Combination of OH–ions and –OH Groups Within QPPO/PVA Hybrid Membranes for Acid Recovery

Yonghui Wu,Miaomiao Jiang,Jie Cao,Tongwen Xu,Fulin Mao

DOI: https://doi.org/10.1080/19443994.2015.1111810

IF: 1.1

2015-01-01

Desalination and Water Treatment

Abstract:Hybrid membranes are prepared from quaternized poly(2,6-dimethyl-1,4-phenylene oxide) (QPPO), polyvinyl alcohol (PVA), monophenyl triethoxysilane, and tetraethoxysilane through sol-gel process. QPPO contains the anion-exchange groups which can be in the form of -N+(CH3)(3)OH-, -N+(CH3)(3)Cl-, or -N+(CH3)(3)Br-. The OH- ions can combine with PVA-OH groups to form weak interactions such as hydrogen bonds, and thus enhance the compatibility between QPPO and PVA phases and membrane stability. Hybrid membranes with the combination of OH-/-OH are generally homogenous and compact, with the lower water uptake of 57.6-67.4%, methanol content of 38.3-40.2%, and swelling degrees of 223-500% in 65 degrees C water. The ion-exchange capacities are similar in the range of 1.04-1.08mmol/g. Diffusion dialysis (DD) of HCl/FeCl2 solution shows that as the temperature increases from 15 to 55 degrees C, the dialysis coefficients of HCl (U-H) increase from 0.008m/h to 0.014-0.018m/h, while the separation factors decrease from 61-67 to 41-50. The U-H values are similar to that of commercial membrane DF-120 (0.009m/h at 25 degrees C), and the separation factors are higher than those of reported membranes (lower than 48). The U-H values can remain 87-95% after the erosion of HCl/FeCl2 system, with no significant reduction of selectivity. Hence, the combination of OH- ions and PVA-OH groups is effective to elevate membrane stability and selectivity, and the QPPO/PVA hybrid membranes can be potentially applied in DD process for acid recovery.