Abstract:Using CO2 polycarbonates as engineering thermoplastics has been limited by their mechanical performances, particularly their brittleness. Poly(cyclohexene carbonate) (PCHC) has a high tensile strength (40 MPa) but is very brittle (elongation at break <3%), which limits both its processing and applications. Here, well-defined, high molar mass CO2 terpolymers are prepared from cyclohexene oxide (CHO), cyclopentene oxide (CPO), and CO2 by using a Zn(II)Mg(II) catalyst. In the catalysis, CHO and CPO show reactivity ratios of 1.53 and 0.08 with CO2, respectively; as such, the terpolymers have gradient structures. The poly(cyclohexene carbonate)-grad-poly(cyclopentene carbonate) (PCHC-grad-PCPC) have high molar masses (86 < Mn < 164 kg mol-1, ĐM < 1.22) and good thermal stability (Td > 250 °C). All the polymers are amorphous with a single, high glass transition temperature (96 < Tg < 108 °C). The polymer entanglement molar masses, determined using dynamic mechanical analyses, range from 4 < Me < 23 kg mol-1 depending on the polymer composition (PCHC:PCPC). These polymers show superior mechanical performance to PCHC; specifically the lead material (PCHC0.28-grad-PCPC0.72) shows 25% greater tensile strength and 160% higher tensile toughness. These new plastics are recycled, using cycles of reprocessing by compression molding (150 °C, 1.2 ton m-2, 60 min), four times without any loss in mechanical properties. They are also efficiently chemically recycled to selectively yield the two epoxide monomers, CHO and CPO, as well as carbon dioxide, with high activity (TOF = 270-1653 h-1, 140 °C, 120 min). The isolated recycled monomers are repolymerized to form thermoplastic showing the same material properties. The findings highlight the benefits of the terpolymer strategy to deliver thermoplastics combining the beneficial low entanglement molar mass, high glass transition temperatures, and tensile strengths; PCHC properties are significantly improved by incorporating small quantities (23 mol %) of cyclopentene carbonate linkages. The general strategy of designing terpolymers to include chain segments of low entanglement molar mass may help to toughen other brittle and renewably sourced plastics.

Polymer blends using poly(trimethylene carbonate)

Poly(Trimethylene Monothiocarbonate) from the Alternating Copolymerization of Cos and Oxetane: A Semicrystalline Copolymer

Rheology of Poly(lactic Acid)/poly(trimethylene Terephthalate) Blends Compatibilized by Clay or Maleic Anhydride-Grafted Poly(ethylene-Octene) Elastomer

Synthesis and characterization of ester-free poly(trimethylene carbonate) bearing long-alkyl moieties and its degradation

Controllable Degradation of Poly (trimethylene carbonate) via Self-blending with Different Molecular Weights

The Ring-Opening Homopolymerizations of Trimethylene Carbonate and 2,2-Dimethyltrimethylene Carbonate

Blends of Poly(β-hydroxybutyrate) with Poly(propylene carbonate)

Biodegradable Poly(trimethylene Carbonate‐b‐(l‐lactide‐ran‐glycolide)) Terpolymers with Tailored Molecular Structure and Advanced Performance

Review on modification strategies of polyethylene/polypropylene immiscible thermoplastic polymer blends for enhancing their mechanical behavior

Performance evaluation of biodegradable polymer PHBV and PBAT blends with adjustable melt flow behaviour, heat deflection temperature, and morphological transition

Ethylene Polymerization with Hybrid Nickel Diimine/cp2ticl2 Catalyst: a New Method to Prepare Blends of Linear and Branched Polyethylene

Poly (Butylene Adipate‐Co‐Terephthalate) (PBAT) – Based Biocomposites: A Comprehensive Review

In vitro enzymatic degradation of the PTMC/cross-linked PEGDA blends

Simultaneously Enhanced Chain Flexibility, Three Dimensional Printability, and Reduction of Shrinkage Stress in Biodegradable and Photocurable Multiblock Copolymers

Polymerization of trimethylene carbonates using organic phosphoric acids

Controlled Carbon Dioxide Terpolymerizations to Deliver Toughened yet Recyclable Thermoplastics

Ternary Blends from Biological Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate), Poly(propylene carbonate) and Poly(vinyl acetate) with Balanced Properties

Morphological, thermal, rheological and mechanical properties of poly (butylene carbonate) reinforced by stereocomplex polylactide

Morphological Characteristics, Properties, and Applications of Polylactide/Poly(ε‐caprolactone) Blends and Their Composites—A Review

Reactive compatibilization and properties of low-cost and high-performance PBAT/thermoplastic starch blends

Long-term in vivo degradation behavior of poly(trimethylene carbonate-co-2, 2′-dimethyltrimethylene carbonate)