Microstructure and Ablation Properties of C/C-Zr-Si-O Composites Prepared by Carbothermal Reduction of Hydrothermal Co-Deposited Oxides

Haibo Ouyang,Guibiao Li,Cuiyan Li,Jianfeng Huang,Jie Fei,Jing Lu
DOI: https://doi.org/10.1016/j.matdes.2018.08.048
IF: 9.417
2018-01-01
Materials & Design
Abstract:C/C-Zr-Si-O composites were prepared by carbothermal reduction of hydrothermal co-deposited ZrO2, SiO2, and C. The bulk density of composites reached 1.71 g/cm(3) with 8 cycles of co-deposition. The matrix of the composites includes ZrC, SiC, ZrO2, and SiO2 with fine grain size (300-500 nm) and homogeneous distribution. The mass and linear ablation rate of C/C-Zr-Si-O composites were 0.112 mg/cm(2).s and 0.46 mu m/s, respectively, under a plasma flame for 120 s. The attractive ablation resistance of the composites resulted from its unique structure, which tends to form a continuous ZrO2-SiO2 glass layer in the ablation center, a layer of SiO2-ZrO2 bubbles in the transition region, and fluffy SiO2 nanowires layer in the heat-affected region. These ablation layers were barriers to restrain the diffusion of oxidative gas and heat. The C/C-Zr-Si-O composites provide an alternative ceramics system with attractive ablation resistance, while carbothermal reduction of hydrothermal co-deposited oxides is a feasible method for the structural design of carbon fiber reinforced ultra-high temperature ceramic. (C) 2018 Elsevier Ltd. All rights reserved.
What problem does this paper attempt to address?