Abstract:Temperature is one of the critical factors that strongly affect the behavior of hydrogen isotopes in tungsten (W). This work investigates the effect of initial exposure temperature on the deuterium (D) retention and surface blistering in recrystallized W. D plasma exposure is started at 420 K and 600 K, respectively, and then changed to the same temperature of 520 K. For each temperature, the irradiation fluence is ∼ 1 × 1026 D m−2, and therefore the total fluence is ∼ 2 × 1026 D m−2 for each sample. A reference W sample was also exposed at 520 K with the same total fluence. Compared with the reference sample, it is found that the initial temperature of 420 K significantly inhibits the formation of intergranular blisters and leads to a reduction of intragranular blisters in size. Although the initial temperature of 600 K facilitates the formation of intergranular blisters, the intergranular blister size is reduced. This is possibly related to the relatively higher concentration of trapped D over a large depth range as revealed by the TMAP simulation results, leading to the fact that intergranular cracks are more prone to propagate along sloping grain boundaries. Thermal desorption spectra results show that the initial exposure temperature of 420 K and 600 K reduce D retention by a factor of ∼ 56 % and ∼ 34 %, respectively. It is considered to be connected with the blistering-induced defects and D transport in W, which are strongly affected by the initial exposure temperature. This work demonstrates that the initial exposure temperature plays a crucial role in D behavior in W, improving the understanding of the temperature effects of hydrogen isotopes behavior in W.

Aggravated Blistering and Increased Deuterium Retention in Iron-Damaged Tungsten after Exposure to Deuterium Plasma with Various Surface Temperatures

Suppression of Deuterium-Induced Blistering in Pre-Damaged Tungsten Exposed to Short-Duration Deuterium Plasma

Deuterium Distribution and Behavior of Blisters in Pre-Damaged and Undamaged Tungsten

Effect of Heavy Ion Pre-Irradiation on Blistering and Deuterium Retention in Tungsten Exposed to High-Fluence Deuterium Plasma

Dependence of blistering and deuterium retention on damage depth in damaged tungsten exposed to deuterium plasma

Influence of Suppressed Blistering by Heavy Ion Pre-Damage on Deuterium Retention in Tungsten

The Effect of Pre-Damage Distribution on Deuterium-Induced Blistering and Retention in Tungsten

Deuterium Retention and Surface Blistering in Non-Damaged and Damaged Tungsten after Repetitive Plasma Exposure and Outgassing

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Surface Blistering and Deuterium Retention in Tungsten Exposed to Low-Energy Deuterium Plasma at Different Temperatures

The Effect of High-Temperature Pre-Damage on Vacancy-Type Defects and Deuterium Retention in Tungsten

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Decreased surface blistering and deuterium retention in potassium potassium-doped tungsten exposed to deuterium plasma following ion irradiation

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Decreased Surface Blistering and Deuterium Retention in Potassium-Doped Tungsten Exposed to Deuterium Plasma Following Ion Irradiation

Effect of Exposure Temperature on Deuterium Retention and Surface Blistering of Tungsten Exposed to Sequential Nitrogen and Deuterium Plasma

Effect of Anisotropic Grain Boundaries on the Surface Blistering of Tungsten Induced by Deuterium Plasma Exposure

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Blistering on Tungsten Surface Exposed to High Flux Deuterium Plasma

Mitigated Blistering and Deuterium Retention in Tungsten Exposed to High-Flux Deuterium–neon Mixed Plasmas