Ce 3+ -doped silicate-based down-conversion phosphors: investigation on synthesis, structure and photoluminescence properties

Yan Chen,Tinglan Wang,Tianyi Zhou,Minghao Xia,Yongqian Wang

DOI: https://doi.org/10.1007/s10854-018-8526-1

2018-01-01

Abstract:Two types of Ce 3+ -doped silicate-based phosphors with different silicon-to-oxygen (Si-to-O) ratio have been synthesized by high-temperature solid state reaction and investigated systematically the influence of Si-to-O ratio on host structures and photoluminescence properties of Ce 3+ -doped phosphors. Due to diverse Si-to-O ratio in two silicate-based hosts, Ce 3+ shows different site occupancies and luminescence behaviors, since the host structure has been changed by introducing O atom. In the Sr 2+x−y MgSi 2 O 7+x :yCe 3+ (x = 0 or 1, y = 0.005–0.09) phosphors system, the excitation wavelength both showed at UV region, the emission wavelength changed from violet to blue light region with increasing the value of x (x = 0 or 1), which have been analyzed by the crystal-field effect of Ce 3+ . The PL results indicate that Sr 2−0.01 MgSi 2 O 7 :0.01Ce 3+ phosphors (x = 0) exhibits a deep-blue emission with peak at 405 nm, while the peak of Sr 3−0.01 MgSi 2 O 8 :0.01Ce 3+ phosphors (x = 1) moves to 395 nm from the increased ratio of Si-to-O. Besides, the optimal concentration of doping Ce 3+ are both at 0.01 in two kinds of silicate-based phosphors which display stable and good luminescent performance. Our work provides a novel thinking of regulating photoluminescence properties by manipulating Si-to-O ratio in silicates and a valuable example for the emission characteristics of Ce 3+ activators in silicate-based phosphor hosts.