Low Temperature Sintering and Dielectric Properties of (ba0.85ca0.15)(ti0.9zr0.1)o3−xcu2+ Ceramics Obtained by the Sol-Gel Technique

Zhongming Wang,Xiaofang Chen,Xiaolian Chao,Juanjuan Wang,Pengfei Liang,Zupei Yang
DOI: https://doi.org/10.1016/j.ceramint.2016.08.076
IF: 5.532
2016-01-01
Ceramics International
Abstract:Lead-free Cu2+-modified (Ba0.85Ca0.15)(Ti0.9Zr0.1)O3 (BCZT−xCu2+) piezoelectric ceramics was synthesized by sol-gel method. The effects of Cu2+ additions on sintering characteristics, the phase structure, microstructure, electrical properties and complex impedance characteristic were investigated systematically. The XRD patterns exhibited a pure perovskite structure without impurity phase in all samples. SEM micrographs, temperature dependence of dielectric constant and polarization-electric field (P-E) hysteresis loops indicated that a small amount of Cu2+ addition affected the properties obviously. The results revealed that the addition of Cu2+ significantly improved the sinterability of BCZT ceramics which resulted in a reduction of sintering temperature from 1440°C to 1230°C. The TG-DSC was analyzed to verify the reaction process of BCZT−Cu2+ materials. (Ba0.85Ca0.15)(Ti0.9Zr0.1)O3 ceramics with x=0.020 Cu2+ exhibited good electrical properties: εm=12,112, Tc=360K, εr=2614, tanδ=0.026, Kp=0.47 and d33=382pC/N. The results indicated that Cu2+-modified BCZT ceramics could be a promising candidate for commercial purposes.
What problem does this paper attempt to address?