Abstract:The influence of extrusion temperature on microstructure and mechanical properties of Mg97Y2Zn alloy have been investigated. The one-step extrusion and the two-step extrusion were conducted at the different temperatures. It was found that the extrusion temperature not only influence the microstructure of Mg97Y2Zn1 alloy but also its mechanical properties. The microstructure of the Mg97Y2Zn1 alloy processed by the one-step extrusion at 673K is non-uniform. Coarse grains elongated along the extrusion direction coexisted with small volume fraction of fine dynamic recrystallization (DRX) grains formed around secondary phase and in the vicinity of the distorted original grain boundaries. After the two-step extrusion at different temperature from 623K to 773K, the DRX process of Mg97Y2Zn1 alloy is completed and the uniform equiaxed grains were obtained. The final grain size increases with increasing deformation temperature. The alloy processed by first step extrusion exhibits highest strength by lowest elongation. After the second step extrusion, however, the strength is decreased and elongation is increased. During the second step extrusion at 623K, twins are observed at the beginning of the extrusion. The small recrystallized grains appeared along some original grain boundary areas and twinned regions. With increasing strain, the volume fraction of recrystallized grains increases progressively. However, there is no twin occurs observed at the beginning of the second step extrusion at 773K. Instead, some uniform equiaxed recrystallized grains can be observed. The small recrystallized grains appeared along some original grain boundary areas. With increasing strain, the volume fraction of recrystallized grains increases progressively and the grain size is increasing too. It seems that the DRX was brought forward at higher extrusion temperature.

Effects of Temperature in the New Compound Extrusion on Microstructures and Properties of AZ61

Effects of Extrusion–Shear Process Conditions on the Microstructures and Mechanical Properties of AZ31 Magnesium Alloy

Effect of extrusion temperature on microstructure, mechanical properties, and deformation mechanism of Mg-2.5Er-0.6Zr alloy

Effects of Direct Extrusion Process on Microstructure, Texture Evolution and Yield Strength of Magnesium Alloy Az31

Effects of Extrusion Processes on Microstructure and Properties of AZ31 Magnesium Alloy

Effect of Extrusion Deformation on Microstructures and Properties of AZ31 Magnesium Alloy

Study of the microstructure, texture and tensile properties of as-extruded AZ91 magnesium alloy

Microstructure and tensile properties of a low-alloyed magnesium alloy: effect of extrusion temperature

Effects of extrusion ratio and temperature on the microstructure and mechanical properties of Mg–Zn–Yb–Zr extrusion alloys

Microstructures and Mechanical Properties of Extruded Mg-9Gd-4Y-0.6Zr-T5 at Elevated Temperatures

Investigation of microstructure and mechanical properties of ZK60 magnesium alloy achieved by extrusion-shearing process

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Microstructure and Mechanical Properties of Extruded Az31 Magnesium Alloy Sheet

Thermomechanical Processing and Superplasticity of AZ91 Magnesium Alloy

Effect of extrusion temperature on the microstructure and mechanical properties of Mg97Y2Zn1 alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

Microstructure Evolution and Mechanical Properties of AZ31 Magnesium Alloy Sheets Prepared by Low-Speed Extrusion with Different Temperature

Influence of Extrusion Temperature on Microstructure and Mechanical Properties of Mg-4Y-4Sm-0.5Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Ca Alloy

Effect of Extrusion Parameters on Microstructure and Mechanical Properties of Mg-7.5Gd-2.5Y-3.5Zn-0.9Ca-0.4Zr (wt%) Alloy

Effect of grain size distribution and texture on the cold extrusion behavior and mechanical properties of AZ31 Mg alloy