Abstract:Transparent conductive films are important components of organic optoelectronic devices. However, current organic light-emitting devices (OLEDs) used in flexible wearable applications are severely restricted by the fragility and poor conductivity of composing ultra-thin electrodes. In this study, poly(methyl methacrylate) (PMMA)/trimethylaluminum (TMA) was prepared through an atomic layer half-reaction and used as a self-encapsulating nucleation layer. The study suggested coordination between the Au atoms with the functional methyl groups of PMMA/TMA to yield an entire substrate surface. The Au nuclei were evenly and densely distributed on the substrate surface, and island growth of Au film was prevented, leading to good flexibility and photoelectric properties of the Au film deposited on the nucleation layer. For instance, a 7 nm thick layer resulted in a sheet resistance of 18.19 ± 0.44 Ω/◻ at 85.89% transmittance. Furthermore, the use of the as-obtained high-performance electrode in flexible organic optoelectronic devices led to repeated bending over 1000 cycles to a radius of 1 mm without significant reduction in the optoelectronic performances. The nucleation induction layer could also function as a bottom encapsulation with a water vapor transmission rate as low as 2.123 × 10<sup>−3</sup> g/cm<sup>2</sup>/day (60 °C/80% relative humidity). Additionally, the nucleation induction layer exhibited excellent performances in fully transparent devices (75.72% transmittance). In sum, these findings look promising for future flexible wearable applications.

Ultrathin Au Electrodes Based on a Hybrid Nucleation Layer for Flexible Organic Light-Emitting Devices

Ultrathin and Ultrasmooth Au Films As Transparent Electrodes in Ito-Free Organic Light-Emitting Devices

Highly Flexible and Mechanically Robust Ultrathin Au Grid As Electrodes for Flexible Organic Light-Emitting Devices

Fabrication of nucleation induction layer of self-encapsulated metal anode by an atomic layer half-reaction for enhanced flexible OLEDs

Ultra-Smooth and Efficient NiO/Ag/NiO Transparent Electrodes for Flexible Organic Light-Emitting Devices

Highly Flexible Organic-Inorganic Hybrid Perovskite Light-Emitting Devices Based on an Ultrathin Au Electrode

High-Efficiency, Large-Area And Color-Stable Flexible Organic Light-Emitting Diodes Using An Ultra-Thin Metal Electrode

Flexible Organic Light-Emitting Diodes with ITO/Ag/ITO Multi-Layers As Anodes

Interfacial Engineering of Ultrathin Metal Film Transparent Electrode for Flexible Organic Photovoltaic Cells

A Novel Nucleation Inducer for Ultrathin Au Anodes in High Efficiency and Flexible Organic Optoelectronic Devices

Epitaxial Ultrathin Au Films on Transparent Mica with Oxide Wetting Layer Applied to Organic Light-Emitting Devices

Transparent Ultrathin Oxygen‐Doped Silver Electrodes for Flexible Organic Solar Cells

Transparent ultrathin Ag nanomesh electrode fabricated by nanosphere lithography for organic light-emitting devices

Highly transparent and conductive metal oxide/metal/polymer composite electrodes for high-efficiency flexible organic light-emitting devices

Study on ITO/Ag/ITO multilayer film as the electrode of organic light-emitting diodes

A Flexible and Thin Graphene/Silver Nanowires/Polymer Hybrid Transparent Electrode for Optoelectronic Devices.

Fabrication and characterization of Ag film with sub-nanometer surface roughness as a flexible cathode for inverted top-emitting organic light-emitting devices.

Low Roughness Silver Nanowire Flexible Transparent Electrode by Low Temperature Solution-Processing for Organic Light Emitting Diodes

Ultra‐Thin Flexible ITO‐free Organic Solar Cells with Gradient Bilayer Electron Transport Materials

An ultrathin, smooth, and low-loss Al-doped Ag film and its application as a transparent electrode in organic photovoltaics.

Enhanced Efficiency of Organic Light-Emitting Devices by Using a Directly Imprinted Nanopillared Ultrathin Metallic Electrode.