Abstract:To in situ grow carbon nanotubes (CNTs) on the surface of carbon fibre fabric (CFF) with suitable diameter and uniform distribution, controllable catalyst deposition is the key process. A controllable and non-destructive pre-treatment, that is, electrochemical oxidation pre-treatment, was explored to facilitate uniform `seeding` nano-sized catalyst particles on the surface of CFF without causing damage to carbon fibres. Main factors, such as voltage, concentration of electrolyte, electrolytic time, catalyst type and concentration of the catalyst precursor, were investigated. X-ray photoelectron spectroscopy tests indicated that voltage, concentration of electrolyte and duration of electrochemical treatment determined the distribution density of catalyst nanoparticles by controlling the concentration of the functional groups, while the diameter of catalyst particles was decided by the concentration of Fe(NO3)3 and CO(NH2)2. Besides, the diameter of catalyst particles could be modulated by adding Al(NO3)3 in the solution of the catalyst precursor. At the same time, to avoid cementite produced during the calcination and reduction process, the temperature should be controlled below 773 K. Scanning electron microscopy observations indicated that well-dispersed in situ grown CNTs could be obtained after CFF had been chemical oxidised at the voltage of 10 V for 10 s with 0.02 M NH4HCO3 as electrolyte and followed by catalyst deposition.

Preloading Catalysts in the Reactor for Repeated Growth of Horizontally Aligned Carbon Nanotube Arrays

Uniform Patterned Growth of Carbon Nanotubes Without Surface Carbon

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Preferential Growth of Carbon Nanotubes/Nanofibers Using Lithographically Patterned Catalysts

Very Fast Growth of Millimeter-Tall Aligned Carbon Nanotubes Between Two Stacked Substrates Coated with a Metal Catalyst

Multi-Directional Growth of Aligned Carbon Nanotubes Over Catalyst Film Prepared by Atomic Layer Deposition

Growth of High-Density Horizontal SWNT Arrays Using Multi-Cycle In-Situ Loading Catalysts

Carbon dioxide-boosted growth of high-density and vertically aligned carbon nanotube arrays on a stainless steel mesh

Ultralow Feeding Gas Flow Guiding Growth of Large-Scale Horizontally Aligned Single-Walled Carbon Nanotube Arrays

Growth of High-Density Parallel Arrays of Ultralong Carbon Nanotubes with Catalysts Pinned by Silica Nanospheres

Growth of Tall Vertical Carbon Nanotube Forests using Al-Fe Catalysts and Transfer to Flexible Substrates

Mass Production of Aligned Carbon Nanotube Arrays by Fluidized Bed Catalytic Chemical Vapor Deposition

Growth of High-Density Horizontal SWNT Arrays by Pre-Cracking of Carbon Source

Large Area Growth of Aligned CNT Arrays on Spheres: Cost Performance and Product Control

Confined Fe Catalysts for High‐Density SWNT Arrays Growth: a New Territory for Catalyst‐Substrate Interaction Engineering

Rational Recipe for Bulk Growth of Graphene/Carbon Nanotube Hybrids: New Insights from In-Situ Characterization on Working Catalysts

Rapid Growth of Well-Aligned Carbon Nanotube Arrays

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes

How Catalysts Affect the Growth of Single-Walled Carbon Nanotubes on Substrates

Non-destructive and controllable catalyst deposition of in situ growing carbon nanotubes onto the carbon fibre fabric

Selective Growth of Carbon Nanotube on Silicon Substrates