Effect of Cl− Accumulation on Corrosion Behavior of Steels in H2S/CO2 Methyldiethanolamine (MDEA) Gas Sweetening Aqueous Solution
Naiyan Zhang,Dezhi Zeng,Guoqing Xiao,Jianfeng Shang,Yuanzhi Liu,Decai Long,Qiyao He,Ambrish Singh
DOI: https://doi.org/10.1016/j.jngse.2016.02.055
IF: 5.285
2016-01-01
Journal of Natural Gas Science and Engineering
Abstract:Effects of Cl- accumulation on corrosion behavior of the three steels (20,304L and 316L) in H2S/CO2 MDEA desulfuring aqueous solution was investigated by using a HT (high temperature) autoclave, and the corrosion products were characterized by scanning electron microscopy (SEM), energy dispersive Xray spectroscopy (EDX) and X-ray diffraction technique (XRD). Electrochemical measurements such as polarization curve and electrochemical impedance spectroscopy were adopted to analyze the effects of Cl- concentration on the corrosion. Weight loss tests showed that corrosion rate of three steels (20, 304L and 316L) appeared as a reversal "v" shape and reached the peak at 20,000 mg/L Cl- content. SEM, EDX and XRD results showed that the corrosion scales were mainly FeS, FeS2 and FeCO3, and the corrosion process was mainly controlled by H2S, furthermore, CO2 corrosion further weakened as the chlorine ions content increased. Electrochemical studies suggested that, with the rise in chlorine ions content, the corrosion potential shifted negatively, and the activation and dissolution of mental anode accelerated, which can be attributed to the penetration and absorption effect of chloride ion. In addition, chlorine ions competitive absorption also played an important role in corrosion process. Therefore, to prolong the service life of desulfuring equipment, it is suggested that 20 steel not be used in units and facilities with large acid gas load at high temperature and the mass concentration of chloride ion content in the desurfuring MDEA solution should be controlled at a low level with the consideration of its complex effect. (C) 2016 Elsevier B.V. All rights reserved.