Controllable Degradation of Poly (trimethylene carbonate) via Self-blending with Different Molecular Weights

Zhipeng Hou,Siwen Chen,Zhongcun Li,Zhangpei Chen,Jianshe Hu,Jing Guo,Peng Li,Liqun Yang
DOI: https://doi.org/10.1016/j.polymdegradstab.2021.109596
IF: 5.204
2021-07-01
Polymer Degradation and Stability
Abstract:Blend films of Poly (trimethylene carbonate) (PTMC) homopolymers with different molecular weights were prepared. The in vitro enzymatic degradation tests were carried out in lipase solutions to investigate the effect of self-blending on the degradation performance of PTMC. It was observed that the mass loss decreased as the proportion of low molecular weight PTMC in the blend film increased. And the sample's mass loss with the mass ratio of PTMC334/PTMC57=1/16 reached almost 30% after seven weeks, which corresponded to the minimum degradation rate constant k value of 5.219. It is also indicated by the changes in weight as well as the macroscopic and microscopic morphology. Furthermore, during the degradation cycle, the thickness of the film also became thinner with the mass loss, confirming the surface erosion degradation mechanism of the PTMC blend films. The conclusion that PTMC does not produce acidic degradation products has also been confirmed. Finally, decreases in glass transition temperature (T g) and thermal stability were found along with the film degraded, attributing to the accumulation of low molecular weight degradation products on the surface. In brief, the long-acting application of PTMC in biomedical fields could be satisfied by precisely tailoring the degradation properties via its self-blending with different molecular weights.
polymer science
What problem does this paper attempt to address?
The problem that this paper attempts to solve is how to precisely regulate the degradation properties of poly(trimethylene carbonate) (PTMC) with different molecular weights through self - mixing, in order to meet the long - term application requirements in the biomedical field. Specifically, the paper explores the preparation of blend films with different molecular weight ratios by self - mixing high - molecular - weight and low - molecular - weight PTMC, and studies the degradation behavior of these blend films in in - vitro enzymatic degradation tests. The main objective of the study is to find a method that can prolong the degradation cycle of PTMC materials while maintaining good morphological stability, thereby making it more suitable for applications such as long - term sustained - release systems. ### Main research contents: 1. **Synthesis of PTMC with different molecular weights**: - By adjusting the amount of the catalyst Sn(Oct)₂, two PTMC homopolymers with different molecular weights, 57 kg/mol and 334 kg/mol respectively, were synthesized. 2. **Preparation of blend films**: - PTMC blend films with different mass ratios were prepared by the solvent casting method, including films with PTMC 334/PTMC 57 ratios of 1/1, 1/4, 1/8 and 1/16. 3. **In - vitro enzymatic degradation test**: - In - vitro enzymatic degradation tests were carried out on the prepared blend films, mainly examining indicators such as mass loss, degradation rate constant, macroscopic and microscopic morphological changes, thickness loss and pH value change. ### Key findings: - **Mass loss and degradation rate**: - As the proportion of low - molecular - weight PTMC in the blend film increases, the mass loss gradually decreases, and the degradation rate constant \( k \) also decreases accordingly. For example, when the PTMC 334/PTMC 57 ratio is 1/16, the mass loss after seven weeks is only 30%, and the corresponding degradation rate constant \( k \) is 5.219. - **Morphological stability**: - The introduction of low - molecular - weight PTMC significantly reduces the degradation rate of the blend film while retaining the good morphological stability of high - molecular - weight PTMC. In particular, when the PTMC 334/PTMC 57 ratio is 1/16, the film exhibits good morphological stability during the degradation process. - **Surface - erosion degradation mechanism**: - It was found that the degradation of the blend film is mainly manifested as surface erosion, that is, as the degradation time prolongs, holes gradually appear on the film surface and the thickness gradually decreases. - **pH value change**: - During the degradation process, the pH value of the medium remains stable without a significant decrease, indicating that PTMC does not produce acidic degradation products during the degradation process, avoiding possible aseptic inflammation. ### Conclusion: By self - mixing PTMC with different molecular weights, its degradation properties can be effectively regulated, achieving a longer degradation cycle and good morphological stability. This strategy provides a simple and effective solution for the long - term application of PTMC in the biomedical field.