ZrB 2 -Sic-ta 4 HfC 5 /ta 4 HfC 5 Oxidation-Resistant Dual-Layer Coating Fabricated by Spark Plasma Sintering for C/C Composites

Changling Zhou,Yushi Qi,Yehong Cheng,Wenbo Han
DOI: https://doi.org/10.1007/s11665-018-3807-7
IF: 2.3
2019-01-01
Journal of Materials Engineering and Performance
Abstract:In this work, a ZrB2-SiC-Ta4HfC5/Ta4HfC5 oxidation-resistant dual-layer coating was fabricated to improve the oxidation resistance of carbon–carbon (C/C) composites. The coating was prepared by pack cementation combined with the slurry paste method. Spark plasma sintering was used in the procedure. The as-prepared dual-layer coating was approximately 110 μm, and no distinct interface was observed between the coating and the matrix. The isothermal oxidation test results showed that the dual coating effectively prevented C/C composites from oxidizing. The weight loss of the coated samples was only 3.3 and 9.5% after oxidation at 1773 K for 20 h and ten thermal shock cycles between 1773 K and room temperature in air, respectively. The pores and microcracks were the main reason for the failure of the coating.
What problem does this paper attempt to address?