Abstract:The chemical-vapor-deposition (CVD) process is sufficiently well developed to allow the large-scale production of carbon nanotubes (CNTs). Metal nanoparticles (Fe, Co, Ni, etc.) are usually immobilized on a solid support and then decompose the gaseous hydrocarbon feedstocks into fragmented carbon units at elevated temperatures of 700-1100°C. Metal carbides are formed and then these dominate the growth of filamentous carbon as a structural template. The produced CNTs cannot stay firmly with an inert support and so inevitably detach away, especially during liquidphase purification or mechanical treatment. The biggest difficulties when handling the loose powder are filtration in the slurry-phase operations and the large pressure drops in fixed-bed reactors. These problems very much limit the application of CNTs on a large scale. The fabrication of carbon filaments on a structured support (e.g., activated carbon, carbon fibers, porous frameworks, graphite) has also suffered from discontinuities in the structure. The future use of CNTs has also been restricted by the technical requirements and the necessary high energy consumption to operate the intense and complicated CVD process. To avoid any mechanical post-treatment of powder and the risk of explosion during CVD synthesis, we have explored a simple method to produce monolithic CNTs directly as millimeter-scale spheres, featuring an integral continuity in the structure from microscopic to macroscopic scales. The whole process of CNTs growth has been conducted in a flow of ultrapure N2, involving a set of elementary steps in the solid phase being less complex than the widely used CVD process. The growth of CNTs is based on a solid reaction mechanism and well-graphitized nanotubes can be obtained even at a temperature as low as 400C. Direct observation of all growth events is made by using in-situ transmission electron microscopy (TEM), X-ray diffraction (XRD), IR, Raman spectroscopy and thermogravimetric analysis. A commercial styrene-divinylbenzene copolymer resin was used as the carbon precursor. According to Scheme 1, the ion-exchanged resin spheres were calcined at 800C in a flow of N2 or vacuum, after which the average diameter decreases from 0.77 to 0.49 mm, while the bulk density increases from 0.55 to 0.91 g ml. A novel macroscopic structure can be clearly seen, especially after the removal of the Fe nanoparticles and the amorphous carbon species by refluxing the spheres in concentrated HNO3. As seen in Fig. 1a, the twisted nanotubes construct the monolith while keeping a spherical shape. The cross-section views of the hand-broken spheres show no difference in the structure between the bulk and the surface, indicating a homogeneous distribution of the nanotubes in the millimeter-scale spheres (Fig. 1b). The nitrogen adsorption/ desorption isotherm shows a hysteresis loop to identify a typical mesoporous feature. The measured BET surface area and the pore volume are 223.7 m g and 0.42 ml g, respectively. The distribution of the pores ranges between about 2 and 15 nm.

Large Scale Production of Carbon Nanotube Arrays on the Sphere Surface from Liquefied Petroleum Gas at Low Cost

Large‐Scale Synthesis of Rings of Bundled Single‐Walled Carbon Nanotubes by Floating Chemical Vapor Deposition

Large Area Growth of Aligned CNT Arrays on Spheres: Towards the Large Scale and Continuous Production

Large Area Growth of Aligned Cnt Arrays on Spheres: Towards Large Scale and Continuous Production

Liquefied petroleum gas containing sulfur as the carbon source for carbon nanotube forests

Large Area Growth of Aligned CNT Arrays on Spheres: Cost Performance and Product Control

Growth of High-Density Parallel Arrays of Ultralong Carbon Nanotubes with Catalysts Pinned by Silica Nanospheres

Spherical Multi-Walled Carbon-Nanotube Architectures : Formation Mechanism and Catalytic Performance

SYNTHESIS OF SINGLE-WALLED CARBON NANOTUBES FROM LIQUEFIED PETROLEUM GAS

The Mass Production of Carbon Nanotubes Using a Nano-Agglomerate Fluidized Bed Reactor: A Multiscale Space–time Analysis

Radial growth of vertically aligned carbon nanotube arrays from ethylene on ceramic spheres

Modulating the Diameter of Carbon Nanotubes in Array Form Via Floating Catalyst Chemical Vapor Deposition

Plasma-modified Flaky FeSiAl Alloy for Efficient Growth of Carbon Nanotube Arrays with High Carbon Conversion Rate

Coupled process of plastics pyrolysis and chemical vapor deposition for controllable synthesis of vertically aligned carbon nanotube arrays

Mass Production of Aligned Carbon Nanotube Arrays by Fluidized Bed Catalytic Chemical Vapor Deposition

Growth of Uniform Carbon Nanotube Arrays with Sandwich Technology

Vertically aligned carbon nanotube arrays grown on a lamellar catalyst by fluidized bed catalytic chemical vapor deposition

Controllable and Large-Scale Synthesis of Carbon Nanofibers, Bamboo-Like Nanotubes, and Chains of Nanospheres over Fe/Sno2 and Their Microwave-Absorption Properties

Rapid Growth of Well-Aligned Carbon Nanotube Arrays

Ultralow Feeding Gas Flow Guiding Growth of Large-Scale Horizontally Aligned Single-Walled Carbon Nanotube Arrays

Floating Bimetallic Catalysts for Growing 30 cm‐Long Carbon Nanotube Arrays with High Yields and Uniformity