Abstract:Nanosized zeolites have been found in extensive applications. Herein, a rapid two-step crystallization process (8 h) in a semisolid-like gel system, constructed by simply mixing and grinding solid silica gel, NaOH with TPAOH aqueous solution without extra water addition and any other additives, for the first time is demonstrated to synthesize nanosized silicalite-1 zeolites (similar to 66 nm) with high crystallinity and high product yield (>90%). The obtained nanosized silicalite-1 zeolites exhibit a large BET surface area (418 m(2) g(-1)), a high micropore surface area (316 m(2) g(-1)), and a rich micropore volume (0.14 cm(3) g(-1)). The rapid evolution process of nanosized zeolites could be decoupled into the nucleation stage at low temperatures and the crystallization stage at high temperatures during the two-step crystallization process. Importantly, the semisolid-like gel ensures fast nucleation. Moreover, in the later crystallization period, the fast crystal growth and inhibited ripening endow nanosized zeolite crystals with good crystallinity through a mass transfer-confined space. The obtained silicalite-1 zeolites were successfully applied in the preparation of (h0h)-oriented MFI zeolite membranes on hollow fibers, showing the flux up to 5.44 kg m(-2) h(-1) and the separation factor of 70 during the pervaporation test (5 wt % ethanol/water solution, 60 degrees C). This research develops a state-of-the-art synthetic approach for the efficient preparation of high-quality MFI-type nanozeolites.

Size-controlled Synthesis of Silicalite-1 Nanocrystals

Rapid Synthesis of Small Zeolite Y Crystals in the Absence of Seed Gel

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Size-controlled synthesis of silicalite-1 single crystals in the presence of benzene-1,2-diol

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

Microwave-assisted hydrothermal synthesis of nanozeolites with controllable size

Synthesis of Zeolite ZSM-5 Small Particle Aggregates by a Two-Step Method in the Absence of an Organic Template

Mesoporous Silicalite-1 Zeolite Crystals with Unique Pore Shapes Analogous to the Morphology

Influence of Synthesis Conditions on the Morphology of Silicalite-1 Zeolite

Controlled synthesis of hierarchically porous SAPO-34 zeolites with tailored crystal size and morphology

Synthesis and application of colloidal nanocrystals of the MFI-type zeolites

Facile Synthesis of Hierarchical Nanosized Single‐Crystal Aluminophosphate Molecular Sieves from Highly Homogeneous and Concentrated Precursors

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

Assembled pentasil nanosheet zeolites: Adjusting the sheet thickness through a simple and direct dual templating approach

Nanosized CaCO<sub>3</sub>as Hard Template for Creation of Intracrystal Pores within Silicalite-1 Crystal<sup>†</sup>

Nanoscale Kirkendall growth of silicalite-1 zeolite mesocrystals with controlled mesoporosity and size

The Size-Controllable Synthesis of Nanometer-Sized Mesoporous Silica in Extremely Dilute Surfactant Solution

Self-pillared pentasil zeolites: adjusting the thickness of nanosheets through a simple and direct dual templating approach

Studies on the crystallization process of titanium silicalite-1 (TS-1) synthesized using tetrapropylammonium bromide as a template

Synthesis of High-Performanced Titanium Silicalite-1 Zeolite at Very Low Usage of Tetrapropyl Ammonium Hydroxide

Synthesis of Large Single Crystals of Silica-sodalite and Silicalite-1 in the Presence of Pyrocatechol