 5420 MPa were reached for a WC-based cemented carbide with 20 wt.% of the equimolar AlFeCoNiCrTi HEA with a bcc lattice. The cemented carbide with 10 wt.% of the Co27.4Cr13.8Fe27.4Ni27.4Mo4 HEA with an fcc lattice had a hardness of 2141 HV and fracture toughness of 10.5 MPa.m1/2. These values are higher than those for the typical WC–10 wt.% Co composite. The substitution of Co with HEAs also influences the phase transitions in the binder (between the fcc, bcc and hcp phases). These phase transformations can be successfully used for the purposeful modifications of the properties of the WC-HEA cemented carbides. The shape of the WC/binder interfaces (e.g., their faceting–roughening) can influence the mechanical properties of cemented carbides. The most possible reason for such a behavior is the modification of conditions for dislocation glide as well as the development and growth of cracks at the last stages of deformation. Thus, the substitution of a cobalt binder with HEAs is very promising for the further development of cemented carbides.

Comparison Between Ultrafine-Grained WC–Co and WC–HEA-cemented Carbides

Effect of Submicron SiC Particles on the Properties of Alcocrfeni High Entropy Alloy Coatings

Microstructure and Mechanical Properties of WC-10wt.%AlCoCrFeNi Cemented Carbides Fabricated by Plasma-Assisted Ball Milling

Microstructure and properties of WC-Co/CrMnFeCoNi composite cemented carbides

Insight into Grain Refinement Mechanisms of WC Cemented Carbide with Al0.5CoCrFeNiTi0.5 Binder

The Effect of Carbon Content on the Microstructure and Mechanical Properties of Cemented Carbides with a CoNiFeCr High Entropy Alloy Binder

Densification behavior of ultrafine WC‐based composites with AlxCoCrCuFeNi high‐entropy alloy binders

High Entropy Alloy Bonded Cemented Carbides: Composition, Processing, Microstructure, Properties and Applications

WC-based cemented carbide with NiFeCrWMo high-entropy alloy binder as an alternative to cobalt

WC-Based Cemented Carbides with High Entropy Alloyed Binders: A Review

Comparative study of the microstructure and phase evolution of FeCoCrNiAl high-entropy alloy-matrix WC nanocomposite powders prepared by mechanical alloying

Microstructure and properties of coarse WC-10CoCrFeMnNi cemented carbide by mechanical alloying and hot pressing sintering

Microstructure, Mechanical Properties and Wear Behaviors of Ultrafine-Grain WC-Based Cermets with Different Binder Phases Fabricated by Spark Plasma Sintering

Microstructure and Properties of CoCrFeNi(WC) High-Entropy Alloy Coatings Prepared Using Mechanical Alloying and Hot Pressing Sintering

Metastable FeCrMnCo HEAs with the reinforcement of tungsten carbide fabricated by laser melting: Microstructure, mechanical properties and tribological behaviors

Microstructure and mechanical properties of CoCrFeNiTa high entropy alloy prepared by mechanical alloying and spark plasma sintering

Study on Microstructure and Properties of WC Particle-Reinforced FeCoCrNi-Matrix High Entropy Alloy Composites

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Effect of phase transformation of CoCrFeNiAl high-entropy alloy on mechanical properties of WC-CoCrFeNiAl composites

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides

Study on Effect of High-Entropy Alloy Binder on Microstructure and Properties of WC Cemented Carbide Doped with Rare Earth Oxide