Abstract:To predict brittle fracture in high-strength steels, this study introduces a methodology for analyzing hydrogen-assisted degradation. The proposed approach considers the fully coupled problems of deformation-hydrogen diffusion and cohesive zone modeling. The analysis of hydrogen diffusion assumes that trapped and lattice hydrogen remain in a equilibrium state while accounting for the relationships between the increase in trap sites and plastic strain. The diffusion model simulates hydrogen diffusion in the small scale yielding (SSY) configuration at a crack tip. The simulation results reveal that hydrogen diffusion follows the hydrostatic stress distribution around the crack tip region. Additionally, the plastic strain near this area leads to an increased number of trap sites. Notably, the simulations indicate that lattice hydrogen is the dominant source of embrittlement when a sufficient amount of hydrogen atoms dissolve into the steel, as compared to trapped hydrogen. The hydrogen-assisted degradation evolution is studied by investigating the influence of hydrogen in a cohesive zone modeling (CZM) with a trapezoidal traction separation law (TSL), based on Hydrogen-Enhanced DEcohesion (HEDE) framework. The fully computational framework is utilized to simulate the hydrogen-charged fracture toughness test in a (CT) specimen made of 30CrMo high strength steel. It is demonstrated that the load bearing capacity of the specimen decreases with an increase in the initial hydrogen concentration. Furthermore, the study examines the evolution of the initial crack time with varying initial hydrogen concentrations. The initial hydrogen concentrations are estimated to match the maximum loads observed in the experimental load-displacement curves based on computational framework. The computational CTOD-R curves for hydrogen generally follow the experimental data, the marginally elevated computational CTOD values to underestimate the embrittling in hydrogen-contaminated steel. Overall, the present study proves the capability of this numerical technique to reproduce experimental findings related to hydrogen-assisted fracture.

Numerical Simulation of Hydrogen Permeation in Steels

Numerical Evaluation on Analysis Methods of Trapping Site Density in Steels Based on Hydrogen Permeation Curve

Modelling of hydrogen diffusion in a steel containing micro-porosity. Application to the permeation experiment

Numerical Simulation on the Leakage and Diffusion of Hydrogen in Indoor Environment

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

Numerical Simulation for Tortuosity of Porous Media

Numerical Modeling for Hydrogen Permeation Through Steel Under Sour-Corrosion and Tensile Stress

Simulation of hydrogen permeation through pure iron for trapping and surface phenomena characterisation

Numerical Simulation of Hydrogen Diffusion in Low Alloy Steel Welded Joint under Wet H2S Environment

Numerical Approach for Predicting Hydrogen Diffusion in Dual-Phase Hot Stamped Boron Steel with Hydrogen Embrittlement

Experimental and numerical analysis of hydrogen diffusion behaviors in an ultra-fine bainitic steel

Phase-Field Modeling of Hydrogen Diffusion and Trapping in Steels

3D FINITE ELEMENT SIMULATION OF HYDROGEN DIFFUSION IN 16mnr STEEL WELDMENT

Simulation of the Hydrogen Permeation Behavior of X80 Pipeline Steels in H<sub>2</sub>S Saturated Environment by Cathodic-Charging Method

Analysis of hydrogen permeation tests considering two different modelling approaches for grain boundary trapping in iron

DIFFUSIVITY OF HYDROGEN IN STEELS AT LOW TEMPERATURES

Numerical Simulation for Hydrogen-Assisted Cracking: An Explicit Phase-Field Formulation

Numerical Simulation Analysis of Hydrogen Leakage and Diffusion in Tunnel

Numerical Simulation on the Diffusion of Hydrogen Due to High Pressured Storage Tanks Failure

Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel

Predictive Environmental Hydrogen Embrittlement on Fracture Toughness of Commercial Ferritic Steels with Hydrogen-Modified Fracture Strain Model