Abstract:The synthesis of zeolites with nanosheet morphology has been attracting extensive attention. Despite the steady progress, the direct synthesis of ultrathin nanosheets of FER zeolite with thickness of less than 10 nm is still a great challenge. Herein we report a facile synthesis of FER zeolite nanosheets (named SCM-37) by using octyltrimethylammonium chloride (OTMAC) and 4-dimethylaminopyridine (4-DMAP) as dual organic templates. The effects of synthesis parameters, including initial molar ratio of SiO 2 /Al 2 O 3 , crystallization temperature and time were investigated. It turned out that the crystallization field of SCM-37 was narrow. A two-step crystallization method was utilized to obtain pure and completely crystallized SCM-37 zeolite. SCM-37 was characterized by multiple techniques, including X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen physisorption, Fourier transform infrared (FTIR), ammonia-temperature programmed desorption (NH 3 -TPD) and nuclear magnetic resonance (NMR), and compared with the conventional FER zeolite (C- FER ). The two most significant features of SCM-37 are the ultrathin crystal nanosheet and extremely high external surface area. The thickness of SCM-37 along the a -axis is 4∼7 nm, while that of C- FER is over 20 nm. The external surface area reaches 198 m 2 g −1 , which is over ten times larger than that of C- FER . The catalytic performances of the FER zeolites were evaluated by the cracking of 1,3,5-triisopropylbenzene (T i PB). Although possessing a lower amount of total acid sites, SCM-37 showed higher conversion of T i PB, as well as selectivity to the deep cracking products. The superior performance of SCM-37 was attributed to the higher external surface area arising from the ultrathin nanosheets.

Self-pillared pentasil zeolites: adjusting the thickness of nanosheets through a simple and direct dual templating approach

Assembled pentasil nanosheet zeolites: Adjusting the sheet thickness through a simple and direct dual templating approach

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

Design of a Small Organic Template for the Synthesis of Self-Pillared Pentasil Zeolite Nanosheets

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Synthesis of self-pillared pentasil zeolites without organic templates and seeds

Synthesis of Self-Pillared Zeolite Nanosheets by Repetitive Branching

Two Coexisting Forms of Simple Molecules for Directing Sesqui-Unit-Cell Zeolite Nanosheets

Synthesis of Zeolite ZSM-5 Small Particle Aggregates by a Two-Step Method in the Absence of an Organic Template

Seed-assisted synthesis of a nanosheet-assembled hierarchical SSZ-13 zeolite by coupling a small amount of TMAdaOH with TPOAC

Pillared MFI zeolite nanosheets of a single-unit-cell thickness

Tunable Hierarchical Porous Silica Materials Using Hydrothermal Sedimentation-Aggregation Technique

Controlled synthesis of hierarchically porous SAPO-34 zeolites with tailored crystal size and morphology

Zeolites: Simple Strategies for Fabrication of a Periodic Mesoporous Aluminosilicate with Crystalline Walls (Small 21/2014)

Rational Manipulation of Stacking Arrangements in Three‐Dimensional Zeolites Built from Two‐Dimensional Zeolitic Nanosheets

Tailoring Zeolite ZSM-5 Crystal Morphology/Porosity Through Flexible Utilization of Silicalite-1 Seeds As Templates: Unusual Crystallization Pathways in a Heterogeneous System.

Synthesis of Dendritic ZSM-5 Zeolite through Micellar Templating Controlled by the Amphiphilic Organosilane Chain Length

Facile Synthesis of Hierarchical Nanosized Single‐Crystal Aluminophosphate Molecular Sieves from Highly Homogeneous and Concentrated Precursors

Mesoscale Reorganization of the Depolymerized Aluminosilicate into Single-Crystalline Hierarchical Zeolite

Direct synthesis of ultrathin FER zeolite nanosheets via a dual-template approach

Beyond Creation of Mesoporosity: the Advantages of Polymer‐Based Dual‐Function Templates for Fabricating Hierarchical Zeolites