Abstract:The general CO2 corrosion rates of C1018 carbon steel have been measured for NaCl concentrations 3 – 25 wt% at 20oC, pH 4.0, 5.0 and 6.0. The corrosion process was monitored by linear polarization resistance and potentiodynamic sweeps. AC impedance was used to measure and correct for solution resistance while weight loss was used to verify the corrosion rate magnitude. Experimental results showed that high salt concentrations decreased the general CO2 corrosion rate significantly and nonlinearly. Potentiodynamic sweep analysis shows that both cathodic and anodic processes were retarded. Flow velocity effects on general CO2 corrosion rate were minimized due to an increase of salt concentration. No effect of high salt concentration on initiation of localized attack was detected. A parallel research project was conducted to investigate the high salt concentration effect on H2S corrosion. The main objective was to study if the high concentration of chloride could initiate localized attack in a H2S system. Experiments were conducted in a nitrogen purged system with trace amount of H2S (50 ppm). Weight loss was used to measure corrosion rates. Scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffraction (XRD) methods were used to characterize the morphology, composition and phase identity of the corrosion products. Experimental results show that high salt concentration significantly slowed down the reaction rate in H2S corrosion. Some pitting attack was found both in salt-free and high-salt conditions. Experimental results did not show evidence that chlorides can initiate localized corrosion in H2S systems.

The corrosion behaviour of sulphur on the carbon steel used in oil & gas field with high concentration of H2S

Unraveling the effect of H2S on the corrosion behavior of high strength sulfur-resistant steel in CO2/H2S/Cl− environments at ultra high temperature and high pressure

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Effect of Temperature on Corrosion Behavior and Mechanism of S135 and G105 Steels in CO2/H2S Coexisting System

Corrosion Mechanism of Oil Field Gathering Pipeline Containing Small H2S Impurity

Insights into the effect of H2S on the corrosion behavior of N80 steel in supercritical CO2 environment

Effect of carbon dioxide on corrosion of tubular steel in high hydrogen sulfide and carbon dioxide environments

A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

Effect of H2S on CO2 Corrosion of Mild Steel in High Temperature Supercritical CO2 Condition

Effect of H2S concentrations on corrosion failure of L245NS steel in CO2-O2-H2S system

Effect of interaction between corrosion film and H2S/CO2 partial pressure ratio on the hydrogen permeation in X80 pipeline steel

Effect of Temperature and H<sub>2</sub>S Concentration on Corrosion of X52 Pipeline Steel in Acidic Solutions

Effects of Adding CO2 to Low Level H2S Containing Aqueous Environments on the Corrosion and Hydrogen Penetration Behaviors of High-Strength Steel

Corrosion Behavior of X52 Anti-H2S Pipeline Steel Exposed to High H2S Concentration Solutions at 90 °C

Effect of Temperature and Pressure on CO2/H2S Corrosion Rate of N80 Steel

Hydrogen Sulfide Corrosion of Metal Equipment in Oil and Gas Field

Corrosion of Mild Steel in the Presence of Elemental Sulfur

Effect of CO2/H2S and Applied Stress on Corrosion Behavior of 15cr Tubing in Oil Field Environment

20 10 HIGH SALT CONCENTRATION EFFECTS ON CO 2 CORROSION AND H 2 S CORROSION

Influence of S on Corrosion Film of P110 Steel in S+CO2 Oilfield

Hydrostatic pressure effects on corrosion behaviour of X80 steel in artificial sea water