Abstract:Silicalite-1-type zeolites with unique intracrystal holes or cracks were successfully prepared using a cellulose nanofiber (CNF) as an additional mediating material, and their vapor phase adsorption properties toward methyl tert-butyl ether (MTBE) and n-nitrosodimethylamine (NDMA) were examined. It was found that the mixing protocol of CNF and structure-directing agents (SDAs), the addition amount of CNF, and the CNF/SDAs amount ratio play important roles in forming the holed silicalite-1. The synthesis route that preliminarily mixes CNF with SDAs in a series of controlled conditions is particularly beneficial for the formation of the holed silicalite-1 with mesoporosity and larger pores because the CNF-SDAs composite structure benefits the zeolite growth closely encompassing CNF inside the crystal structure. It also promotes the preferential formation of the orthorhombic phase vicinal to the CNF surface, namely, the surface of the formed internal holes or cracks, with the twin-type crystal size reduced as compared to the non-CNF-templated sample. On the contrary, the synthesis route that mixes CNF with SDAs-silicate composite ions tends to modify the twin-type crystal shape at the same time to form small but uniform well-crystallized particles with less holes or cracks and a dominative monoclinic phase. It was considered that both the inter-subunit structural defect and silanol defect whose content is increased with CNF addition influence the adsorptivity of MTBE and NDMA. Owing to the small twin-type crystal size, the smaller crystal subunits, and the favored short path from the surface of internal holes or cracks, the holed silicalite-1 derived from the CNF and SDA premixture assures the easiest access of adsorbate molecules to the most energetically favored sites and is most appropriate for the adsorption of both MTBE and NDMA among the examined zeolites.

Nanoscale Kirkendall growth of silicalite-1 zeolite mesocrystals with controlled mesoporosity and size

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Microwave-assisted hydrothermal synthesis of nanozeolites with controllable size

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

Space-confined synthesis of nanorod oriented-assembled hierarchical MFI zeolite microspheres

Synthesis of Mesoporous Zeolite Single Crystals with Cheap Porogens

Nucleophilic Etching Growth of Zeolite Materials with High Tunability

Kinetics Guided Synthesis and Performance of Monodisperse Zeolite LTA Microspheres

Seeding-growth of Helical Mesoporous Silica Nanofibers Templated by Achiral Cationic Surfactant.

Cellulose-Nanofiber-Mediated Sorption-Benefitting Holed Silicalite-1 Crystals.

A Seed Surface Crystallization Approach for Rapid Synthesis of Submicron ZSM-5 Zeolite with Controllable Crystal Size and Morphology

Size-controlled Synthesis of Silicalite-1 Nanocrystals

Solvent Evaporation Assisted Preparation of Oriented Nanocrystalline Mesoporous MFI Zeolites

The Synthesis Of Mesoporous Molecular Sieves

Nanosized CaCO<sub>3</sub>as Hard Template for Creation of Intracrystal Pores within Silicalite-1 Crystal<sup>†</sup>

Facile Synthesis of Hierarchical Nanosized Single‐Crystal Aluminophosphate Molecular Sieves from Highly Homogeneous and Concentrated Precursors

Synthesis of MFI Zeolites with Improved Crystallization Rate and Mesoporosity in the Presence of CO2-in-water Emulsions

Single-crystalline MFI Zeolite with Sheet-like Mesopores Layered along the a Axis.

Pillared MFI zeolite nanosheets of a single-unit-cell thickness