Abstract:In this study, [Sr0.99Eu0.01]3MgSi2O8 phosphors were sintered at 1200–1400 °C for 1–5 h by using the solid-state reaction method. The crystallinity and morphology of these phosphors were characterized through X-ray diffraction analysis and field-emission scanning electron microscopy, respectively, to determine their luminescence. The photoluminescence properties, including the excitation and emission properties, of the prepared phosphors were investigated through fluorescence spectrophotometry. The α-Sr2SiO4, Sr2MgSi2O7, and Sr3MgSi2O8 phases coexisted in the [Sr0.99Eu0.01]3MgSi2O8 phosphors, which were synthesized at low temperatures. The particles of these phosphors had many fine hairs on their surface and resembled Clavularia viridis, which is a coral species. Transmission electron microscopy and energy dispersive X-ray spectroscopy indicated that the fine hairs contained the Sr2SiO4 and Sr2MgSi2O7 phases. However, when the [Sr0.99Eu0.01]3MgSi2O8 phosphors were sintered at 1400 °C, the Sr3MgSi2O8 phase was observed, and the Eu2+-doped Sr3MgSi2O8 phase dominated the only broad emission band, which had a central wavelength of 457 nm (blue light). The emission peaks at this wavelength were attributed to the 4f65d1–4f7 transition at the Sr2+(I) site, where Sr2+ was substituted by Eu2+. The average decay time of the synthesized phosphors was calculated to be 1.197 ms. The aforementioned results indicate that [Sr0.99Eu0.01]3MgSi2O8 can be used as a blue-emitting phosphor in ultraviolet-excited white light-emitting diodes.

VUV-UV-vis Photoluminescence, X-ray Radioluminescence and Energy Transfer Dynamics of Ce3+ and Eu2+ in Sr2MgSi2O7.

Ultraviolet-Vacuum Ultraviolet Photoluminescence and X Ray Radioluminescence of Ce3+-Doped Ba3mgsi2o8

Luminescence of Ce3+ at Two Different Sites in Α-Sr2p2o7 under Vacuum Ultraviolet-Uv and X-Ray Excitation

Photoluminescence Studies on Eu2+ and Ce3+-doped Li2SrSiO4

Luminescence and energy transfer of Ce3+, Eu2+ Co-doped SrSi2O2N2 phosphors

Synthesis, structure, and luminescence properties of SrSiAl<sub>2</sub>O<sub>3</sub>N<sub>2</sub>:Eu<sup>2+</sup> phosphors for light-emitting devices and field emission displays

Luminescence of Ce3+ and Pr3+ Doped Sr2Mg(BO3)2 under VUV–UV and X-ray Excitation

Photoluminescence properties of a Ce3+ doped Sr3MgSi2O8 phosphor with good thermal stability

Spectroscopic Properties, Energy Transfer and Structural Analysis of Sr2CeO4:M+ and Sr2CeO4:Eu3+, M+ (M+ = Li+, Na+, K+).

Photoluminescence evolutions and physical mechanism discussions of Sr1.95-(Ca/Ba) MgSi2O7:Eu2+ phosphors

Preparation, Structure and Photoluminescence Properties of Eu2+ and Ce3+-doped SrYSi4N7

X-ray Excited Luminescence and Persistent Luminescence of Sr2MgSi2O7:Eu2+, Dy3+ and Their Associations with Synthesis Conditions

Synthesis and Luminescence Properties of Eu2+-Doped Sr3MgSi2O8 Blue Light-Emitting Phosphor for Application in Near-Ultraviolet Excitable White Light-Emitting Diodes

Optical Properties And Energy Transfer Of Sr1-X-Ymgp2o7:Xce(3+), Ytb(3+) Phosphor Under Ultraviolet Excitation

Luminescence properties of CaSi2O2N2 ∶Ce3+/Eu phosphors

Synthesis and Luminescent Properties of Ce3+,Mn2+ Doped Sr2SiO4 Phosphors

A study on the luminescence of different crystallographic sites for Sr2SiO4 : Eu2 + phosphors

Luminescence of Ce<sup>3+</sup>-doped Sr<sub>10</sub>(PO<sub>4</sub>)<sub>6</sub>S phosphors

Er3+ Co-Doped Sr1.956MgSi2O7: 0.004eu2+, 0.04dy3+ Phosphors and Enhancement of Luminescent Properties

Eu 3+ -doped Sr 2 (Al 1−x Mg x )(Al 1−x Si 1+x )O 7 phosphors: electronic, crystal structures and photoluminescence properties

Color-tunable photoluminescence and energy transfer properties of single-phase Sr2MgSi2O7:Eu3+, Dy3+