Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

Rolling Contact Fatigue Wear Behavior of Carbide-free Bainitic Steel

Fatigue and recrystallization evolution of carbide-free bainitic layer under high-stress rolling sliding contact

High-silicon spring steel transformation to carbide-free bainitic (CFB) steel: a mechanical and tribological approach under rolling/sliding conditions

Carburization Induced Extra-Long Rolling Contact Fatigue Life of High Carbon Bearing Steel

Effect of Primary Carbides on Rolling Contact Fatigue Behaviors of M50 Bearing Steel

The effect of microstructure evolution on the ratchetting-fatigue interaction of carbide-free bainite rail steels under different heat-treatment conditions

Microstructural-based analysis of the unexpected differences in rolling contact fatigue behavior between SAE52100 and SAE4320

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Effects of Double Quenching on Fatigue Properties of High Carbon Bearing Steel with Extra-High Purity

Influence of Toughness and Retained Austenite on Wear Behaviour of Carbide-Free Bainite in High Silicon Steel

Influence of original microstructure on rolling contact fatigue property of D2 wheel steel

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

Rolling contact fatigue failure mechanism of bearing steel on different surface roughness levels under heavy load

Investigation on Rolling Contact Fatigue of 55 Medium-Carbon Steel

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Initiation of internal fatigue crack in a carbide-free bainitic steel during high cycle fatigue

BEHAVIOR OF SHORT FATIGUE CRACKS IN MEDIUM CARBON BAINITIC BACK-UP ROLL STEEL UNDER MILD TRACTIVE ROLLING CONTACT

Study on fatigue wear competition mechanism and microstructure evolution on the surface of a bainitic steel rail

The effect of retained austenite on rolling/sliding contact fatigue of high carbon steel

Effect of microstructure on wear and rolling contact fatigue behaviors of bainitic/martensitic rail steels

Rolling Contact Fatigue Crack Initiation in Medium Carbon Bainitic Steel