Abstract:A supported Ni–P amorphous catalyst (Ni–P/SiO2) was prepared by electroless plating. When the sample was treated at elevated temperatures from 363 to 973 K in N2 flow for 2.0 h, the XRD patterns and SEM morphologies revealed that the Ni–P amorphous alloy crystallized stepwise from 673 to 873 K. The stabilizing effect of the support on the Ni–P amorphous alloy was observed by DSC, TPO, and TPR, which was attributed to the high dispersion of the Ni–P alloy particles in the support matrix, the affinity of SiO2 support for the Ni–P alloy particles, and the transfer of the heat produced during the crystallization from the surface to the bulk of the support. The change in the activity of the as-prepared Ni–P/SiO2 amorphous catalyst during heat treatment was measured using the liquid phase benzaldehyde hydrogenation as a probe and by comparing to that of the corresponding Ni/SiO2 crystalline catalyst. On one hand, the activity of both two catalysts decreased with the increase of the treating temperature owing to the decrease in surface active Ni atoms caused by the coalescence of small Ni particles at high temperature. On the other hand, the two catalysts exhibited considerably different catalytic behaviors during the heating treatment. (1) Only a smooth decrease in the activity of the Ni/SiO2 catalyst was observed with the increase of the treating temperature. While an impressive decrease in the activity of the Ni–P/SiO2 amorphous catalyst was observed in the temperature range from 673 to 873 K corresponding to its crystallization; (2) no significant change in the apparent activation energy (Ea) and the TOF value was observed during the heating pretreatment of the Ni/SiO2 catalyst. However, a considerable increase in Ea and a decrease in the TOF value were observed after the crystallization of the Ni–P/SiO2 amorphous catalyst. These results demonstrated a crystallization deactivation of the Ni–P/SiO2 amorphous catalyst. According to various characterizations, such as EXAFS, XRD, SEM, TEM, XPS, DSC, ICP, TPR, TPO, TPD, and hydrogen chemisorption, the decrease in the number of surface active Ni atoms and the surface P content in the Ni–P alloy, the change in the structural characteristics, and the adsorbing properties of the Ni active sites were the main factors responsible for the deactivation of Ni–P/SiO2 amorphous catalyst during the crystallization.

Interaction Mechanism of Ni(NO3)2·6H2O and P123 in Preparing Highly-Dispersed Ni/SBA-15 Catalytic Materials

Equilibrium Uptake and Adsorption State of Pd Precursor in Preparation of Pd/C Catalyst by Impregnation

Role of Poly(n-Vinyl-2-pyrrolidone) in Ni Dispersion for Highly-Dispersed Ni/SBA-15 Catalyst and Its Catalytic Performance in Carbon Dioxide Reforming of Methane

High Catalytic Activity of Magnetic FeOx/NiOy/SBA-15: the Role of Ni in the Bimetallic Oxides at the Nanometer Level

Dispersion of Nano Nickel Particles over SBA-15 Modified by Carbon Films on Pore Walls

Co2 Reforming of Methane to Syngas over Highly-Stable Ni/Sba-15 Catalysts Prepared by P123-Assisted Method

Characterization of Dispersion and Surface States of NiO/γ-alumina and NiO/La2O3–γ-alumina Catalysts

Noble Metal Catalyzed Preparation of Ni2P/α-Al2O3

Promotion Of Ni On Performance Of Pd-Only Catalyst For Destractive Removal Of Volatile Organic Wastes

An Approach to Preparing Highly Dispersed Ni2P/SiO2 Catalyst

Preparation of PdNi bimetallic loaded amino modified porous carbon material catalyst based on chitosan and its applications

Template-Mediated Ni(Ii) Dispersion in Mesoporous Sio2 for Preparation of Highly Dispersed Ni Catalysts: Influence of Template Type

Synthesis of highly dispersed Pd nanoparticles within SBA-15 for the catalytic reduction of p-nitrophenol

Promotional effect of embedded Ni NPs in alginate-based carbon toward Pd NPs efficiency for high-concentration p-nitrophenol reduction

Synthesis of Pd Decorated Flower-Like NiO Composite and Its High Catalytic Performance for CO Oxidation under Ambient Conditions

Effects of Ni–Al2O3 Interaction on NiMo/Al2O3 Hydrodesulfurization Catalysts

ABATEMENT OF HARMFUL CARBON MONOXIDE OVER THE NICKLE DOPED CO3 O4 CATALYST

Crystallization Deactivation of Ni–P/SiO2 Amorphous Catalystand the Stabilizing Effect of Silica Support on the Ni–P Amorphous Structure

Characterization Of Dispersion And Surface-States Of Nio/Gamma-Alumina And Nio/La2o3-Gamma-Alumina Catalysts

Regulation of Ni3Sn2 Intermetallic Catalyst by Highly Dispersed Pd Species to Boost Propyne Semi-Hydrogenation

Preparation of Highly Dispersed Nickel Phosphide Catalyst Supported on Nano-Sized Y Zeolite and Its Hydrodesulfurization Performance