Unraveling the Impact of Cr Content on the Corrosion of Tubing Steel in High CO2 and Low H2S Environments
Dezhi Zeng,Jiancheng Luo,Hanwen Zhang,Chunyan Zheng,Xueke Chen,Wenguang Zeng,Hao Chen,Baojun Dong
DOI: https://doi.org/10.1007/s11665-024-10391-z
IF: 2.3
2024-12-12
Journal of Materials Engineering and Performance
Abstract:A theoretical foundation for selecting corrosion-resistant materials is necessary to address the corrosion risks in complex oil and gas fields and tubing for CO 2 capture, utilization, and storage (CCUS). To achieve this, experiments were conducted using actual oilfield simulated formation water as the corrosive medium. Weight-loss corrosion tests and surface analysis methods were employed to investigate and compare the corrosion of four steel materials (C110, 3Cr, 5Cr, and 9Cr) in high mineralization, CO 2 , and trace H 2 S coexistence environments. The results show that all materials experience CO 2 -dominated corrosion under CO 2 and trace H 2 S conditions, with corrosion rates exceeding the controlled limit for oilfields (0.076 mm/y). The corrosion severity is classified as extremely severe, and the corrosion products mainly comprise a mixed carbonate of FeCO 3 and CaCO 3 . Both uniform and localized corrosion rates decrease gradually with increasing chromium content in the materials. The experimental study demonstrates that chromium has good corrosion resistance. The morphology of the corrosion product film transitions from irregular particles to rhombohedral blocks or flakes with increased chromium content. Carbon steel primarily forms Fe x Ca 1-x CO 3 corrosion products with a small amount of Fe 2 O 3 inclusion, while corrosion products in chromium-containing steel include Cr 2 O 3 , Cr(OH) 3 , Fe x Ca 1-x CO 3 , and Fe 2 O 3 . As the chromium content in the steel material increases, the content of Ca and Cl elements in the corrosion product film gradually decreases. These findings provide valuable insights into the corrosion behavior of different steel materials under the challenging conditions of high mineralization, CO 2 -rich, and trace H 2 S environments. They contribute to the theoretical basis for selecting suitable corrosion-resistant tubing materials for oil and gas operations, including CCUS, enabling the industry to mitigate corrosion risks effectively.
materials science, multidisciplinary