Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H2S at 90°C
Junwen Tang,Yawei Shao,Tao Zhang,Guozhe Meng,Fuhui Wang
DOI: https://doi.org/10.1016/j.corsci.2011.01.041
IF: 7.72
2011-01-01
Corrosion Science
Abstract:The corrosion behavior of SAE-1020 carbon steel in H 2 S-containing solutions with different concentration of HCl at 90 °C was investigated by weight loss, electrochemical measurements, SEM and XRD analysis. The results showed that the corrosion rate of carbon steel increased with increasing HCl concentration. Uniform corrosion was found on the carbon steel surface in H 2 S + HCl solutions, while corrosion cavities were observed in the solution only containing H 2 S. The ratio of Faradaic process of total corrosion process increased with the increase of HCl concentration. The corrosion products were solely composed of mackinawite in the H 2 S-containing solutions with or without HCl. Keywords A. Steel B. Weight loss B. EIS B. SEM B. XRD C. Acid corrosion 1 Introduction Petrochemical plants have suffered continuous economic loss and human casualties due to metallic materials corrosion in H 2 S-containing environments [1] . The salts and sulfide compounds dissolved in crude oil can provoke the formation of a corrosive aqueous solution whose chemical composition involves the presence of both hydrochloric acid (HCl) and hydrogen sulfide (H 2 S) [2,3] . This corrosion aqueous solution is very aggressive causing varied damages on carbon steel during plant operation in primary distillation plants. Several previous studies have been performed related to the corrosion process of iron and steel in H 2 S solutions [2,4–15] . These works studied the influence of H 2 S on the corrosion phenomena at ambient temperature. In H 2 S-containing solutions, the corrosion process of metal may be accompanied by the formation of sulfide film on the metal surface and leads to more complicated corrosion behavior [12] . Previous researches have shown that H 2 S had a remarkable acceleration effect on both the anodic iron dissolution and the cathodic evolution in most cases [6–9] , but H 2 S may exhibited an inhibitive effect on the corrosion of iron or steel weld while the lower H 2 S concentration (⩽0.04 mmol L −1 ), pH value of 3–5, and the longer immersion time (⩾2 h) are met simultaneously [7,8,12,13] . Recently, the influence of H 2 S concentration on the corrosion behavior of carbon steel at 90 °C has been investigated [16] . However, little research has been done on the corrosion behavior of carbon steel in the presence of H 2 S and HCl at the temperature of the condensation system in primary distillation plants, which usually is greater than 70 °C. Therefore, the purpose of the present work was to study the effect of HCl concentration on the corrosion behavior of SAE-1020 carbon steel in H 2 S-containing solutions at a typical temperature (90 °C) of the condensation system in CNPC primary distillation plants by means of weight loss method, electrochemical measurements, X-ray diffraction (XRD) and scanning electron microscopy (SEM). 2 Experiment 2.1 Experimental setup Experiments were conducted at atmospheric pressure in a glass cell ( Fig. 1 ) including a water bath in order to control temperature to 90 ± 1 °C. A typical three-electrode cell was used with a saturated calomel electrode (SCE) (GD-II, BRICEM, China) as the reference electrode, a large piece of platinum plate with a surface area of over 4 cm 2 as the counter electrode, and a SAE-1020 carbon steel specimen as the working electrode. Residual H 2 S was absorbed by gas absorbent. 2.2 Material and specimen preparation The material employed was SAE-1020 carbon steel, which has a composition of 0.20% C, 0.32% Si, 0.56% Mn, 0.033% P, 0.032% S and Fe as the balance. The specimens with an exposed surface of 10.0 × 10.0 mm 2 were machined from the carbon steel sheet and embedded in the epoxy resin. Only its cross-section contacted the electrolyte. Prior to each experiment, the exposed metal surface of each specimen was ground with wet silicon carbide paper to 1000 grade, degreased with acetone, cleansed with distilled water and dried in a compressed hot air flow. 2.3 Electrolyte solutions preparation Analytical reagent grade H 2 SO 4 , HCl, Na 2 SO 4 and Na 2 S were used directly without further purification. The 0.25 M Na 2 SO 4 , 0.5 M H 2 SO 4 and 0.5 M Na 2 S solutions were prepared in distilled water. Base solution (0.25 M Na 2 SO 4 ) containing 198.99 mg L −1 H 2 S were used as a common corrosion environment. The chemical composition of hydrogen sulfide solution was obtained based on the average concentration of H 2 S in the condensation system of CNPC primary distillation plants. The H 2 S-containing solutions with different concentration of HCl were prepared from the concentrated Na 2 S solution and the H 2 SO 4 solution and the analytical regent grade HCl in the following way: 1000 mL of the 0.25 M Na 2 SO 4 solution was filled in the glass cell at first, and then the suitable volume of Na 2 S solution and an equivalent volume of H 2 SO 4 solution were added into the Na 2 SO 4 solution, subsequently the suitable volume of concentrated hydrochloric acid (37 wt%) was added into above solution. Take the case of the preparation of the 198.99 mg L −1 H 2 S solution containing 0.010 wt% HCl, 25.43 ml of 0.5 M Na 2 S solution and the same volume of 0.5 M H 2 SO 4 solution were firstly added into 1000 ml Na 2 SO 4 solution, and then 0.25 ml of 37 wt% HCl was added to the solution. The pH value of the test solution was determined using a pH meter (PHSJ-4A, SPSIC, China). The precise concentration of H 2 S was determined by the iodometric titration method in triplicate to make sure the results were reproducible and reliable. Table 1 summarizes the different electrolyte solutions studied in the present work. 2.4 Electrochemical measurement Potentiodynamic polarization curves measurements were performed at a potential scan rate of 0.333 mV s −1 . The potential range was from −0.30 V to 0.30 V vs. open-circuit potential (OCP). All potentials reported in this paper were measured with respect to the SCE. The electrochemical impedance spectroscopies (EIS) were performed at OCP with a sinusoid signal of 5 mV amplitude and at frequencies ranging from 100 kHz to 10 MHz. The data were acquired in four cycles at each frequency, for providing good precision at all frequencies. The experimental data were analyzed using the commercial software ZsimpWin®. For better reproducibility, all above electrochemical experiments were repeated more than three times and were carried out using IviumStat Electrochemical Interface (Ivium Technologies, Netherlands) controlled by PC. 2.5 Weight loss experiment Specimens were cut into 10.0 × 10.0 × 2.5 mm for weight loss tests and three specimens used for each series were measured for good reproducibility. The samples were weighed before exposure by means of a digital balance (Sartorius CP225D) with a precision of 0.00001 g for the original weight ( W 0 ). After immersion for 1 h in test solutions with a bath at 90 ± 1 °C, the corroded specimens were taken out from the solutions, and cleaned with distilled water. The corrosion products on carbon steel surface were removed using the chemical products-cleanup method [17] . Finally, the samples were weighed again in order to obtain the final weight ( W 1 ). The corrosion rate ( CR ) (g m −2 h −1 ) was calculated with Eq. (1) . (1) CR = W 0 - W 1 A × t where W 0 (g) and W 1 (g) are the original weight and final weight of specimens, respectively, A (m 2 ) is the exposed surface area of specimens, and t (h) represents the immersion time. 2.6 Surface morphology observation and corrosion products analysis The corrosion morphology of carbon steel was characterized by a digital camera (SONY W170) and SEM (Cambridge S240). Corrosion products on the corroded samples were analyzed using X′ Pert Pro X-ray diffractometer with a Cu Kα X-ray source to determine the phases. To observe the corrosion morphology under the corrosion products, the corrosion products were removed using the chemical products-cleanup method [17] . 3 Results 3.1 Corrosion rates of carbon steel Weight loss measurements can provide the most reliable results concerning the corrosion rates ( CR ) of carbon steel, so that the corresponding corrosion data obtained from them approach service conditions are more accurately than that obtained with any other test [18,19] . The average corrosion rates of carbon steel in the H 2 S solutions with and without HCl obtained from weight loss tests are shown in Fig. 2 . Corrosion rates of carbon steel increased significantly with increasing HCl concentration. The corrosion rate increased up to 17.31 g m −2 h −1 in the solution with 0.100 wt% HCl, which was 2-fold greater than that of carbon steel in HCl-free solution (8.30 g m −2 h −1 ). The results indicated that the HCl concentration had a strong influence on the corrosion resistance of the carbon steel and the carbon steel showed a greater activity for higher HCl concentrations. 3.2 Potentiodynamic polarization curves The potentiodynamic polarization curves for carbon steel in the H 2 S-containing solutions in absence and presence of different HCl concentrations at 90 °C are shown in Fig. 3 . A typical feature of these polarization curves was that the hydrogen evolution reaction (cathodic curve) was remarkably accelerated by increasing HCl concentration. However, the anodic curves obtained showed very similar current densities, regardless of the HCl concentration. As can be seen in Fig. 3 , the anodic process of carbon steel exhibited the anodic iron dissolution. This could be due to the fact that the corrosion process involved formation and dissolution of corrosion products, always maintaining the surface active [4] . Therefore, the fact that the anodic current densities were not modified in the H 2 S-containing solutions with various HCl concentrations was possibly attributed to metal dissolution [20–22] . However, the cathodic process of carbon steel was more complicated and remarkably depended on the concentration of HCl. The determination of corrosion parameters ( E corr , R p , b a , b c , and i corr ) could provide more information about the overall corrosion process. Jankowski and Juchniewicz [23] proposed a four-point method for determining the corrosion rate as a simple and accurate method. In this method, four current density values at four applied potentials, E = Δ E , - Δ E , 2 Δ E , and - 2 Δ E , on a polarization curve are used to determine the corrosion current density ( i corr ) and the harmonic mean of the Tafel constants ( B ) and of each Tafel constant ( b a and b c ). The i corr and b a and b c are determined from the following equations [23,24] : (2) i corr = I 1 I - 1 I 2 I - 2 - 4 I 1 I - 1 (3) B = b a b c 2.3 ( b a + b c ) = Δ E cosh - 1 I 2 I - 2 2 I 1 I - 1 - 1 (4) b a = Δ E log { I 1 / i corr [ 1 - exp ( Δ E / B ) ] } (5) b c = 2.3 b a B b a - 2.3 B where I 1 , I −1 , I 2 , and I −2 are the current densities at the four overpotentials, Δ E , - Δ E , 2 Δ E , and - 2 Δ E . These equations from the Bulter–Volmer equation that is valid in the potential range where reactions are controlled by activation process [24] . Additionally, according to Stern and Geary [25] , the polarization resistance ( R p ) can be expressed as: (6) R p = B i corr The corrosion parameters for the carbon steel were determined by the analysis software of IviumStat Electrochemical Interface with the four-point method. Table 2 summarizes the corrosion potentials ( E corr ), Tafel slopes ( b a and b c represent anodic and cathodic, respectively) and corrosion currents ( i corr ) and their standard deviation as well as the calculated values of polarization resistances ( R p ). The corrosion potential shifted towards positive direction with increasing HCl concentration and the phenomenon seemed to be more remarkably in the solutions with high concentration of HCl. For example, the corrosion potential of carbon steel in the solution containing 0.100 wt% HCl was close to −0.57 V SCE , which was 100 mV more positive than that measured in the HCl-free solution. It is well known that the corrosion potential is the result of the two competitive reactions of the cathodic and anodic process [26,27] . In this work, the anodic current densities were not modified in the H 2 S-containing solutions with various HCl concentrations, so the cathodic hydrogen evolution process of metal surface was promoted with increasing HCl concentration, which contributed to the positive shift of the corrosion potential. Anodic Tafel slops, b a ( Table 2 ), in all solutions were very similar (about 0.08 V per decade), regardless of the concentration of HCl in the H 2 S solutions. This behavior indicated that the concentration of HCl contributed similarly to the anodic process. However, the slopes of cathodic branch, b c , ( Table 2 ) were considerably dependent on the concentration of HCl. This fact, along with greater values of these slopes compared with those from the anodic branch, indicated the complex nature of the reduction process [4] . Additionally, the corrosion current density ( i corr ) increased from 0.188 mA cm −2 to 1.49 mA cm −2 and the polarization resistance R p values decreased with increasing HCl concentration in the solutions ( Table 2 ). The results implied that the cathodic process was controlled by the concentration of HCl in the solutions, and the corrosion resistance of carbon steel was obviously deteriorated with increasing concentration of HCl from 0 wt% to 0.100 wt%. 3.3 Electrochemical impedance spectroscopy Fig. 4 shows the Nyquist diagrams obtained for carbon steel in the H 2 S-containing solutions with various concentration of HCl at the open-circuit potential (OCP). The shape and the diameter of these experimental impedance circles depended on the concentration of HCl. The impedance diagrams obtained in the solutions without and with different HCl concentrations (0.005, 0.010, 0.025, and 0.050 (in wt%)) revealed two well-separated capacitive loops, including a high frequency (HF) depressed capacitive loop and a low frequency (LF) capacitive loop. However, the diagram measured in the 0.100 wt% HCl solution seemed to make up of three semicircles with two capacitive loops and an inductive loop. According to the measured EIS spectra in Fig. 4 , it can be seen that the diameter of the circle of the high frequency loop decreased with increasing concentration of HCl. It was determined that the diameter was about 35 Ω cm 2 in the H 2 S solution without HCl, which was almost 5-fold greater than that of carbon steel in the 0.100 wt% HCl solution (about 7 Ω cm 2 ). This indicated that the corrosion resistance of carbon steel deteriorated with increasing HCl concentration, which was in good agreement with the results of the weight loss test ( Fig. 2 ) and the potentiodynamic polarization curves ( Fig. 3 ). At the same time, the Nyquist plot measured in the 0.010 wt% HCl solution exhibited a high frequency capacitive loop whose top frequency (5.62 Hz) was greater than that of the capacitive loop (2.37 Hz) obtained in the H 2 S solution with 0.005 wt% HCl or without HCl. The top frequency of a high frequency capacitive loop remarkably increased as HCl concentration increased above 0.025 wt%, up to 0.100 wt% ( Fig. 4 b), which also indicated that the carbon steel was corroded more easily in the stronger acidic solutions [7] . 3.4 Effect of H 2 S and HCl on the corrosion product and corrosion morphology Fig. 5 shows the X-ray diffractograms of the corrosion products on the surface of carbon steel in H 2 S-containing solution without and with 0.010 wt% HCl at 90 °C, respectively. It was determined that the corrosion products just consisted of mackinawite in both of the above cases, indicating that hydrochloric acid had not influence on the composition of corrosion products in H 2 S-containing solutions. In general, the corrosion products on carbon steel surface are non-stoichiometric iron sulfide films mainly composed of mackinawite and pyrrhotite in environment containing H 2 S [2,28–42] . Berner [40,43] and Rickard [44] have observed that mackinawite is typically the sole crystalline product of precipitation of ferrous ions by H 2 S or its salts below 100 °C in the absence of oxidants. However, the protective property of iron sulfide film depends on the H 2 S concentration, pH of solution and immersion time of electrode [8] . The solubility of iron sulfide increased with decreasing pH value or increasing the HCl concentration. At the pH values of 3–5, H 2 S begins to exhibit its inhibiting effect as FeSH + species can form partially mackinawite [8] . Shoesmith et al. [45] studied the corrosion of iron in a deaerated H 2 S-saturated solution and found that metal dissolution predominated and very little iron sulfide was formed at the lower pH values (1.7 and 2.7). The macroscopical corrosion morphology of carbon steel surface after 1 h immersion in the H 2 S-containing solutions with different HCl concentration at 90 °C is shown in Fig. 6 . The black corrosion products formed on the steel surface in the H 2 S-containing solutions without HCl ( Fig. 6 a) or with low HCl concentration (0.005 wt% and 0.010 wt%) ( Fig. 6 b and c) could be observed. With the increase of HCl concentration, the region of carbon steel surface covered with the black corrosion products decreased obviously ( Fig. 6 d–f). The pH value decreased with increasing the HCl concentration and the iron sulfide not easily deposited on the steel surface. At the lower pH values metal dissolution predominated and little iron sulfide formed due to the relatively greater solubility of iron sulfide phases [8,13] . SEM micrographs of carbon steel after 1 h immersion in H 2 S-containing solutions with different concentration of HCl are shown in Fig. 7 . The carbon steel surface was greatly corroded in all solutions. After removing the corrosion products, the corrosion cavities were observed on the carbon steel in the H 2 S-containing solution without HCl ( Fig. 7 b). However, when HCl was added into the H 2 S-containing solutions, the corrosion cavities on the carbon steel surface disappeared and the uniform corrosion appeared. Additionally, the granular substances appeared on the surface of carbon steel were also observed ( Fig. 7 d, f, h, k, and n). 4 Discussion 4.1 Effect of HCl on the corrosion of non-Faradaic process From optical micrograph of SAE-1020 carbon steel ( Fig. 8 ), the phases of carbon steel mainly consisted of ferrite (F), and carbides (Fe 3 C) deposited in the grain boundary especially in the tri-angle grain boundary [16] . The corrosion processes of carbon steel in H 2 S-containing solutions consisted of two simultaneous processes: grain dissolution process and micro-galvanic corrosion process [16] . Severe corrosion cavities on the carbon steel surface in the H 2 S-containing solution due to cementites stripping off from the grain boundary, which is the potential-independent “chemical dissolution” process or the non-Faradaic process. However, with the addition of HCl in the H 2 S-containing solution, the grain dissolution process was promoted by the addition of HCl, the cementite was not easily stripped off and the uniform corrosion appeared on the carbon steel surface ( Fig. 7 d, f, h, k, and n). i corrweight of the weight loss method reflected the total corrosion rate, including Faradaic process and non-Faradaic process. However, i corrTafel of the potentiodynamic polarization method just reflected the corrosion rate of Faradaic process. Ratio in Eq. (7) can reflect the influence of non-Faradaic process on the total corrosion rate ( Fig. 9 ). (7) Ratio ( % ) = i corrweight - i corrTafel i corrweight × 100 From Fig. 9 , in the H 2 S-containing without HCl, Ratio is 76%, which meant that non-Faradaic process was the dominant process. That is to say, the process of cementites stripped off from the grain boundary was the dominant process. From Fig. 7 b, the corrosion cavities formed on the surface of carbon steel due to cementites stripping off from the grain boundary [16] . With the addition of HCl, Ratios were decreased. When HCl concentration increased to 0.025 wt%, it could be found that Ratio was 49.2%. HCl concentration increased to 0.100 wt%, Ratio was 4.6%, which meant that the corrosion process mainly obeyed Faraday’s law and non-Faradaic process became weak. From Fig. 7 d, f, h, k, and n, the uniform corrosion appeared and no corrosion cavities. Therefore, HCl in the H 2 S-containing solution could increase the ratio of Faradaic process of total corrosion process. 4.2 Mechanism of formation and dissolution of the corrosion products Based on the previous researches [6–9,16] and the above results of EIS ( Fig. 4 ), XRD ( Fig. 5 ), and corrosion morphology ( Fig. 6 ), a probable mechanism of formation and dissolution mechanism of mackinawite as corrosion products in the H 2 S-containing solutions with different HCl concentrations could be described as follows [8,16,46] : (8) Fe + H 2 S + H 2 O → FeSH ads - + H 3 O + and / or Fe + HS - → FeSH ads - (9) FeSH ads - ⇌ k - 1 k + 1 FeSH ads + + 2 e - where the subscript ‘ads’ represents the adsorption on surface of carbon steel. The species FeSH ads + on the electrode surface could be incorporated directly into a layer of mackinawite via the following reaction [45] : (10) FeSH ads + → k 2 FeS 1 - x + x SH - + ( 1 - x ) H + or it could be hydrolyzed to yield Fe 2+ via Eq. (11) [8] . (11) FeSH ads + + H 3 O + → Fe 2 + + H 2 S + H 2 O H 2 S exhibited the different role on anodic process of carbon steel depending on the pH value in the solutions. When the HCl was absent or its concentration was low (0.005 wt% HCl), the pH value of the H 2 S-containing solution was about 3.03–3.31, the local supersaturation of FeS 1− x could be formed on the carbon steel surface via the reaction (10) , then nucleation and growth of one or more of the iron sulfide, mackinawite. The pH value (⩽2.75) of the H 2 S-containing solution decreased as the HCl concentration increased above 0.010 wt% and up to 0.100 wt%, iron dissolved by the reaction (11) and little iron sulfide formed on the electrode surface due to the relatively greater solubility of the sulfide solid. The precipitation of sulfide could dissolve directly, and the cathodic reaction occurred at cementite became weak. So the corrosion cavities on the carbon steel surface disappeared. Moreover, it was noted that the protective ability of mackinawite was worse than that of troilite [8] . Consequently, even if at lower HCl concentration and pH range of 3.03–3.31, the iron sulfide film had not any protection against corrosion of carbon steel. 4.3 Analysis of the shape of EIS data From simply fitting of EIS data, the values of the capacitance associated with the high frequency capacitive loop is about 10 −3 Ω −1 cm −2 s n . This is a greater value comparing with the conventional fitting data. Is it a reasonable data? We think that the present experiment was done at 90 °C, the results probably was different with the results presented in other researches at ambient temperature. Moreover, according to Yin et al. [46] and Li et al. [47] , the capacitance of electrical double layer is around 10 −2 Ω −1 cm −2 s n . So the results of EIS measurement in the present work are reasonable. Furthermore, the classical EIS theory is based on the measurement of static state. In this work, the corrosion process of iron or carbon steel in H 2 S-containing solutions is in the static state, although its corrosion rate is high. Hence, the classical EIS theory introduced by Cao [48] is suitable to interpret the impedance results. Cao [48] believed that if diffusion was not involved in the Faradic process for reaction sequence, the admittance Y (or impedance Z ) for the electrode could be expressed as: 1 / Z = Y = j ω C dl + Y F If the electrode reaction was controlled by one surface state variable X , then the faradic admittance Y F could be described as [48] : Y F = 1 / R t + ( ∂ I F / ∂ X ) ss ( ∂ X ′ / ∂ E ) ss / ( j ω - ∂ X ′ / ∂ X ) Correspondingly Y = j ω C dl + 1 / R t + ( ∂ I F / ∂ X ) ss ( ∂ X ′ / ∂ E ) ss / ( j ω - ∂ X ′ / ∂ X ) There was a capacitive loop in the high frequency range due to the double layer capacitance, C dl . There was a capacitive loop in the low frequency range caused by the Faradic electrochemical reaction process when ( ∂ I F / ∂ X ) ss ( ∂ X ’ / ∂ E ) ss < 0 . In contrast, there was an inductive loop in the low frequency range when ( ∂ I F / ∂ X ) ss ( ∂ X ′ / ∂ E ) ss > 0 . Let θ 1 and C FeSH ads - be the fraction of the surface coverage of the adsorbed intermediate FeSH ads + and the concentration of FeSH ads - in the H 2 S-containing solutions, respectively, then the rates of the reactions (9) and (10) can be expressed as: I + 1 = k + 1 ′ exp ( 1 - α 1 ) F RT E C FeSH ads - ( 1 - θ 1 ) = k + 1 C FeSH ads - ( 1 - θ 1 ) I - 1 = k - 1 ′ exp - α 1 F RT E θ 1 = k - 1 θ 1 v 2 = k 2 θ 1 I 1 = I + 1 - I - 1 = k + 1 C FeSH ads - ( 1 - θ 1 ) - k - 1 θ 1 where k +1 and k −1 are the formal rate constants of the forward and backward electrochemical reaction (9) , respectively; α 1 is the charge-transfer coefficient in reduction, which is assumed to be within 0 and 1 and independent of the electrode potential; F is the Faraday constant, E is the electrode potential, T is absolute temperature, and R = 8.314 J K −1 mol −1 . The state variable besides E is θ 1 in the present case, and then the rate of the increase of θ 1 can be expressed as: Ξ 1 = d θ 1 dt = K 1 I 1 - v 2 = K 1 k + 1 C FeSH ads - ( 1 - θ 1 ) - k - 1 θ 1 - k 2 θ 1 K 1 is the coverage-electricity conversion coefficient. ∂ Ξ 1 ∂ θ 1 ss = - K 1 k + 1 C FeSH ads - + k - 1 + k 2 < 0 where the subscript ‘ss’ denotes steady-state. The stability condition is fulfilled [48] . So the variable b can be calculated as: b = ∂ Ξ 1 ∂ E ss = K 1 ∂ I + 1 ∂ E ss - ∂ I - 1 ∂ E ss = K 1 F RT [ ( 1 - α 1 ) I + 1 + α 1 I - 1 ] > 0 The Faradic current density is I F = I 1 = I + 1 - I - 1 thus m = ∂ I F ∂ θ 1 ss = k + 1 C FeSH ads - + k - 1 < 0 and mb < 0 According to the theory of Cao [48] , when mb < 0, the impedance plane display will exhibit a capacitive loop at low frequencies. Additionally, it was believed that hydrogen evolution is the most dominant cathodic reaction at a given H 2 S concentration of the acidic solutions. When hydrogen ions diffuse through the diffusion boundary layer to the metal surface, hydrogen evolution involving an intermediate adsorbed hydrogen atom take place according to the following reactions: (12) H + + e - ⇌ k - 3 k + 3 H ads (13) H ads + H ads → k 4 H 2 where the rate constants of the unit reactions are k +3 , k −3 , and k 4 . If the fraction of the surface coverage of the adsorbed intermediate H ads is θ 2 , the rates of the reactions can be expressed as: I + 3 = k + 3 ′ exp - α 2 F RT E C H + ( 1 - θ 2 ) = k + 3 C H + ( 1 - θ 2 ) I - 3 = k - 3 ′ exp ( 1 - α 2 ) F RT E θ 2 = k - 3 θ 2 v 4 = k 4 θ 2 2 I 3 = I + 3 - I - 3 where I +3 and I −3 are the current densities of the forward and backward reaction (12) , respectively; C H + is the concentration of H + in solution nearby the surface of the electrode; k +3 and k −3 are the formal rate constants. α 2 is the charge-transfer coefficient in reduction. α 2 is assumed to be within 0 and 1 and independent of the electrode potential; F is the Faraday constant, E is the electrode potential, T is absolute temperature, and R = 8.314 J K −1 mol −1 . The effect of the diffusion H + is assumed to be ignored and the only state variable other than E is θ 2 in the presence case and the rate of the increase of θ 2 can be expressed as: Ξ 2 = d θ 2 dt = K 2 I 3 - v 4 = K 2 [ k + 3 C H + ( 1 - θ 2 ) - k - 3 θ 2 ] - k 4 θ 2 2 where K 2 is the coverage-electricity conversion coefficient. ∂ Ξ 2 ∂ θ 2 ss = - [ K 2 ( k + 3 C H + + k - 3 ) + 2 k 4 θ 2 ] < 0 Therefore, the stability condition is fulfilled. And then the variable b can be calculated as following: b = ∂ Ξ 2 ∂ E ss = K 2 ∂ I + 3 ∂ E ss - ∂ I - 3 ∂ E ss = - K 2 F RT α 2 I + 3 + ( 1 - α 2 ) I - 3 < 0 The Faradic current density is I F = I 3 = I + 3 - I - 3 thus m = ∂ I F ∂ θ 2 ss = - ( k + 3 C H + + k - 3 ) < 0 and mb > 0 which indicated that Nyquist plot should contain an inductive loop related to the surface state variable of adsorbed hydrogen ( θ 2 ) [48] . From the above theoretical calculation, the impedance diagram of anodic reaction, SAE-1020 carbon steel was corroded in H 2 S-containing solutions without HCl and with HCl, exhibited a capacitive loop at low frequencies; the impedance diagram of cathodic reaction, hydrogen evolution, exhibited an inductive loop. With the increase of HCl concentration, more hydrogen atoms might be absorbed on the carbon steel surface, the characteristic inductive loop will became more obvious. While HCl concentration increased to 0.100 wt% the characteristic inductive loop in the middle frequency appeared ( Fig. 4 b and c). 5 Conclusion The corrosion rate of SAE-1020 carbon steel at 90 °C increased with increasing the HCl concentration. HCl played a acceleration role on the cathodic hydrogen evolution and decreased the impedance modulus with the increase of HCl concentration from 0.005 wt% to 0.100 wt% in the H 2 S-containing solutions. The corrosion products, mackinawite, were not easily formed on the carbon steel surface due to the relatively greater solubility of the iron sulfide with increasing HCl concentration. The corrosion processes of carbon steel in H 2 S-containing solutions consisted of Faradaic process and non-Faradaic process. HCl in the H 2 S-containing solution could increase the ratio of Faradaic process of total corrosion process. Uniform corrosion was found on the carbon steel surface in H 2 S solutions with various concentration of HCl, while severe localized corrosion was observed in the solution only containing H 2 S which may be attributed to cementites stripped off from the grain boundary. Acknowledgments The authors acknowledge support of the academe of Lanzhou Petrochemical Company, CNPC, the program for New Century Excellent Talents in University of China (NCET-09-0052), the Fundamental Research Funds for the Central Universities (HEUCFZ1019). References [1] R. Cabrera-Sierra E. Sosa M.T. Oropeza I. Gonzalez Electrochemical study on carbon steel corrosion process in alkaline sour media Electrochim. Acta 47 2002 2149 2158 [2] H. Vedage T.A. Ramanarayanan J.D. Mumford S.N. Smith Electrochemical growth of iron sulfide films in H 2 S-saturated chloride media Corrosion 49 2 1993 114 121 [3] Z.A. Foroulis Role of solution pH on wet H 2 S cracking in hydrocarbon production Corros. Prev. Control 8 1993 84 89 [4] M.A. Veloz I. González Electrochemical study of carbon steel corrosion in buffered acetic acid solutions with chlorides and H 2 S Electrochim. Acta 48 2002 135 144 [5] S. Aezola J. Genesca The effect of H 2 S concentration on the corrosion behaviour of API 5L X-70 steel J. Solid State Electrochem. 8 2005 197 200 [6] H.Y. Ma X.L. Cheng S.H. Chen G.Q. Li X. Chen S.B. Lei H.Q. Yang Theoretical interpretation on impedance spectra for anodic iron dissolution in acidic solutions containing hydrogen sulfide Corrosion 54 1998 634 640 [7] H. Ma X. Cheng S. Chen C. Wang J. Zhang H. Yang An ac impedance study of the anodic dissolution of iron in sulfuric acid solutions containing hydrogen sulfide J. Electroanal. Chem. 451 1998 11 17 [8] H. Ma X. Cheng G. Li S. Chen Z. Quan S. Zhao L. Niu The influence of hydrogen sulfide on corrosion of iron under different conditions Corros. Sci. 42 2000 1669 1683 [9] X.L. Cheng H.Y. Ma J.P. Zhang X. Chen S.H. Chen H.Q. Yang Corrosion of iron in acid solutions with hydrogen sulfide Corrosion 54 1998 369 376 [10] Y.S. Choi J.G. Kim Aqueous corrosion behaviour of weathering steel and carbon steel in acid-chloride environments Corrosion 56 2000 1202 1210 [11] H.H. Huang W.T. Tsai J.T. Lee Cracking characteristics of A516 steel weldment in H 2 S containing environments Mater. Sci. Eng. A 188 1994 219 227 [12] H.H. Huang J.T. Lee W.T. Tsai Effect of H 2 S on the electrochemical behaviour of steel weld in acidic chloride solutions Mater. Chem. Phys. 58 1999 177 181 [13] H.H. Huang W.T. Tsai J.T. Lee Electrochemical behaviour of the simulated heat-affected zone of A516 carbon steel in H 2 S solution Electrochim. Acta 41 1996 1191 1199 [14] H.H. Rehan S.A. Salih H. El-Daley A.G. Gad-Allah Effect of sulfide ions on the corrosion behaviour of mild steel in acetate buffer Collect. Czech. Chem. Commun. 58 1993 547 [15] L. Quej-Aké R. Cabrera-Sierra E. Arce-Estrada J. Marín-Cruz EIS evaluation of the effect of neutralizing and inhibitor compounds on corrosion process of 1018 carbon steel in acid solutions typical of atmospheric distillation plants Int. J. Electrochem. Sci. 3 2008 56 66 [16] J. Tang Y. Shao J. Guo T. Zhang G. Meng F. Wang The effect of H 2 S concentration on the corrosion behaviour of carbon steel at 90 °C Corros. Sci. 52 2010 2050 2058 [17] Corrosion of metals and alloys—removal of corrosion products from corrosion test specimens, GB/T 16545-1996, idt ISO 8407, 1991. [18] E. Poorqasemi O. Abootalebi M. Peikari F. Haqdar Investigating accuracy of the Tafel extrapolation method in HCl solutions Corros. Sci. 51 2009 1043 1054 [19] Mohammed A. Amin Sayed S. Abd E.E.F. El-Rehim Rady S. El-Sherbini The inhibition of low carbon steel corrosion in hydrochloric acid solutions by succinic acid: Part I. Weight loss, polarization, EIS, PZC, EDX and SEM studies Electrochim. Acta 52 2007 3588 3600 [20] J.O’M. Bockris D. Drazic R. Despic The electrode kinetics of the deposition and dissolution of iron Electrochim. Acta 4 1961 325 [21] E.J. Kelly The active iron electrode J. Electrochem. Soc. 112 1965 124 [22] E. McCafferty N. Hackerman Kinetics of iron corrosion in concentrated acidic chloride solutions J. Electrochem. Soc. 119 1972 999 [23] J. Jankowski R. Juchniewicz A four-point method for corrosion rate determination Corros. Sci. 20 1980 841 851 [24] Y. Yi H. Kim Y. Park J. Kim Effect of an inhibitor on the stress corrosion cracking behaviour of alloy 600 in a high-temperature caustic solution Corrosion 61 2005 403 410 [25] M. Stern A.L. Geary Electrochemical polarization: I. A theoretical analysis of the shape of polarization curves J. Electrochem. Soc. 104 1957 56 63 [26] J. Liu Y. Lin X. Yong X. Li Study of cavitation corrosion behaviours and mechanism of carbon steel in neutral sodium chloride aqueous solution Corrosion 61 2005 1061 1069 [27] M.L. Doche J.Y. Hihn A. Mandroyan R. Viennet F. Touyeras Influence of ultrasound power and frequency upon corrosion kinetics of zinc in saline media Ultrason. Sonochem. 10 2003 357 362 [28] E. Sosa R. Cabrera-Sierra M.E. Rincoon M.T. Oropeza I. Gonzaalez Evolution of non-stoichiometric iron sulfide film formed by electrochemical oxidation of carbon steel in alkaline sour environment Electrochim. Acta 47 2002 1179 1208 [29] R.C. Newman K. Rumash J. Webster The effect of pre-corrosion on the corrosion rate of steel in neutral solutions containing sulphide: relevance to microbially influenced corrosion Corros. Sci. 33 1992 1877 [30] S. Tsujikawa A. Miyasaka M. Veda S. Ando T. Yamada Alternative for evaluating sour gas resistance of low-alloy steels and corrosion-resistant alloys Corrosion 49 1993 409 419 [31] T. Hemmingsen H. Lima Electrochemical and optical studies of sulphide film formation on carbon steel Electrochim. Acta 43 1998 35 40 [32] H.T. Param B.C. Allan Dissolution of iron during the initial corrosion of carbon steel in aqueous H 2 S solutions Can. J. Chem. 57 1979 188 196 [33] A.G. Wikjord T.E. Rummery F.E. Doern D.G. Owen Corrosion and deposition during the exposure of carbon steel to hydrogen sulfide water solutions Corros. Sci. 20 1980 651 [34] F.H. Meyer O.L. Riggs R.L. McGlasson J.D. Sudbury Corrosion products of mild steel in hydrogen sulfide environments Corrosion 14 1958 109 115 [35] H.T. Param B.C. Allan Dissolution of iron sulfide (troilite) in aqueous sulfuric acid J. Phys. Chem. 80 1976 1844 1848 [36] B.G. Pound G.A. Wright R.M. Sharp The anodic behaviour of iron in hydrogen sulfide solutions Corrosion 45 1989 386 392 [37] C. Milton Kansite = mackinawite FeS Corrosion 22 1966 191 193 [38] B.G. Pound R.M. Sharp G.A. Wright The corrosion of carbon steel and stainless steels in simulated geothermal media Aust. J. Chem. 38 1985 1133 1140 [39] R.A. Berner Tetragonal iron sulfide Science 137 1962 669 [40] R.A. Berner Thermodynamic stability of sedimentary iron sulfides Am. J. Sci. 265 1967 773 785 [41] R.H. Hausler L.A. Goeller R.P. Zimmerman R.H. Rosenwald Contribution to the “filming amine” theory: an interpretation of experimental results Corrosion 28 1972 7 16 [42] P. Taylor The stereochemistry of iron sulfides—a structural ration for the crystallization of some metastable phases from aqueous solution Am. Mineral. 65 1980 1026 [43] R.A. Berner Iron sulfides formed from aqueous solution at low temperatures and atmospheric pressure J. Geol. 72 1964 293 306 [44] D.T. Rickard The chemistry of iron sulphide formation at low temperatures Stockholm Contrib. Geol. 20 1969 67 95 [45] D.W. Shoesmith P. Taylor M.G. Bailey D.G. Owen The formation of ferrous monosulfide polymorphs during the corrosion of iron by aqueous hydrogen sulfide at 21 °C J. Electrochem. Soc. 127 1980 1007 1015 [46] Z.F. Yin W.Z. Zhao Z.Q. Bai Y.R. Feng W.J. Zhou Corrosion behaviour of SM 80SS tube steel in stimulant solution containing H 2 S and CO 2 Electrochim. Acta 53 2008 3690 3700 [47] J.B. Li X. Hou M.S. Zheng J.W. Zhu Joint effect of temperature, stress states and sulfur ions on the CO 2 corrosion behavior of N80 tubing steel Int. J. Electrochem. Sci. 2 2007 607 617 [48] C. Cao On the impedance plane display for irreversible electrode reactions based on the stability conditions of the steady-state: I. One state variable besides electrode potential Electrochim. Acta 35 1990 831 836