Abstract:Poly(trimethylene carbonate-co-2, 2′-dimethyltrimethylene carbonate) P(TMC-co-DTC) copolymers with different molecular weights or molar ratios were prepared by bulk ring-opening polymerization (ROP) of trimethylene carbonate (TMC) and 2, 2′-dimethyltrimethylene carbonate (DTC). The in vivo degradation behavior of the resulting copolymers of 2 mm diameter was subsequently investigated by implanting the samples subcutaneously in the back of rats. The data showed that the sample's mass loss was reduced, and the form-stability was enhanced with the increase of DTC segments content in the copolymer while increasing the molecular weight could accelerate the degradation rate and improve the form-stability of the copolymers. Among them, the samples containing 25 mol% DTC segments with a molecular weight of 205 kDa achieved the highest mass loss of 26.1% and maintained good form-stability after 35 weeks of implantation. In particular, implants with high DTC segments amount of 75 mol% (molecular weight of 208 kDa) maintained excellent form-stability and a low mass loss of 4.8% during the implantation cycle and exhibited some properties different from the other groups. Further experimental results showed that the content of DTC segments increased from 74.4% to 77.3%, and the crystallinity of the copolymer transformed to semi-crystalline state also increased from 61.4% to 76.4% during the degradation. The Tg, Tm and hardness of the degraded polymers were correspondingly improved. In addition, the degradation mechanism of surface erosion in vivo of the resulting P(TMC-co-DTC) copolymers were verified. This work provides a promising class of candidate carrier materials for the application of long-acting drug delivery systems through a detailed study of the in vivo degradation behavior of P(TMC-co-DTC) copolymers.

The Ring-Opening Homopolymerizations of Trimethylene Carbonate and 2,2-Dimethyltrimethylene Carbonate

Pyridyl-urea catalysts for the solvent-free ring-opening polymerization of lactones and trimethylene carbonate

Controlled Ring-Opening Polymerization of β-Butyrolactone <i>Via</i> Bifunctional Organoboron Catalysts

Controllable Ring-opening Polymerization of Δ-Valerolactone Catalyzed by Quinolinyl-Urea/MTBD Systems

Synthesis of Poly(trimethylene carbonate) Oligomers by Ring-Opening Polymerization in Bulk

Polymerization of trimethylene carbonates using organic phosphoric acids

Rare Earth Complexes [ln(edbp)2(dme)na(dme)3] As Catalysts for the Polymerization of 2,2-Dimethyltrimethylene Carbonate

Ring-Opening Copolymerization Of Alpha-Chloromethyl-Alpha-Methyl-Beta-Propiolactone With 1,3-Trimethylene Carbonate

Ring‐Opening Polymerization of Cyclic Acetals: Strategy for Both Recyclable and Degradable Materials

Ring-opening copolymerization of α-chloromethyl-α-methyl-β-propiolactone with 1,3-trimethylene carbonate

Ring Opening Polymerization of Aliphatic Cyclic Carbonates in the Presence of Natural Amino Acids

Long-term in vivo degradation behavior of poly(trimethylene carbonate-co-2, 2′-dimethyltrimethylene carbonate)

CO2-Based Polycarbonates through Ring-Opening Polymerization of Cyclic Carbonates Promoted by a NHC-Based Zinc Complex

RARE EARTH COMPLEXES[Ln(EDBP)_2(DME)Na(DME)_3]AS CATALYSTS FOR THE POLYMERIZATION OF 2,2-DIMETHYLTRIMETHYLENE CARBONATE

Ring-opening Polymerizaion of 2,2-Dimethyltrimethylene Carbonate Initiated by in Situ Generated, Tetrahydrosalen Stablized Yttrium Borohydride Complex and Random Copolymerization with Ɛ -Caprolactone

Rare Earth Complex Initiated Ring-Opening Polymerization of 2,2-Dimethyltrimethylene Carbonate

Recent Progress in Controlled Ring-Opening Polymerization of Aliphatic Polyesters

Polymerization of 2,2′‐dimethyltrimethylene Carbonate by Lutetium Complexes Bearing Amino‐phosphine Ligands

Polymer blends using poly(trimethylene carbonate)

Ring-Opening Polymerization of Trimethylene Carbonate Catalyzed by Novel Single Component Rare Earth Calixarene Complexes

Ring-opening polymerization of 2,2-dimethyltrimethylene carbonate using rare earth tris(4-tert-butylphenolate)s as a single component initiator